CAD/CAM kullanılarak farklı seramik materyallerinden hazırlanan inley restorasyonların kuvvet altındaki davranışlarının mekanik ve sonlu elemanlar stres analizi yöntemleriyle incelenmesi
The investigation of behaviour of inlay restorations prepared from different ceramic materials using CAD/CAM with mechanical and finite element stress analysis methods under loading
- Tez No: 426874
- Danışmanlar: PROF. DR. MEHMET YILDIZ
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Makine Mühendisliği, Dentistry, Mechanical Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2014
- Dil: Türkçe
- Üniversite: Atatürk Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 107
Özet
Amaç: Bu çalışmamızın amacı; farklı içeriklere sahip seramik inleylerin kırılma dayanımlarının in vitro olarak ve sonlu elemanlar yöntemi kullanılarak değerlendirilmesidir. Materyal ve Metot: Yapay bir diş üzerinde MOD inley kavitesi hazırlandı ve ölçü alınarak 50 adet özdeş metal analog üretildi. İnleyler, 5 farklı CAD/CAM seramikten (bir feldspatik seramik, Cerec Blocs; bir lösitle güçlendirilmiş seramik, IPS Empress CAD; iki rezin nano seramik, 3M ESPE Lava Ultimate ve VITA Enamic; bir lityum disilikat seramik, IPS e.max CAD) CEREC 4 CAD/CAM sistemi kullanılarak elde edildi (n=10, N=50). Örnekler metal analoglara bir rezin simanla (3M ESPE U200) yapıştırıldı. Üniversal test cihazı kullanılarak inleylerin kırılma testleri gerçekleştirildi. Veriler SPSS 20 istatistik yazılımı ile analiz edildi. Deney şartları, sonlu elemanlar analizi yazılımına (ANSYS Workbench) aktarılarak değerlendirildi. Aynı zamanda inleyler için 400 N yük altında, sonlu elemanlar yöntemi kullanılarak gerilme analizi gerçekleştirildi. Bulgular: Lityum disilikat inleylerin kırılma dayanımı (3949 N) diğer inleylere göre önemli derecede daha yüksek bulundu (p0.05). Sonlu elemanlar gerilme analizi sonuçları, inleylerin kırılma dayanımlarının ölçüldüğü deney sonuçlarını doğrular nitelikteydi. 400 N yük altında en yüksek gerilme lityum disilikat seramik inleyde oluşurken, en düşük gerilmeler rezin nano seramik inleylerde oluştu. Sonuç: Mekanik olarak, inleylerin ağızda oluşan kuvvetlere dayanabilecekleri gösterilmiştir. Sonlu elemanlar yöntemi kullanılarak gerçekleştirilen gerilme analizlerinden elde edilen sonuçlar, mekanik analizlerle uyumlu bulunmuştur.
Özet (Çeviri)
Aim: The purpose of this study was to examine the fracture strength of ceramic inlays in vitro and using finite element analysis. Material and Method: MOD inlay cavity was prepared on an artificial tooth and 50 identical metal analogues were produced by taking impression from cavity. Inlays were made from five different CAD/CAM ceramics (a feldspathic ceramic, Cerec Blocs; a leucite-reinforced ceramic, IPS Empress CAD; two resin nano ceramics, 3M ESPE Lava Ultimate and VITA Enamic; a lithium disilicate ceramic, IPS e.max CAD) using CEREC 4 CAD/CAM system. Samples were adhesively cemented to metal analogues with a resin cement (3M ESPE, U200). The fracture tests were carried out with an universal testing machine. Data were analyzed with statistics software SPSS 20. Experimental conditions were evaluated by transferring to a finite element analysis software (Ansys Workbench). Also finite element analysis were performed for inlays under 400 N load. Results: Fracture strength of lithium disilicate inlays (3949 N) was found to be higher than other ceramic inlays (p0.05). Finite element stress analysis confirmed the results of experiments that measured the fracture strength of inlays. The highest stress was formed in lithium disilicate ceramics while the lowest stress was in resin nano ceramics under 400 N load. Conclusion: Fracture strength results demonstrate that inlays can withstand the forces in the mouth. The results of finite element stress analysis were found to be compatible with mechanical analysis.
Benzer Tezler
- Lamina restorasyonlarında kullanılan seramiklerin rengi ile ışık geçirgenliğinin ve rezin siman renginin, restorasyonların renk uyumuna etkisi
Effect of color and tranclucency of ceramics and color of resin cements on the final color of laminate veneers
ECE ŞENGÜN
- CAD-CAM materyalleri ile üretilen implant üstü restorasyonların farklı siman aralıklarındaki stres dağılımlarının karşılaştırılması
Comparison of stress distributions in different cement thicknesses of implant- retained fixed restorations produced with current CAD-CAM materials
RAZİYE YILDIZ
Diş Hekimliği Uzmanlık
Türkçe
2021
Diş HekimliğiEge ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. AYŞE GÖZDE TÜRK
- CAD/CAM yardımıyla kişiye özel hazırlanmış polietereterketon post-korların kırılma dayanımlarının değerlendirilmesi
Evaluation of the fracture strength of CAD/CAM milled custom polyetheretherketone dental post-cores
AYETULLAH DİREK
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiFırat ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ SAMET TEKİN
- CAD/CAM seramiklerinin fonksiyon sonrası oluşan mekanik değişikliklerinin değerlendirilmesi
Evaluation of phisical changes of CAD/CAM materials after function
MEHMET MERT ÖZCAN
Doktora
Türkçe
2018
Diş Hekimliğiİstanbul ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. TAYFUN BİLGİN
- Farklı renklerdeki rezin simanların çeşitli monolitik cad/cam materyallerin sonuç rengi üzerine etkisi
The effect of different colors of resin cements on the final color of various monolithic cad/cam materials
NEŞE CIZIROĞLU
Doktora
Türkçe
2022
Diş Hekimliğiİstanbul Aydın ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ERMAN BÜLENT TUNCER