Sıcaklık ve manyetik alan duyarlı poli(vinil asetat)/poli(vinil klorür)/polifuran üçlü kompozit ve nanokompozit filmlerinin hazırlanması ve karakterizasyonu
Synthesis and characterization of temperature and magnetic field sensitive poly(vinyl acetate)/poly(vinyl chloride)/polyfuran ternary composite and nanocomposite films
- Tez No: 395777
- Danışmanlar: PROF. DR. BEKİR SARI
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2015
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 139
Özet
Bu çalışmada; kimyasal polimerleşme yöntemiyle, yükseltgen olarak demir(III) klorür (FeCl3) ve çözücü olarak susuz kloroform (CHCl3) kullanılarak polifuran (PF) sentezlendi. PF'nin uygun oranlarında; poli(vinil asetat) (PVAc) ve poli(vinil klorür) (PVC) termoplastik polimerleri ile (PVAc/PVC/PF) üçlü kompozitleri ve magnetit (Fe3O4) katkılı (PVAc/PVC/PF/Fe3O4) nanokompoziti toz ve film halinde hazırlandı. Elde edilen özgün iletken filmlerin, belirli sıcaklık aralığında (25-50℃) katlanabilme ve ilk haline dönebilme, manyetik alan duyarlı olma gibi üstün özelliklere sahip olduğu gözlendi. Hazırlanan örneklerin; yapısal ve ısıl özellikleri, yüzey morfolojileri, iç yapıları ve yüzey pürüzlülüğü sırasıyla FTIR, Termogravimetrik Analiz (TGA), Taramalı Elektron Mikroskobu (SEM), Geçirimli Elektron Mikroskobu (TEM) ve Atomik Kuvvet Mikroskobu (AFM) ile incelendi. Örneklerin iletkenlikleri, oda sıcaklığında ve farklı sıcaklıklarda dört nokta tekniği ile ölçüldü. Sıcaklık arttıkça kompozitlerin ve nanokompozitin iletkenliklerinin arttığı belirlendi. Gouy ölçümlerinden elde edilen değerler tüm polimerlerin iletkenlik mekanizmalarının polaron yapıda olduğunu gösterdi. X-Işını Kırınımı (XRD) analizi sonuçları, PF ve kompozitlerin amorf yapıda olduklarını, buna karşılık nanokompozitin ise kristal yapıda olduğunu gösterdi. Magnetit ve nanokompozitin manyetik özellikleri Titreşimli Örnek Manyetometresi (VSM) ile belirlendi, doygunluk mıknatıslanma (Ms) değerleri sırasıyla 58,9 ve 5,3 emu g-1 olarak tespit edildi. Magnetit katkılı nanokompozitin oda sıcaklığında süperparamanyetik özelliğe sahip olduğu bulundu.
Özet (Çeviri)
In this study, polyfuran (PF) was synthesized via chemical polymerization method using iron (III) chloride (FeCl3) as an oxidant and anhydrous chloroform (CHCl3) as solvent. Polyfuran in the appropriate ratios; with poly(vinyl acetate) (PVAc) and poly(vinyl chloride) (PVC) thermoplastic polymers, (PVAc/PVC/PF) ternary composites and magnetite (Fe3O4) doped (PVA/PVC/PF/Fe3O4) nanocomposite were prepared as powders and films. It was observed that the prepared novel conductive films have superior properties such as to be able fold a certain temperature range (25-50℃) and to turn it into the first and magnetic field sensitive. The structural properties, thermal behavior, surface morphology, internal structure and surface roughness of the prepared samples were investigated by FTIR, Thermogravimetric Analysis (TGA), Scanning Electron Microscopy (SEM), Transmission Electron Microscopy (TEM) and Atomic Force Microscopy (AFM), respectively. The conductivities of the samples were measured at room temperature and different temperatures by the four-point technique. It was found that the conductivities of ternary composites and nanocomposite increased with increasing temperature. The values obtained from the gouy measurements showed that the conducting mechanisms of all the polymers showed a polaron nature. X-Ray Diffraction (XRD) analysis results demonstrated that the PF and composites are amorphous structure, whereas nanocomposite is crystalline form. The magnetic properties of the magnetite and nanocomposite were determined by Vibration Sample Magnetometer (VSM), the saturation magnetization (Ms) values were found 58.9, 5.3 emu g-1, respectively. It was found that magnetite doped nanocomposite has superparamagnetic properties at room temperature.
Benzer Tezler
- Sıcaklık ve manyetik alan duyarlı poli(dimetilsiloksan)/poli(vinil asetat)/politiyofen üçlü kompozit ve nanokompozit filmlerinin sentezi ve özelliklerinin araştırılması
Synthesis of temperature and magnetic field sensitive poly(dimethylsiloxane)/poly(vinyl acetate)/polythiophene ternary composite films and nanocomposite films and investigation of their properties
HÜSNİYE MELİKE KAYABAŞ
- Manyetik alan ve sıcaklık duyarlı poli(n-t-bütilakrilamit-ko-akrilamit)/poli(vinil metil eter) yarı-içiçe geçmiş ağ yapılı ferrojellerinin sentezi ve karakterizasyonu
Preparation and characterization of magnetic field and thermo-sensitive poly (n-t-butylacrylamide-co-acrylamide)/poly(vinyl methyl ether) semi-interpenetrating networks ferrogels
DÖNE YÖRÜK
- Sıcaklığa duyarlı manyetik polimerlerin sentezi, karakterizasyonu ve uygulama alanlarının incelenmesi
The synthesis and characterization of thermosensitive magnetic polymers and investigation of their applications
GAMZE ÇETİN
Doktora
Türkçe
2018
Kimya Mühendisliğiİstanbul ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. HASİNE KAŞGÖZ
DOÇ. DR. SERKAN EMİK
- Poli(N-izopropilakrilamit) in poli(etilen teraftalat) yüzeyine doku mühendisliği uygulamaları için foto başlatma yoluyla aşılanması
Photo-induced grafting of poly(N-isopropylacrylamide) from poly(ethylene terephthalate) surface for tissue engineering applications
PARISA GOLSHAEI
- Biyouyumlu akıllı polimerik nanoparçacık geliştirilmesi ve kontrollü ilaç salınım uygulamaları
Development of biocompatible smart polymeric nanoparticles for controlled drug relase applications
MEHMET ULAŞAN
Doktora
Türkçe
2014
BiyokimyaSelçuk ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. YUNUS ÇENGELOĞLU
DOÇ. DR. MUSTAFA SELMAN YAVUZ