Farklı uygulama tekniklerinin self-ETCH modunda kullanılan universal adezivlerin dentindeki mikrogerilme bağlanma dayanımına etkisinin araştırılması

Evaluation of the effects of different application techniques on the dentin microtensile bond strength of universal adhesives used in self ETCHmode

PDF İndir

  1. Tez No: 454126
  2. Yazar: MUHİTTİN UĞURLU
  3. Danışmanlar: PROF. DR. RABİA BANU ERMİŞ
  4. Tez Türü: Diş Hekimliği Uzmanlık
  5. Konular: Diş Hekimliği, Dentistry
  6. Anahtar Kelimeler: Dental bonding, Dental materyaller, Dental restorasyon, Dental stres analizi, Dental çimentolar, Dentin, Dental bonding, Dental materials, Dental restoration, Dental stress analysis, Dental cements, Dentin
  7. Yıl: 2016
  8. Dil: Türkçe
  9. Üniversite: Süleyman Demirel Üniversitesi
  10. Enstitü: Diş Hekimliği Fakültesi
  11. Ana Bilim Dalı: Restoratif Diş Tedavisi ve Endodonti Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: Belirtilmemiş.

Özet

Bu in vitro çalışmanın amacı, farklı uygulama tekniklerinin self-etch modunda kullanılan universal adezivlerin dentindeki mikrogerilme bağlanma dayanımına etkisinin araştırılmasıdır. Seksen adet çekilmiş diş randomize olarak gruplara ayrıldı (n=10): CSE; Clearfil SE Bond, XTR; Optibond XTR, CUB; Clearfil Universal Bond, CUB+CSEbond1; Clearfil Universal Bond (polimerizasyon var)+Clearfil SE Bond bond, CUB+CSEbond2; Clearfil Universal Bond (polimerizasyon yok)+Clearfil SE Bond bond, SBU; Single Bond Universal, SBU+CSEbond1; Single Bond Universal (polimerizasyon var)+Clearfil SE Bond bond, SBU+CSEbond2; Single Bond Universal (polimerizasyon yok)+Clearfil SE Bond bond. Adeziv uygulamayı takiben dentin yüzeylerinde bir nanohibrit kompozit rezin (Filtek Ultimate) ile 5-6 mm yüksekliğinde üst yapılar hazırlandı. Preparasyonu yapılan 1.0x1.0 mm genişliğindeki ve 8-9 mm uzunluğundaki örnekler, 1 mm/dk'lık hızda 100 N'luk gerilme kuvveti uygulanarak test edildi. Başarısızlık tiplerinin analizi stereomikroskop ve taramalı elektron mikroskobu ile yapıldı. Elde edilen sonuçlar istatistiksel olarak karşılaştırıldı (p=0.05). Dentindeki mikrogerilme bağlanma dayanımı değerleri CSE; 47.08±3.12 MPa, XTR; 45.38±6.54 MPa, CUB; 28.87±14.72 MPa, CUB+CSEbond1; 32.03±11.44 MPa,CUB+CSEbond2; 30.56±13.02 MPa, SBU; 30.81±13.18 MPa, SBU+CSEbond1; 33.84±11.92 MPa ve SBU+CSEbond2; 32.00±12.46 MPa olarak saptandı. İki basamaklı self-etch adezivlerin mikrogerilme bağlanma dayanımı değerleri, universal adezivlerin mikrogerilme bağlanma dayanımı değerlerinden istatistiksel olarak daha yüksek bulundu (ANOVA, Tukey's HSD, p<0.05). Farklı uygulama teknikleri ile kullanılan universal adezivlerin mikrogerilme bağlanma dayanımı değerleri arasında istatistiksel olarak anlamlı bir fark saptanmadı (ANOVA, Tukey's HSD, p>0.05). Self-etch modunda kullanılan universal adezivler ile birlikte çözücü içermeyen hidrofobik bir bonding ajanın ayrı bir tabaka halinde uygulanmasının ve bonding ajan uygulanmasından önce adeziv rezinin ışık ile polimerize edilip edilmemesinin, universal adezivlerin dentindeki mikrogerilme bağlanma dayanımını etkilemediği sonucuna varılabilir.

