Farklı dental porselen sistemlerinin aşınma ve renk değişimlerinin araştırılması
Investigation of the wear and color changes of different dental porcelain
- Tez No: 480946
- Danışmanlar: PROF. DR. GİRAY BOLAYIR
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental materyaller, Dental porselen, Diş aşınması, Diş erozyonu, Diş renk değişikliği, Yüzey pürüzlülüğü, Zirkonyum, Çiğneme, Dental materials, Dental porcelain, Tooth abrasion, Tooth erosion, Tooth discoloration, Surface roughness, Zirconium, Mastication
- Yıl: 2017
- Dil: Türkçe
- Üniversite: Cumhuriyet Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada, günümüzde kullanılan dört farklı porselen sisteminin (düşük ısı feldspatik, monolitik zirkonya, lityum disilikat cam seramik ve lösit cam seramik), farklı yüzey işlemleri (overglaze ve mekanik cila) uygulanması sonucu doğal mine karşısındaki aşınma miktarlarının ve renk değişimlerinin incelenmesi amaçlandı. Tüm porselen grupları, overglaze işlemi uygulanan ve mekanik cila uygulanan iki alt gruba ayrıldı. Bu alt gruplar 8'er porselen örneği içermekteydi. Örnekler, 9 mm çapında ve 3 mm yüksekliğinde daire tabanlı silindirler olarak hazırlandı. Toplam 64 adet porselen örneğinin karşıtı olarak kullanılmak üzere ortodontik veya periodontal endikasyonlar sebebiyle çekilmiş, doku kaybına uğramamış, çürük ve dolgu bulunmayan 64 adet alt 1. premolar diş hazırlandı. Örneklere, çiğneme simülatöründe (SD Mechatronik Chewing Simulator CS-4.8), 50 N çiğneme kuvveti altında, 1 Hz frekansta, 600.000 çiğneme siklusu ve 10.000 adet 5- 55 °C arasında termal siklus uygulandı. Porselen örneklerin yüzey pürüzlüğü ölçümleri için optik profilometre (Phaze View / Zee Scope, France), Taramalı Elektron Mikroskobu (Tescan / Mira 3 / Çek Cumhuriyeti) , renk değerleri için spektrofotometre (Vita Easyshade Advance / Almanya), karşıt dişlerin ağırlık ölçümleri için hassas tartı (A&D Weighing GR-300 lab balance / ABD) kullanıldı. Çalışmamızın bulguları; zirkonya içerikli porselenlerin, glaze ve mekanik cila işlemi uygulanan gruplarının arasında, aşınma ve aşındırma durumlarında anlamlı bir fark bulunmadı (p>0,05). Lityum disilikat ve lösit porselenlerin, glazeli grupları ile mekanik cilalı gruplarının arasında, aşınma ve aşındırma durumlarında anlamlı bir fark bulundu (p<0,05). Feldspatik porselenlerin, glazeli grupları ile mekanik grupları arasında aşınma değerleri anlamlı farklılığa sahipken (p<0,05) aşındırma değerleri arasında anlamlı bir fark bulunamadı. (p>0,05) Tüm porselenlerin ΔE değerleri istatistiksel olarak anlamlı farklılığa sahip olup (p<0,05), glazeli grupların renk değişim (ΔE) değerleri mekanik gruplara göre fazla olduğu görüldü. Sonuç; Tüm glazeli grupların, mekanik cilalı gruplara göre daha fazla madde kaybettiği ve karşıt dişleri daha fazla aşındırdığı, daha fazla renk değişimine sahip olduğu gözlemlendi. Zirkonya seramikler diğer seramiklere göre az aşınma ve aşındırma gösterdi.
Özet (Çeviri)
The aim of this study was to compare the wear of four type of ceramics (low-fusing feldspathic, monolithic zirconia, lithium disilicate glass and leucite glass ceramic) with different surface treatments (glazed and polished) against enamel. All dental porcelain groups included 8 samle of glazed and 8 sample of polished porcelain. This speciments shape was 9 mm diameter circle based cylindrical with 3 mm height. 64 cavity and filling free mandibular 1st premolar teeth, which were removed due to orthodontic or periodontal indications, were prepared to use as antagonist. Speciments were mechanically loaded in dual-axis chewing simulator and subjected to 600.000 cyles of 50N masticating force each at a frequency of 1 Hz and 10.000 thermal cycles of 5-55 °C. Optical profilometer (Phaze View / Zee Scope, France) and electron microscope Tescan / Mira 3 / Czech Republic) were used for surface roughness measurements, spectrophotometer (Vita Easyshade Advance / Germany) was used for color measurements of porcelain samples. Sensitive digital scale (A&D Weigthing GR-300 lab balance / USA)) was used for weight measurements of antagonist teeth. Results: Wear and abrasion values between glazed and polished groups of zirconia were found statistically non-significant. (p>0,05) Wear and abrasion values between glazed and polished groups of lithium disilicate glass and leucite glass ceramic were found statistically significant. (p<0,05) Wear values between glazed and polished groups of feldspathic ceramic were found statistically significant (p<0,05) but abrasion values were found statistically non-significant. (p>0,05) ΔE changes of all ceramic groups were found statistically significant. (p<0,05) Between glazed and polished group; glazed group showed the more color change. Conclusion: At the end of the study, ıt was observed that glazed groups of ceramics lost more substanse than polished groups and cause more abrasion in antagonist teeth. Also color shift in glazed groups was more than polished groups. Zirconia ceramics showed less lost substanse and cause less abrasion in antagonist teeth.
Benzer Tezler
- Basınçlı teknikle uygulanan dökülebilir seramikle yapılan pivolu kronların invivo ve invitro olarak incelenmesi
Research on crowns with pivot: Applied with castable pressurized ceramic as invivo and invitro
BURCU GÜNDOĞAR
Doktora
Türkçe
1999
Diş HekimliğiGazi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. LEVENT NALBANT
- Seramik bloklarının aşınma performanslarının değerlendirilmesi
Evaluation of wear performance of ceramic blocks
DOĞUKAN ÖZKURT
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş Hekimliğiİzmir Katip Çelebi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ENDER AKAN
- Porselen tamir sistemlerinin altyapı materyallerine olan bağlantı kuvvetinin in-vitro değerlendirilmesi
N vitro evaluation of bond strenght of porcelain repair systems to base materials
HASAN HÜSEYİN KOCAAĞAOĞLU
Doktora
Türkçe
2013
Diş HekimliğiErciyes ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. AYŞEGÜL GÜLERYÜZ GÜRBULAK
- Farklı rezin siman sistemlerinin ve yaşlandırma işleminin porselen lamina restorasyonların rengine etkisinin invitro olarak değerlendirmesi
Invitro evaluation of the effects of different resin cement systems and aging process on the color of porcelain laminate restorations
SEDANUR USTAÖMER
Doktora
Türkçe
2011
Diş HekimliğiKaradeniz Teknik ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. BORA BAĞIŞ
- Farklı yüzey parlatma sistemlerinin çeşitli yapılardaki dental seramiklerin yüzey sertliği ve pürüzlülüğüne etkisinin değişik metotlarla değerlendirilmesi
Evaluation of the effect of different surface polishing systems on the surface hardness and roughness of dental ceramics in various structures by different methods
ESRA İNCESU
Diş Hekimliği Uzmanlık
Türkçe
2018
Diş HekimliğiAtatürk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. NURAN YANIKOĞLU