Kitosan-poliüretan esaslı bileşimlerin çelik ve alüminyum altlıklar yüzeyindeki kendini iyileştirme özelliklerinin incelenmesi

Examination of self-healing properties of chitosan-polyurethane based compounds on steel and aluminium substrates

PDF İndir

  1. Tez No: 505685
  2. Yazar: ORHAN DİNÇER
  3. Danışmanlar: PROF. DR. NURHAN CANSEVER
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2018
  8. Dil: Türkçe
  9. Üniversite: Yıldız Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Malzeme Bilim Dalı
  13. Sayfa Sayısı: 95

Özet

Malzemelerin kendi kendini iyileştirme özellikleri, çizilme, aşınma veya yırtılma sonunda meydana gelen hasarların malzemenin kendisi tarafından onarılması, başka bir deyişle hasar öncesi durumuna benzer yapıya geri dönmesidir. Bu özellikten yararlanılarak metalik yüzeyleri dış ortamın olumsuz etkilerine karşı korumak ve malzemenin estetik görüntüsünü muhafaza etmek için kaplamalar geliştirilmiştir. Kaplamanın çizilmesi durumunda açığa çıkan metal yüzeyi, kaplamanın ısı, ışık ve sıcaklık gibi katalizör yardımıyla kendini onarması sayesinde korunmaya devam eder. Bu çalışmanın amacı, kendini iyileştirme özelliği olduğu bilinen kitosan-poliüretan esaslı kaplamanın kullanıldığı farklı bileşimler hazırlamak ve bu bileşimleri çelik (AISI 1040) ve alüminyum (AA 7178) altlıklar yüzeyine uygulayarak kendini iyileştirme özelliğini takip ve tespit etmektir. Bu amaç doğrultusunda 3 farklı karışım hazırlanmış ve önce bunların metal yüzeyleri kaplama özellikleri incelenmiştir. Daldırma yöntemi ile hazırlanan kaplamalarda homojen kalınlık elde edilemediğinden döndürerek kaplama yöntemi de denenmiştir. Kaplamaların karakterizasyonu çalışmalarında kalınlık ölçümü, gözle inceleme ve elektrokimyasal deneyler kullanılmıştır. Kaplamaların kendilerini iyileştirme özelliğini belirlemek için kaplama yüzeyi keskin bir uçla metal numuneye değecek şekilde çapraz çizilmiş, çizildikten hemen sonra, belirli sürelerde bekletildikten sonra gözle ve optik mikroskop ile inceleme, tuzlu suda bekletme ve elektrokimyasal deneyler yapılmıştır. Polarizasyon eğrilerinde korozyon potansiyelinin çizik sonrası aktif yönlere kayması ve farklı sürelerde bu değerlerde kalması, çizikli kaplamanın yüzeyi korumadığını göstermiştir. Bu da kaplama bileşiminin deney süresince kendini iyileştirmediğini göstermektedir. Deneysel verilere destek sağlamak amacıyla kendini iyileştirme özelliği olan CorrosionX Heavy Duty isimli kaplama ürünü alınmış ve püskürtme yöntemiyle çelik ve alüminyum altlıklara uygulanmıştır. Karakterizasyon çalışmaları hazırladığımız kitosan-poliüretan kaplamalarla aynı şekilde uygulanmıştır. Bu ürün ile yapılan deney sonuçları, CorrosionX Heavy Duty'nin metal yüzeyleri koruduğu, çiziklerde kendini iyileştirdiğini göstermiştir.

