Poli (2-siklopentiliden-1,3-dioksalan-4-il-metil metakrilat-ko-stiren) polimerinin fiziksel ve termodinamik özelliklerinin invers gaz kromatografisi ile incelenmesi

Analysis of physical and thermodynamic properties of poly(2-cyclopentylidene-1,3-dioxolan-4-yl-methyl-methacrylate-co-styrene)copolymer with inverse gas chromatography

  1. Tez No: 387729
  2. Yazar: ADNAN KALKAN
  3. Danışmanlar: YRD. DOÇ. DR. M.HAMDİ KARAGÖZ
  4. Tez Türü: Yüksek Lisans
  5. Konular: Bilim ve Teknoloji, Science and Technology
  6. Anahtar Kelimeler: [2-cyclopentylidene-1, 3-dioxolan-4-yl-methyl-methacrylate-co-styrene], Inverse Gas Chromatography, physical and thermodynamic properties
  7. Yıl: 2011
  8. Dil: Türkçe
  9. Üniversite: Yüzüncü Yıl Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 59

Özet

Bu çalışmada, poli(2-siklopentiliden-1,3-dioksalan-4-il-metil metakrilat-ko-stiren) İnvers Gaz Kromatografisi ile termodinamik özellikleri incelendi. Kromosorb W katısı üzerine kaplanmış kopolimer kolon içine doldurularak 313-473 K aralığında problar enjekte edilerek spesifik alıkonma hacimleri (Vg0) tayin edildi.1/T; lnVg grafiğinden polimerin camsı geçiş sıcaklığı (Tg) 110 0C dolaylarında bulundu. Tg altındaki sıcaklıklarda polimer üzerinde probların adsorpsiyon ısıları bulundu. Tg üzerinde sorpsiyon için probların H1s, ?S1s ve ?G1s değerleri tayin edildi.Sonsuz seyreltik hale ait probların ağırlıkça aktiflik katsayısı (a1/w1), Flory-Huggins etkileşim parametresi (), kısmi molar serbest enerji (?G1?) ve kısmi molar ısı (H1) değerleri bulundu. Flory-Huggins etkileşim parametresi değerlerinden faydalanılarak polimerlerin çözünürlük parametresi (?2) tayin edildi. Çözünürlük parametresinin sıcaklık arttıkça azaldığı gözlendi.Anahtar Kelimeler : [2-(siklopentiliden)-1,3-dioksalan-4-il] metil metakrilat-ko-stiren, İnvers Gaz Kromatografisi, fiziksel ve termodinamik özelikler.

Özet (Çeviri)

In this work, the thermodynamic parameters of poly [2-cyclopentylidene-1,3-dioxolan-4-yl-methyl-methacrylate-co-styrene] were investigated by using Inverse Gas Chromatography. Polymer was covered by the Chromosorb W and was packed within column, then the probes were injected at different temperatures (313-473 K) and the specific retention volumes were obtained.The glass transition temperature (Tg) of polymer were found about 110 0C from the plot of in Vg0 versus 1/T. The heats of the adsorbtion of probes on the polymer at the temperatures below the glass transition temperature were found. Above the glass transition temperature H1s, S1s and G1s values of probes for sorption were determined.The weight activity coefficients (a1/w1), Flory-Huggins interaction parameters (), partial molar free energies (G1) and partial molar heats (H1) values of probes were obtained for infinite dilution state. The solubility parameters (2) of polymer was determined by values of Flory-Huggins interaction parameters. It was observed that the solubility parameters decreased with the increasing temperature.

Benzer Tezler

  1. 1,3-dioksalan halkası içeren metakrilat monomer ve polimerlerinin sentezi ve özelliklerinin incelenmesi

    Monomer of 1,3-dioxalane ring contain methacrylate with polymers synthesis and characterization

    ARZU ÜNAL

    Yüksek Lisans

    Türkçe

    Türkçe

    2002

    KimyaFırat Üniversitesi

    Kimya Ana Bilim Dalı

    YRD. DOÇ. DR. ZÜLFİYE İLTER

  2. Compatibilization of poly (2,6-dibromo 1,4- phenylene oxide) with sulfonated polystyrene ionomers

    Poli (2,6-dibromo 1,4-fenilen oksit) polimerinin sülfonlanmış polistiren iyonomerleri ile uyumluluk çalışması

    CEMİL ALKAN

    Yüksek Lisans

    İngilizce

    İngilizce

    1999

    KimyaOrta Doğu Teknik Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. LEYLA ARAS

  3. Poli (2-akrilamido 2-metil propan sülfonik asit)'in sentezi, karakterizasyonu ve elektroreolojik özelliklerinin incelenmesi

    Synthesis, characterisation and elektrorheological properties of pol (2-acrylamido-2-methyl-1-propane sulfonic acid)

    HAŞİM YILMAZ

    Yüksek Lisans

    Türkçe

    Türkçe

    1999

    KimyaGazi Üniversitesi

    Kimya Ana Bilim Dalı

    DOÇ.DR. HALİL İBRAHİM ÜNAL

  4. Synthesis and self assembly of poly(2-isopropyl-2-oxazoline)-b-poly(2-phenyl-2-oxazoline)-b-poly(2-isopropyl2-oxazoline)

    Poli(2-izopropil-2-oksazolin)-b-poli(2-fenil-2-oksazolin)-b-poli(2-izopropil-2-oksazolin) sentezi ve kendiliğinden yapılanması

    ÇAĞRI TURAN

    Yüksek Lisans

    İngilizce

    İngilizce

    2022

    KimyaOrta Doğu Teknik Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. İREM EREL GÖKTEPE

  5. Grafting of poly (2-(Dimethylamino) ethyl methacrylate) onto crosslinked poly(Vinyl benzyl chloride) resin for removal of acidic dyes

    Poli̇ (2-(di̇meti̇lami̇no) eti̇l metakri̇lat'in çapraz bağlı poli̇ (Vi̇ni̇l benzi̇l klorür)'e aşılanması ve asi̇di̇k boyaların atık sudan gi̇deri̇lmesi̇nde kullanımı

    MERVE HAMAMCI

    Yüksek Lisans

    İngilizce

    İngilizce

    2014

    Kimyaİstanbul Teknik Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. BAHİRE FİLİZ ŞENKAL