3B yazıcı teknolojisi ile üretilen protezlerde kaide plağı ve yapay diş bağlantısının incelenmesi
Evaluation of the bond strength between the artificial teeth and denture base produced with the 3D printer
- Tez No: 870592
- Danışmanlar: PROF. DR. HAYRUNNİSA CANAN BURAL ALAN
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: hareketli protezler, kaide plağı, yapay dişler, bağlanma dayanımı, 3B yazıcı teknolojisi, removable denture, denture base, artificial teeth, bond strenght, 3D printed technology
- Yıl: 2024
- Dil: Türkçe
- Üniversite: İstanbul Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Protetik Diş Tedavisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada 3 boyutlu (3B) yazıcı teknolojisiyle üretilen tam protezlerde kaide plağı ile yapay dişler arasındaki bağlanma dayanımı (BD) değerlendirilmiştir. Fotopolimerizan esaslı kaide plağı ve yapay diş reçineleri 3B yazıcı teknolojisi kullanılarak 5x7x10 mm boyutlarında bloklar üretildi. Yapay diş ile kaide plağı ara yüzüne uygulanan 4 farklı bağlanma ajanının (otopolimerizan akrilik reçine ve rezin siman, fotopolimerizan yapay diş ve kaide plağı reçineleri) 3 farklı bağlanma aralığında (0.25, 0.5 ve 1 mm) uygulanmasıyla 12 adet deney grubu oluşturulmuştur (n=13). Kontrol grubu olarak basınçla kalıplama yöntemiyle üretilen kaide plağı ve plastik yapay diş değerlendirilmiştir. Final boyutları 1x1x20 mm boyutlarına getirilen mikro çubuk formundaki örneklere universal test cihazında 1mm/dk hızda ve 300 MPa kuvvet altında mikroçekme testi uygulanmıştır. Kopma anındaki maksimum kuvvet ölçüldükten sonra kopma anındaki yüzey alanına bölünerek maksimum BD değerleri hesaplanmıştır. Bağlanma ajanının ve aralığının BD etkisi iki yönlü varyans analizi testi, anlamlılık belirlenen parametrelerin post-hoc ikili karşılaştırmalarında Bonferroni testi ve Pearson korelasyon testi uygulanmıştır (p<0.05). En yüksek anlamlı BD otopolimerizan akrilik reçinenin 1 mm aralıkta (47,4 ± 8,4 MPa) uygulandığı örneklerde saptanırken tüm deney gruplarına ait ortalama BD değerleri kontrol grubundan (55,6 ± 7,5 MPa) düşüktür (p<0.001). Fotopolimerizan kaide plağı reçinesinin uygulandığı örneklerde ortalama BD en yüksek 0.5 mm aralığında elde edilmiştir (p< BD ve bağlanma aralığı arasında korelasyon pozitiftir (p<0.001, r=0.489). Çalışmanın bulguları 3B yazıcı teknolojisiyle üretilen protezlerde yapay dişlerin kaide plağı ile bağlantısının oluşturulmasında otopolimerizan ajanların 1 mm; fotopolimerizan kaide plağı reçinesinin ise 0.5 mm bağlanma aralıklarında uygulanabileceğini önermektedir. Fotopolimerizan yapay diş reçinesinin bağlanma ajanı olarak uygulandığı tüm bağlanma aralıklarında klinik olarak dayanıklı bir bağlantı sunmamaktadır.
Özet (Çeviri)
This study evaluated the bond strength (BS) between denture base and artificial teeth processed with three-dimensional (3D) printing technology and compared the differences according to the type of bonding agents and bonding gap. Photopolymerized denture base and artificial teeth blocks with 5x7x10 mm dimensions were 3D printed. Twelve experimental groups were formed (n=13), according to 4 bonding agents (autopolymerizing acrylic resin and resin cement, 3D printed photopolymerizing denture base and artificial teeth resin) and 3 bonding gaps (0.25, 0.5 ve 1 mm). The samples manufactured with compression moulding technique were used as the control group. Final sample sizes having dimensions of 1x1x20 mm were applied to microtensile test under 300 MPa at a speed of 1 mm/min at universal testing device. At rupture, maximum load was measured and by dividing the values at the bonding area, the maximum BS values were obtained. Data were analyzed using two-way ANOVA, Bonferroni Test for the post hoc comparisons and pearson correlation test (p<0.05). The significant highest BS (47.4 ± 8.4 MPa) was found when autopolymerizing acrylic resin was applied at 1mm (p<0.001). The BS of all experimental groups were significantly lower than the control group (55.6 ± 7.5 MPa) (p<0.001). The correlation between the BS and bonding gap was positive (p<0.001, r=0.489). As a bonding agent, photopolymerized 3D printed denture base resin resulted in the significant highest BS at 0.5 mm (p<0.001). The results of this study indicated that autopolymerizing bonding agents can be applied at 1 mm, and 3D printed photopolymerizing denture base resins can be applied at 0.5 mm to obtain a durable bond. Photopolymerized 3D printed artificial teeth resin seems not to provide enduring bond.
Benzer Tezler
- Maksillofasiyal protezlerin yapımında kullanılan silikonların polimerizasyon ve üç boyutlu yazıcı yöntemleri ile üretilmiş farklı rezin altyapı malzemelerine bağlantı dayanımının incelenmesi
Peel bond strength of silicones used in extraoral maxillofacial prostheses from different resin substructures
BERNA ÖZCAN
Diş Hekimliği Uzmanlık
Türkçe
2024
Diş HekimliğiSağlık Bilimleri ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ TUĞGEN MERSİN
- Nanopartikül ilavesinin farklı protez kaide rezinlerinin mekanik ve fiziksel özelliklerine etkisinin değerlendirilmesi
Evaluation of the effect of nanoparticle addition on the mechanical and physical properties of different denture base resins
BEŞAR İZZETAĞA
Doktora
Türkçe
2024
Diş HekimliğiZonguldak Bülent Ecevit ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. GAYE SAĞLAM
- Design process, manufacturing and material characterization of a prosthetic polymer aortic heart valve
Protez polimer aort kalp kapağının tasarım süreci, üretimi ve malzeme karakterizasyonu
MÜGE YAREN YAŞARTÜRK
Yüksek Lisans
İngilizce
2024
Kardiyolojiİstanbul Teknik ÜniversitesiHesaplamalı Bilim ve Mühendislik Ana Bilim Dalı (disiplinlerarası)
PROF. DR. MUSTAFA SERDAR ÇELEBİ
- 3B yazıcı ile üretilen PLA40/ABS60 malzemesinin termal ve mekanik özelliklerinin deneysel incelenmesi
Experimental investigation of thermal and mechanical properties of PLA40/ABS60 produced with 3d printer
SAMET YAMAN
Yüksek Lisans
Türkçe
2019
Makine MühendisliğiDüzce Üniversitesiİmalat Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ MUSTAFA AYYILDIZ
- Biyobozunur polimerler için yeni bir 3D yazıcı tasarımı ve gerçeklenmesi
Designing and implementation of a new 3D printer for biodegredable polymer
İBRAHİM ERDOĞDU
Yüksek Lisans
Türkçe
2025
Mekatronik MühendisliğiSakarya Uygulamalı Bilimler ÜniversitesiMekatronik Mühendisliği Ana Bilim Dalı
DOÇ. DR. BARIŞ BORU