Özet (Çeviri)

The aim of this in vitro study was to investigate the effect of different application techniques/procedures on the microtensile bond strength of universal adhesives to dentin used in self etch mode. Eighty extracted third molars were randomly divided into eight experimental groups. (n=10): CSE; Clearfil SE Bond, XTR; Optibond XTR, CUB; Clearfil Universal Bond, CUB+CSEbond1; Clearfil Universal Bond (with light curing)+Clearfil SE Bond bond, CUB+CSEbond2; Clearfil Universal Bond without light curing)+Clearfil SE Bond bond, SBU; Single Bond Universal, SBU+CSEbond1; Single Bond Universal (with light curing)+Clearfil SE Bond bond, SBU+CSEbond2; Single Bond Universal (without light curing)+Clearfil SE Bond bond. Nanofilled composite resin (Filtek Ultimate) blocks in height of 5-6 mm were prepared on the dentine surfaces after the application of adhesive resins. The prepared samples, 1.0x1.0 in width and 8-9 mm in length, were tested by applying 100 N tensile forces at 1mm/min speed. The resin dentin interfaces and the fracture modes were evaluated using a stereomicroscop and SEM. ANOVA and Tukey's HSD test were performed for the statistical analysis of the data (p=0.05) The microtensile bond strength values were determined as CSE; 47.08±3.12 MPa, XTR; 45.38±6.54 MPa, CUB; 28.87±14.72 MPa, CUB+CSEbond1; 32.03±11.44 MPa,CUB+CSEbond2; 30.56±13.02 MPa, SBU; 30.81±13.18 MPa, SBU+CSEbond1; 33.84±11.92 MPa ve SBU+CSEbond2; 32.00±12.46 MPa. The microtensile bond strength values of the two step self-etch adhesives were significantly higher than the universal adhesives' values (ANOVA, Tukey's HSD, p<0.05). There were no significant differences between the microtensile bond strength values of the universal adhesives using with different application tehniques (ANOVA, Tukey's HSD, p>0.05). Within the limits of this study; it might be concluded that the application of hydrophobic resin as a separate layer with universal adhesive resins used in self etch mode and whether the adhesive resin polymerize prior to application of the bonding agent do not effect the microtensile bond strength of the universal adhesives to dentine used in self etch mode.

Benzer Tezler

  1. Tez No

    960525

    Farklı kavite derinliklerinde inlay restorasyonların rezin simanlarla yapıştırıldıktan sonra marjinal ve internal uyumunun mikro-CT ile incelenmesi

    Evaluation of the marginal and internal adaptation of inlay restorations cemented with resin cements at different cavity depths using micro-CT

    BEYZA KOÇ

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2025

    Diş HekimliğiAnkara Yıldırım Beyazıt Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. FİLİZ AYKENT

  2. Tez No

    871277

    Komplike olmayan kron kırıklarının tedavisinde insizal fragmanınreataçmanında kullanılan universal adezivlerin farklı uygulamatekniklerinin ve ph'larının kırılma dayanımı üzerine etkisininaraştırılması

    The effect of different application techniques and ph values of universaladhesives used in the reattachment of incisal fragment of non-complicated crownfractures on fracture strength

    ZEYNEP BAĞDATLI

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2024

    Diş HekimliğiHacettepe Üniversitesi

    Restoratif Diş Tedavisi Ana Bilim Dalı

    DOÇ. DR. UZAY KOÇ VURAL

  3. Tez No

    939142

    Adeziv uygulama tekniklerinin dentine mikrogerilim bağlanma dayanımı üzerine etkisi

    Effect of adhesive application techniques on microtensile bond strength to dentin

    ALPASLAN CAN ÇELİK

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2025

    Diş HekimliğiSelçuk Üniversitesi

    Restoratif Diş Tedavisi Ana Bilim Dalı

    PROF. DR. NİMET ÜNLÜ

  4. Tez No

    929770

    Manuel lenfatik drenajın farklı tutuş tekniklerinin üst ve alt ekstremitede lokal dokudaki su oranı ve doku kalınlığına etkisinin karşılaştırılması

    Comparison of the effects of different gripping techniques of manual lymphatic drainage on the local tissue water ratio and tissue thickness in the upper and lower extremities

    ŞEYMA ÖZMEN

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    Fizyoterapi ve RehabilitasyonGazi Üniversitesi

    Fizyoterapi ve Rehabilitasyon Ana Bilim Dalı

    PROF. DR. İLKE KESER

  5. Tez No

    941809

    A few-shot learning with self-knowledge distillation approach for medical image recognition

    Tıbbi görüntü tanıma için kendinden bilgi damıtmı yaklaşımı ile birkaç atımda öğrenme

    MOHAMED EL HACEN HABIB

    Doktora

    İngilizce

    İngilizce

    2025

    Elektrik ve Elektronik MühendisliğiKocaeli Üniversitesi

    Elektronik ve Haberleşme Mühendisliği Ana Bilim Dalı

    PROF. DR. OĞUZHAN URHAN

Geri Dön