Özet (Çeviri)

Self-healing features of the materials are repair of the damage caused by scratching, abrasion or rupture, in other words return to a structure similar to the pre-damage situation. Benefiting from this feature, coatings have been developed to protect metallic surfaces against external enviromental effects and preserve the aesthetic appearance of the material. In case of scratching the coatings, exposed metal surface continues to be protected by self-reapair of the coatings by means of a catalyst such as heat, light and temperature. The purpose of this study, to prepare different compostions using the chitosan-polyurethane based coatings known to be self-healing feature and to observe and determine the self-healing feature by applying these compostions to the surfaces of steel (AISI 1040) and aluminum (AA 7178) substrates. In accordance wth this purpose, three different mixtures were prepared and first, their featrures of coatings metal surface have been examined. Since homogeneous thickness can not be obtained in coatings prepared by dip coating method, the spin coating method also been tried. Thickness measurement, visual inspection and electrochemical experiments were used in the characterizastion studies of coatings. In order to determine the self-healing features of the coatings, the coatings surface is cross-scratched in such a way that it touches the metal sample with a sharp tip, then immediately after scratched, after waiting for a certain period of time, visual and optical microscope examination, salt water immersion and electrochemical experiments were performed. Experimental results have shown that some compositions are not suitable for steel surface. Corrosion products were found after coating on steel surface Since there is no significant change in aluminum samples, electrochemical experiments were performed in these samples. It showed that the scratched coatings do not protect the metal surface due to the corrosion potentials in the polarization curves go into active directions after scratching and remain at these values at different times. This shows that compostion of the coating can not heal itself during the experiment. In order to provide support to experimental data, CorrosionX Heavy Duty commercial product known to be self-healing purchased and then applied to steel and aluminum substrates by spraying. Characterization studies have been performed in the same way as chitosan-polyurethane coatings. Experimental results with this product show that CorrosionX Heavy Duty protects metal surfaces and heals after scratching.

Benzer Tezler

  1. Tez No

    138821

    Protein liflerinin (yün, ipek) terbiyesinde enzimlerin kullanımı

    Using of enzymes on treatment of protein fibers (wool, silk)

    NURHAN ONAR

    Yüksek Lisans

    Türkçe

    Türkçe

    2003

    Tekstil ve Tekstil MühendisliğiDokuz Eylül Üniversitesi

    Tekstil Bilimleri Ana Bilim Dalı

    YRD. DOÇ. DR. MERİH SARIIŞIK

  2. Tez No

    352583

    Biyomedikal poliüretan sentezi ve antibakteriyel etkinliğinin geliştirilmesi

    Synthesis of biomedical polyurethane and improve its antibacterial activity

    FİLİZ KARA

    Doktora

    Türkçe

    Türkçe

    2014

    KimyaGazi Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. SERPİL AKSOY

    PROF. DR. NESRİN HASIRCI

  3. Tez No

    741060

    Double layer thermoplastic polyurethane-gelatin electrospun wound dressings for biomedical applications

    Biyomedikal uygulamalarda kullanılmak üzere elektroeğirme yöntemiyle üretilmiş termoplastik poliüretan-jelatin içeren çift katmanlı yara örtüsü

    ARZU YILDIRIM

    Yüksek Lisans

    İngilizce

    İngilizce

    2022

    Kimyaİstanbul Teknik Üniversitesi

    Polimer Bilim ve Teknolojisi Ana Bilim Dalı

    PROF. DR. FATMA SENİHA GÜNER

    PROF. DR. MELEK MÜMİNE EROL TAYGUN

  4. Tez No

    154140

    Tekstil yapay damarlarının performans özelliklerine yapısal parametrelerinin etkisi

    Effects of structural parameters on the performance properties of textile vascular prostheses

    SEMİHA EREN

    Yüksek Lisans

    Türkçe

    Türkçe

    2004

    Tekstil ve Tekstil MühendisliğiUludağ Üniversitesi

    Tekstil Mühendisliği Ana Bilim Dalı

    DOÇ.DR. YUSUF ULCAY

  5. Tez No

    526550

    Design, fabrication and characterization of biodegradable scaffolds for tissue engineering and regenerative medicine applications

    Doku mühendisliği ve rejeneratif tıp uygulamaları için biyoçözünür iskele yapılarının tasarımı, üretimi ve karakterizasyonu

    MUHAMMAD ANWAAR NAZEER

    Doktora

    İngilizce

    İngilizce

    2018

    BiyomühendislikKoç Üniversitesi

    Biyomedikal Bilimler ve Mühendislik Ana Bilim Dalı

    PROF. DR. İSKENDER YILGÖR

Geri Dön