Sıvı azotta bekletme ve geleneksel kriyojenik işlemlerin sae 4140 çeliğin mekanik ve mikroyapı özelliklerine etkilerinin karşılaştırılması
Comparison of affects of holding in liquid nitrogen and traditional cryoganic processes on mechanical and microstructure properties of sae 4140 steel
- Tez No: 371659
- Danışmanlar: YRD. DOÇ. İSMAİL ŞAHİN
- Tez Türü: Yüksek Lisans
- Konular: Makine Mühendisliği, Metalurji Mühendisliği, Mechanical Engineering, Metallurgical Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2014
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Makine Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 85
Özet
Bu çalışmada, sıvı azotta bekletme işlemi ve kriyojenik yöntemin SAE 4140 çeliğe etkileri deneysel olarak incelenmiştir. Bu kapsamda SAE 4140 çeliğine ıslah işlemi, sıvı azotta bekletme işlemi, kriyojenik işlem ve menevişleme işlemleri farklı sıra ve gruplar halinde uygulanmış ve toplamda 8 değişken oluşturulmuştur. Sıvı azotta bekletme işlemi görecek olan numuneler, 1,6 °C/dk ortalama hızla oda sıcaklığından -196 °C'ye indirilmiş ve bu sıcaklıkta 24 saat süreyle bekletilmiştir. Kriyojenik işlem uygulanacak numuneler ise 2 °C/dk sabit hızla oda sıcaklığından -140 °C'ye indirilmiş ve bu sıcaklıkta 24 saat boyunca bekletilmiştir. Yapılan mikrosertlik incelemeleri ve çekme deneyleri sonucunda, ıslah işlemi ardından yapılan tüm soğutma işlemlerinde, sertlikten ödün vermeksizin tokluğun arttığı gözlenmiştir. Tokluk açısından en bariz iyileşme; %32.83'lük artış ile ıslah işleminin ardından kriyojenik işlem ve son olarak menevişleme işlemi uygulanan 8 numaralı değişken numunelerinde görülmüştür. Sıvı azotta bekletme işlemi ve kriyojenik yöntemin, yüzey kalitesine olumlu ya da olumsuz bir etkisinin olmadığı gözlenirken; eş merkezlilik performansı bakımından sıvı azotta bekletme işlemi, kriyojenik yönteme bire bir alternatif teşkil edebilecek performansta gerçekleşmiştir. Kopma dayanımında en yüksek artış, 66 N/mm2 iyileşme ile 8 numaralı değişkende gerçekleşmiştir. Kriyojenik işlem veya sıvı azotta bekletme işlemi uygulanan tüm numunelerin mikroyapısında, martenzit dağılımında iyileşme ve martenzit oranında artış gözlenmiştir. Bu da sertlik verilerinde bir miktar artış sağlamıştır. Çalışma kapsamında incelenen özellikler bakımından; sıvı azotta bekletme işleminin, klasik kriyojenik işleme değişen oranlarda alternatif teşkil edebileceği görülmüştür.
Özet (Çeviri)
In this study, the effects of the cryogenic method by waiting SAE 4140 steel into liquid nitrogen were experimentally investigated. In this context, SAE 4140 was exposed of the treatment process, incubation into the liquid nitrogen, cryogenic treatment and tempering operations in the groups of alternate rows, and a total of eight variants were generated. The temperature of samples ready for the liquid nitrogen process was lowered to -196 °C from room temperature by 1,6 °C/min speed and remained for 24 hours. The samples ready for the cryogenic process, on the other hand, were subjected to the same application from room temperature to -140 °C by 2 °C/min. The results of the micro hardness investigations and tensile tests; the cooling processes applied after subsequent treatments point the increase in toughness without any hardness deficiency. The most obvious improvement in terms of toughness was observed as 32.83% in the sample variants of number eight after applications of the treatment, cryogenic and tempering processes. Neither positive nor negative impact of the Soaking in liquid nitrogen and cryogenic method was observed. In terms of concentricity performance, soaking in liquid nitrogen process was an identical alternative of the cryogenic method. The highest increase in tensile strength was realized as 66 N/mm2 in the variant with the number 8. The increase in the distribution and the ratio of the martensite were observed in the microstructures of all the samples which were exposed to cryogenic process or soaking in liquid nitrogen treatment. This leads to an increase in the hardness results. According to the properties investigated in this study, the soaking in the liquid nitrogen treatment was suggested to be an alternative for the classical cryogenic method in various proportions.
Benzer Tezler
- Düşük karbonlu mikro alaşımlı çeliklerin sertlik ve mikro yapıları üzerine soğuma hızının etkisi
Effect of cooling rate on the microstructure and hardness of low carbon microalloyed steels
CİHAN EKİNCİ
Yüksek Lisans
Türkçe
2011
Fizik ve Fizik MühendisliğiSüleyman Demirel ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. NAZIM UÇAR
- Kriyojenik koşullar altında termal stres ile modifiye edilmiş çok duvarlı karbon nanotüplerin makrodispersiyonuna yüzey aktif maddelerin etkisi
Effect of surface-active substances on the macrodispersion of thermal stress modified multi-wall carbon nanotubes under cryogenic conditions
AYKUT YİRMİBEŞOĞLU
Yüksek Lisans
Türkçe
2023
Kimya MühendisliğiHitit ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
DOÇ. DR. NİHAN KAYA
DOÇ. DR. FİLİZ BORAN
- Siltli ve killi zeminlerin tekrarlı yükler altındaki davranışı
The cyclic behavior of silty and clayey soils under cyclic loads
MEHMET BARIŞ CAN ÜLKER
Yüksek Lisans
Türkçe
2004
İnşaat Mühendisliğiİstanbul Teknik ÜniversitesiZemin Mekaniği ve Geoteknik Mühendisliği Ana Bilim Dalı
DOÇ. DR. AYFER ERKEN
- Çelikte Ferrovanadyum Yerine Nitrovanadyum Kullanımının Elektriksel Aşındırma ile İşlenebilirliğe Etkisinin İncelenmesi
Investigation of nitrovanadium effect instead of ferrovanadium in steel on electrical discharge machinability
İSA KESKİN
Yüksek Lisans
Türkçe
2017
Makine MühendisliğiBülent Ecevit ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. NİHAL EKMEKCİ
- Sıvı nitrojende depolanan Ephestia kuehniella Zell. (un güvesi) yumurtalarında Trichogramma evanescens Westwood ve Trichogramma brassicae Bezdenko türlerinin kitle üretimlerinin araştırılması
Mass production of Trichogramma evanescens Westwood and Trichogramma brassicae Bezdenko using Ephestia kuehniella Zell. eggs stored in liquid nitrogen
ŞENNUR BAŞÜĞÜT
Yüksek Lisans
Türkçe
2019
ZiraatTekirdağ Namık Kemal ÜniversitesiBitki Koruma Ana Bilim Dalı
PROF. DR. NİHAL ÖZDER