Basınç kontrollü Cu-bazlı şekil hafızalı alaşımların üretimi ve karakterizasyonu

The production and characterization of pressure controlled Cu-based shape memory alloys

PDF İndir

  1. Tez No: 458026
  2. Yazar: TERCAN POLAT
  3. Danışmanlar: DOÇ. DR. CANAN AKSU CANBAY
  4. Tez Türü: Yüksek Lisans
  5. Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2017
  8. Dil: Türkçe
  9. Üniversite: Fırat Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Fizik Ana Bilim Dalı
  12. Bilim Dalı: Genel Fizik Bilim Dalı
  13. Sayfa Sayısı: 108

Özet

Bu çalışmada ergitme yöntemiyle elde edilen Cu- 22,90 Al - 4,87 Mn - 0,90 Ni (% at.) kompozisyonuna sahip dörtlü şekil hafızalı alaşımın uygulanan farklı basınçlar altında yapısında meydana gelen değişimler ve termal davranışları incelendi. Bu incelemeler için X-ışınları kırınımı (XRD) analizleri, optik mikroskop gözlemleri, diferansiyel termal analiz (DTA) ve diferansiyel taramalı kalorimetri (DSC) analiz yöntemleri kullanıldı. XRD metoduyla numunelerin sahip oldukları kristal yapılar ve difraksiyonu meydana getiren düzlemler belirlendi. Oda sıcaklığında alınan optik mikroskop gözlemleriyle numunelerde uygulanan basınçlar sonucunda martensit yapının oluşup oluşmadığı ve martensit yapıların çeşitleri gözlendi. DTA ölçümleriyle numunelerde düşük sıcaklık bölgesinde ve yüksek sıcaklık bölgesinde meydana gelen faz geçişleri ve faz geçiş sıcaklıkları belirlendi. DSC ölçümleriyle martensitik dönüşümün sıcaklık parametreleri olan Ms, Mf, As ve Af sıcaklıklarının, uygulanan basınçlarla nasıl değiştiği incelendi. XRD analizleri sonucunda kullanılan numunelerin kristal yapılarının ortorombik yapıya sahip olduğu bulunmuştur. Yapılan hesaplamalar sonucunda kristal yapının a, b ve c parametreleri hesaplanmış, uygulanan basınçlarla birlikte a parametresinin değerinin arttığı, b ve c parametrelerinin ise azaldığı görülmüştür. Ayrıca Debye-Scherer eşitliğinden kristal boyutları hesaplanmıştır. Optik mikroskop gözlemlerinde uygulanan basıncın arttırılmasıyla birlikte martensit oluşumların azaldığı ve son basınç değerinde martensit yapıların oluşmadığı gözlemlenmiştir. DTA analizleriyle faz geçişleri belirlenmiş, faz geçişlerinin A2→B2→18R veya A2→B2→L21→18R şeklinde meydana geldiği görülmüştür. Son basınç değerinde martensit yapıya geçiş olmadığı görülmüştür. DSC ölçümleri sonucunda martensit ve austenit faz dönüşüm sıcaklıkları belirlenmiştir. Basınç değerlerinin artmasıyla beraber dönüşüm sıcaklıklarının arttığı görülmüştür. Fakat 560 MPa basınç uygulanmış numunenin kristal boyutu diğerlerine göre çok büyük olmasından dolayı istenilen sonuç bu numunede olmamıştır. Son basınç değerinde ise dönüşüm olmadığı görülmüştür.

Özet (Çeviri)

In this work, the structural evolations and thermal behavior of Cu- 22,90 Al - 4,87 Mn - 0,90 Ni (% at.) quaternary shape memory alloy, which was produced by are melting, were investigated by applying different pressure values. For these investigations, X-Ray analysis, optical microscope observations, differential thermal analysis (DTA) and differential scanning calorimetry (DSC) methods were used. The crystal structure and difraction planes of the samples were determined by X-Ray measurements. The structure of the samples according to applying different pressure values was investigated by optical microscope analysis at room temperature. The phase transitions from low temperature to high temperature were determined by DTA measurements. The characteristic phase transition temperatures as Ms, Mf, As and Af were determined by DSC measurements. It was found that the crystal structur of the samples are ortotombic according X-Ray analysis results. As a result of the calculations, the a, b and c parameters of the crystal structure were calculated and it was observed that the value of a parameter increased and the values of b and c parameters decreased. Besides this, the crystal size were determined by using Debye-Scherer equation. In optical microscopy observations, it was observed that the martensite formation was decreased by the increase of pressure value and there was no martensite formation observed in last pressure value. The phase transitions were determined by DTA analysis and phase transitions occured in the format A2→B2→18R or A2→B2→L21→18R. The martensite and austenite phase transformation temperatures were determined by DSC. It was observed that, the phase transitions temperatures increased by the increase of pressure value. But the sample which 560 MPa pressure applied,not give the desined result due to the bigger crystal size according to other samples. At last pressure value it was seen that no transformation occured.

Benzer Tezler

  1. Tez No

    467252

    Mineralogy and geochemistry of gossans developed on selected Kuroko–type VMS deposits occuring in eastern pontides (NE Turkey)

    Doğu pontitler (KD Türkiye)'de bulunan seçilmiş bazı Kuroko-tipi VMS yatakları üzerinde gelişen gossanların mineralojisi ve jeokimyası

    SHAIG HAMZALIYEV

    Yüksek Lisans

    İngilizce

    İngilizce

    2017

    Jeoloji Mühendisliğiİstanbul Teknik Üniversitesi

    Jeoloji Mühendisliği Ana Bilim Dalı

    PROF. DR. EMİN ÇİFTÇİ

  2. Tez No

    364151

    Microwave assisted synthesis of PAMAM type dendrimers and their analytical applications

    PAMAM tipi dendrimerlerin mikrodalga destekli sentezi ve analitik uygulamaları

    ALİ SEROL ERTÜRK

    Doktora

    İngilizce

    İngilizce

    2014

    KimyaYıldız Teknik Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. ABDÜRREZZAK EMİN BOZDOĞAN

    DOÇ. DR. METİN TÜLÜ

  3. Tez No

    55659

    Transiet contact analysis of a hermetic reciprocating compressor valve

    Başlık çevirisi yok

    İBRAHİM YILDIRIM

    Yüksek Lisans

    İngilizce

    İngilizce

    1996

    Makine Mühendisliğiİstanbul Teknik Üniversitesi

    PROF.DR. H. TEMEL BELEK

  4. Tez No

    439654

    Comparative effects of Ni-Co addition and milling parameters on corrosion resistance behavior of W-Cu based P/M alloys

    Nikel-kobalt ilavesi ve öğütme parametrelerinin toz metalurjisiyle üretilmiş tunsgten-bakır alaşımlarında korozyon direnci davranışına etkisinin karşılaştırmalı incelemesi

    FULYA BAŞAK KUMKUMOĞLU

    Yüksek Lisans

    İngilizce

    İngilizce

    2016

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DOÇ. DR. BURAK ÖZKAL

    DOÇ. DR. YAMAN ERARSLAN

  5. Tez No

    909010

    Production and characterization of al-CoCrFeNi-M (M=Mo, Cu, Mn) high entropy alloys by combustion synthesis method

    Al-CoCrFeNi-M (M=Mo, Cu, Mn) yüksek entropili alaşımlarının yanma sentezi yöntemiyle üretimi ve karakterizasyonu

    FARUK KAYA

    Doktora

    İngilizce

    İngilizce

    2024

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    PROF. DR. CEVAT BORA DERİN

Geri Dön