Geri Dön

Polimer-organokil nanokompozitlerin sentezlenmesi, mekanik ve morfolojik özelliklerinin incelenmesi

Synthesis of polymer-organoclay nanocomposites, investigation of their mechanical and morphological

  1. Tez No: 473142
  2. Yazar: MERVE ARAS ERDOĞAN
  3. Danışmanlar: PROF. DR. FATİH MENGELOĞLU
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya, Chemistry
  6. Anahtar Kelimeler: Kompozit, Nanokompozit, Polimer–kil nanokompozitleri Kimyasal Modifikasyon, Fiziksel Modifikasyon, Composite, Nanocomposite, Polymer-clay Nanocomposite, Chemical Modification, Physical Modification
  7. Yıl: 2017
  8. Dil: Türkçe
  9. Üniversite: Kahramanmaraş Sütçü İmam Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 110

Özet

Bu tez çalışmasında, sentezlenen organokil ve aktive edilen kil numuneleri ile polimer-kil nanokompozitleri üretilmiştir. Setiltriamonyum bromür (CTAB) ve Hekzadesiltrimetoksisilan (HTMS) organokil sentezlenmiş ve asit aktivasyonu ve soda aktivasyonu yapılmıştır. Modifiye edilen killerin polikaprolakton (PCL) ile %'5'lik kompozitleri üretilmiş olup, çekme direnç özellikleri incelenmiştir. Çekme direnç özellikleri incelendiğinde, asit ile aktive edilen kille takviye edilen kompozitin en iyi sonuç verdiği tespit edilmiştir. Farklı oranlarda kil kullanımının etkisini belirlemek amacıyla %5 kil kullanımına ilave olarak %2,5, %7,5, %10 kil kullanılarak polimer/kil nanokompozitleri üretilmiştir. Modifiye ve aktive edilen kil numuneleri katyon değişim kapasitesi (KDK), SEM, TGA, XRF ve FTIR analizleri ile değerlendirilmiştir. Ayrıca üretilen kompozitlerin mekanik, morfolojik ve termal özellikleri değerlendirilmiş ve analiz sonuçları sunulmuştur. Organokil sentezi ve soda aktivasyonu başarılı bir şekilde gerçekleştirilmiştir. Asit ve soda aktivasyonu killerin KDK değerlerini arttırmıştır. Asit aktivasyonu ile oktahedron tabakaların çözünerek geriye tetrahedron iskeletinin kaldığı tespit edilmiştir. Kil numunelerinin XRD sonuçlarına göre ise organokillerde karışık mikro-yapı gözlenmiştir. TGA sonuçlarına göre asit aktive edilmiş kilin bozunma sıcaklığının düştüğü fakat kalıntı madde miktarının arttığı görülmüştür. SEM analizi ile morfolojik özellikler incelenmiştir. Yoğunluk analizi yapılmış ve çekme direnç özellikleri ile ilişkilendirilmiştir.

Özet (Çeviri)

In this thesis, polymer-clay nanocomposites were synthesized using synthesized organoclay and activated clay samples. Organocyl was synthesized with Cetyltriammonium bromide (CTAB) and Hexadecyltrimethoxysilane (HTMS) and acid and soda activation was performed. The modified clays were used as filling materials in PCL (polycaprolactone) matrix (level of use of clays were 5% in composites.) and their tensile strenght properties were investigated. When the tensile strength properties were examined, it was found that the composite reinforced with acid-activated clay exhibited the best results. Addition to 5% clay usage, 2,5%, 7,5% and 10% clay were used in polymer/clay nanocomposites to determine how composite performances were affected. The synthesized organoclays and activated clay samples were evaluated by KDK (cation exchange capacity), SEM, TGA, XRF and FTIR analyzes. In addition, the mechanical, morphological and thermal properties of composites were evaluated and the results were presented. Synthesis of organoclay and soda activation has been successfully accomplished. Clay have repeating units of octahedron and tetrahedron layers. By acid activation, the octahedron layers were dissolved leaving only tetrahedron skeleton. According to the XRD results of the clay samples, mixed microstructure was observed in the organoclays. According to the results of TGA, it was observed that the amount of residue increased when decomposition temperature of acid-activated clay decreased. Morphological characteristics were examined by SEM analysis. Density analyzes of composites were performed and correlated with tensile strength properties.

Benzer Tezler

  1. Organokil takviyeli melamin formaldehit köpüklerin (OKMFK) mikrodalga ışınlama tekniği ile sentezi ve karakterizasyonu

    The synthesis and characterization by microwave irradiation technique of organoclay-reinforced melamine formaldehyde foams (OCMFF)

    ELİF ŞAHİN

    Doktora

    Türkçe

    Türkçe

    2024

    Polimer Bilim ve TeknolojisiAtatürk Üniversitesi

    Nanobilim ve Nanomühendislik Ana Bilim Dalı

    PROF. DR. AHMET GÜRSES

  2. Molecular dynamics simulations on the structure and interfacial interactions of polyethylene-organoclay nanocomposites

    Polietilen-organokil nanokompozitlerinin yapısal özelliklerinin ve arayüzey etkileşimlerinin moleküler dinamik simülasyon yöntemleriyle incelenmesi

    EROL YILDIRIM

    Doktora

    İngilizce

    İngilizce

    2011

    Kimyaİstanbul Teknik Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. MİNE YURTSEVER

  3. Hibrit poliimidlerin piridin temelli monomerlerden sentezlenmesi ve özelliklerinin incelenmesi

    Synthesis of hybrid polyimides from pyridine based monomers and investigation of their properties

    SÜLEYMAN KÖYTEPE

    Doktora

    Türkçe

    Türkçe

    2007

    Kimyaİnönü Üniversitesi

    Kimya Bölümü

    PROF.DR. TURGAY SEÇKİN

  4. Polimer/kil nanokompozitlerin hazırlanması mekanik ve termal özelliklerinin incelenmesi

    The preparation of the polymer / clay nanocomposites and the examination of mechanical and thermal properties

    KÜBRA GÜNEŞ

    Doktora

    Türkçe

    Türkçe

    2015

    KimyaAtatürk Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. AHMET GÜRSES

    PROF. DR. SEMRA KARACA

  5. Kil/PVA ve organokil/PVA nanokompozitlerin sentezi ve karakterizasyonu

    Preparation, characterization of clay/PVA and organoclay/PVA nanocomposites

    SEVİM İŞÇİ

    Doktora

    Türkçe

    Türkçe

    2007

    Fizik ve Fizik Mühendisliğiİstanbul Teknik Üniversitesi

    Fizik Ana Bilim Dalı

    PROF.DR. NURFER GÜNGÖR