Nano gümüş partikülleri ile kaplanan ortodontik braketlerde antibakteriyel özelliklerin, iyon salınımlarının ve biyouyumluluğun in vivo ve in vitro olarak değerlendirilmesi
In vivo and in vitro assessment of the antibacterial effects, ion release and biocompatibility of nano silver coated orthodontic brackets
- Tez No: 399124
- Danışmanlar: PROF. DR. REFİA LALE TANER
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2015
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Ortodonti Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 180
Özet
Bu çalışmanın amacı sabit ortodontik tedavilerin sık görülen yan etkisi olan beyaz nokta lezyonlarının (BNL), gümüşün antibakteriyel özelliğinden yararlanılarak önlenmesi amacıyla, nano gümüş partikülleri ile kaplanan ortodontik braketlerin antibakteriyel özelliklerinin, iyon salınımlarının ve biyouyumluluklarının in vivo ve in vitro olarak değerlendirilmesidir. Mandibular kesici dişlerine nano gümüş partikülleri ile kaplanan ortodontik braket ve konvansiyonel ortodontik braket yapıştırdığımız 12 adet Wistar Albino rat çalışma (6) ve kontrol grubu (6) olarak ayrılmıştır. 0,1, 3, 7, 14, 30, 45 ve 75. günlerde molar ve kesici dişler üzerinden dental plak, alt dudak vestibül mukoza smeari, tükürük ve kan örnekleri alınmıştır. Çürük değerlendirilmesi, 75. günün sonunda anestezi altında sakrifiye edilen ratların alt ve üst çene dişlerinin çürük boyayıcı solüsyonlar ile boyanıp, çürük alanı oranlarının hesaplanması ile yapılmıştır. Biyouyumluluk deneyi için 12 adet rat randomize olarak 2 gruba ayrılmıştır. Ratların sırt bölgelerine çalışma grubunda nano gümüş partikülleri ile kaplanan ortodontik braketler, kontrol grubunda ise konvansiyonel ortodontik braketler yerleştirilmiş ve 7, 14, 30 ve 60. günlerde çevre yumuşak dokuları ile beraber çıkarılıp histopatolojik olarak değerlendirilmiştir. Sonuçlarımıza göre çalışma grubunda özellikle 1 ay sonunda braket etrafında S. mutans sayılarının anlamlı derecede azaldığı, molar diş parlak yüzeylerinde çürük oluşumunun önemli düzeyde önlendiği saptanmıştır. Tükürük ve kan örneklerinde 7. günde gümüş konsantrasyonlarının arttığı sonraki günlerde azaldığı izlenmiştir. Biyouyumlulukları histopatolojik olarak gösterilen nano gümüş kaplanan ortodontik braketlerin klinik uygulamalarda BNL'lerin önlenmesinde olumlu sonuçlar verebileceği düşünülmektedir.
Özet (Çeviri)
The aims of this study were to evaluate the antibacterial properties, ion release, and the biocompatibility of nano silver coated orthodontic brackets, to assess the possible reduction of the areas of tooth decay and demineralization during fixed orthodontic treatment compared to conventional brackets. Nano silver coating process was applied to the standard orthodontic brackets and were placed on the mandibular incisors of Wistar Albino rats in the study group (6) and the conventional brackets in the control group (6). Dental plaque, mucosal vestibular smears, saliva and blood samples were collected from rats at 0, 1, 3, 7, 14, 30, 45, and 75th days of the study. The amount of silver ions in blood and saliva was measured and microbiological evaluation was made in the samples of smear and dental plaque for S. mutans. For testing cariogenicity, all rats were sacrified under anesthesia at the end of 75 days. First of all, the soft tissues of both jaws were removed and cleaned and all teeth were stained using a caries indicator, then the caries ratio was assessed. In the biocompatibility study, nano silver coated and standard brackets were aseptically implanted subcutaneously in the dorsal region of rats. Brackets were removed with the surrounding tissues at 7, 14, 30, and 60 days. The specimens were evaluated for inflammatory response. Results showed that nano coated orthodontic bracket favored the inhibition of S. mutans on day 30 and reduction of caries on the smooth surfaces. Silver counts of saliva and serum samples were significantly higher in study group on day 7 and reduced on following days. The biocompatibility results indicated similarities in terms of tissue reaction between the study and control groups. So we suggest that nano coated orthodontic bracket can be helpful for prevention of WSL during fixed orthodontic treatment.
Benzer Tezler
- Development of multi-layer conductive polymer nanocomposites for electromagnetic shielding application
Elektromanyetik kalkanlama uygulamaları için katmanlı iletken polimer nano kompozitlerinin geliştirilmesi
FATMA ZEHRA ENGİN SAĞIRLI
Doktora
İngilizce
2017
Bilim ve Teknolojiİstanbul Teknik ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
PROF. DR. EYÜP SABRİ KAYALI
PROF. DR. ABDÜLKADİR SEZAİ SARAÇ
- Antibacterial coating of fabrics with nanofibers
Kumaşların antibakteriyel nanoliflerle kaplanması
BURCU ADEMOĞLU
Yüksek Lisans
İngilizce
2011
Tekstil ve Tekstil MühendisliğiGaziantep ÜniversitesiTekstil Teknolojisi Ana Bilim Dalı
PROF. DR. ALİ KİREÇCİ
- In situ synthesis of oil based polymer composites containing silver nanoparticles
Nano gümüş partikülleri içeren yağ bazlı polimer kompozitlerin sentezi
OSMAN EKSİK
Doktora
İngilizce
2009
Kimya Mühendisliğiİstanbul Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. A. TUNCER ERCİYES
- Nano gümüş partikülleri kullanılarak hazırlanan bazı bitki ekstraktlarının sclerotinia sclerotiorum (Lib.) de Bary'e karşı antifungal aktivitesinin belirlenmesi
Determination of antifungal activity of some plant extractsprepared using nano silver particles against sclerotiniasclerotiorum (Lib.) de Bary
SİNEM GÜL CILIZ
Yüksek Lisans
Türkçe
2023
ZiraatTokat Gaziosmanpaşa ÜniversitesiBitki Koruma Ana Bilim Dalı
DOÇ. DR. ABDURRAHMAN ONARAN
- Nano gümüş partikülleri ve Lantana camara L. ekstraktının patates güvesi [Pphthorimaea operculella (Zeller)] ergin öncesi dönemlerine karşı etkinliği
Efficacy of nano silver particules and Lantana camara L. extract against pre-adult stages of potato moth [Phthorimaea operculella (Zeller)]
ERHAN GÜLSOY
Yüksek Lisans
Türkçe
2021
ZiraatTokat Gaziosmanpaşa ÜniversitesiBitki Koruma Ana Bilim Dalı
DR. ÖĞR. ÜYESİ AYŞE YEŞİLAYER