Soğuk plazma uygulamasının dental zirkonyanın yüzey özelliklerine ve rezin simanla bağlantısına etkilerinin araştırılması
Evaluation of the effects of non-thermal atmospheric plasma treatment on surface properties and shear bond strength of zirconia ceramics
- Tez No: 510773
- Danışmanlar: DR. ÖĞR. ÜYESİ ÖZLEM ÇÖLGEÇEN
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental bonding, Dental materyaller, Dental porselen, Dental stres analizi, Dental çimentolar, Soğuk plazma, Zirkonyum, Dental bonding, Dental materials, Dental porcelain, Dental stress analysis, Dental cements, Cold plasma, Zirconium
- Yıl: 2018
- Dil: Türkçe
- Üniversite: İzmir Katip Çelebi Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu tez çalışmasının amacı atmosferik soğuk plazmanın, tek başına ve klinik uygulamalarda yaygın kullanılan kumlama ve primer uygulaması yöntemleriyle farklı kombinasyonlar şeklinde uygulamasının, dental zirkonyanın yüzey özelliklerine ve rezin siman ile bağlanma dayanımı üzerine etkilerini değerlendirmektir. Çalışmada zirkonya seramik CAD/CAM bloklardan elde edilen 310 adet örnek sinterlenme sonrası, uygulanacak yüzey işlemine göre 10 gruba ayrıldı: Z (Yüzey işlemi yok), K (Kumlama), Pr (Primer), KPr (Kumlama+primer), ZP (soğuk plazma), KP (kumlama+soğuk plazma), PrP (primer+soğuk plazma), KPrP (kumlama+primer+soğuk plazma), PPr (soğuk plazma+primer) ve KPPr (kumlama+soğuk plazma+primer). Deney gruplarında profilometre ile yüzey pürüzlülüğü, goniometre ile temas açısı (n=10) ve XPS ile elementel analiz (n=1) ölçümleri yapıldı. Rezin siman bağlanma dayanımı self-etch adeziv bir rezin siman kullanılarak, universal test cihazı ile makaslama bağlanma dayanımı testi uygulanarak gerçekleştirildi (n=20). Bağlanma dayanımları değerlendirilecek örneklerin yarısına termal siklus (5000 devir, 5-55 ºC) işlemi uygulandı. Kopma tipleri stereomikroskopta incelendi. İstatistiksel değerlendirme için tek yönlü ve iki yönlü ANOVA, çoklu karşılaştırma testi olarak da Student-Newman-Keuls testleri uygulandı (α=0,05). Çalışmanın sonuçlarına göre, soğuk plazmanın işlemsiz zirkonya yüzeyinde pürüzlülük artışı sağladığı, son aşama olarak uygulandığında yüzey temas açısında belirgin bir azalma yarattığı görüldü (p<0,05). Rezin siman ile bağlanma dayanımı açısından, plazma işleminin uygulama sırasının önem taşıdığı ve işlemsiz zirkonya yüzeyinde primer tabakasından önce uygulandığında (PPr grubu), hem başlangıç hem de termal siklus sonrasında, diğer kombinasyonlara göre daha yüksek bağlanma dayanımı elde edilebildiği görüldü (p<0,001). Soğuk plazma uygulaması zirkonya seramiklerin rezin simantasyonu için yeni alternatif bir yüzey işlemi olabilir; ancak kesin yargılar için konunun in vivo ortamda yapılacak klinik çalışmalarla desteklenmesi gerekmektedir.
Özet (Çeviri)
The purpose of this in-vitro study was to evaluate the effects of non-thermal atmospheric plasma (NTAP) treatment, alone or combinated with sandblasting and/or primer applications on the surface roughness, wettability and bonding to resin cement of zirconia ceramics. In this study, 310 sintered zirconia specimens were divided into 10 groups according to the surface treatments received: Z (control), K (sandblasting), Pr (primer), KPr (sandblasting+primer), ZP (NTAP), KP (sandblasting+NTAP), PrP (primer+NTAP), KPrP (sandblasting+primer+NTAP), PPr (NTAP+primer) and KPPr (sandblasting+NTAP+primer). The surface roughness values was evaluated using a profilometer and the contact angle measurements were performed with a goniometer (n=10). Surface chemistry of specimens was characterized by XPS analysis (n=1). Shear bond strength (SBS) tests were performed using universal testing machine at a cross-head speed of 0,5 mm/min following cementation with a self-etch adhesive resin cement. Half of the specimens were subjected to thermocycling (5000 cycles,5-55°C) before SBS test. The failure mode was recorded by examining each specimen using a stereomicroscope. One-way and two-way ANOVA followed by Student-Newman-Keuls test (α=0.05) were used to analyze the data statistically. According to the results, untreated zirconia surfaces were found to have higher surface roughness values after NTAP treatment. NTAP was also found effective for lower contact angle values for the groups in which it was applied as the final stage. For the SBS values, it had the greatest effect in PPr group. NTAP application may be a novel alternative surface treatment for edhesive cementation of zirconia ceramics; but it needs to be supported by clinical studies.
Benzer Tezler
- Atmosferik soğuk plazma ve mezenkimal kök hücre ile modifiye edilen titanyum yüzeylerde osteojenik hücreaktivitelerinin değerlendirilmesi
The evaluation of the osteogenic cell activities on titanium surface modified with the atmospheric cold plasma and mesenchymal stem cells
MEHMET BURAK KAPILI
Diş Hekimliği Uzmanlık
Türkçe
2017
Diş Hekimliğiİzmir Katip Çelebi ÜniversitesiAğız, Diş ve Çene Cerrahisi Ana Bilim Dalı
YRD. DOÇ. DR. MURAT ULU
- Soğuk atmosferik plazma ile yüzey uygulamasının fiber postların bağlanma dayanımı üzerine etkilerinin değerlendirilmesi
Assessment of surface treatment with atmospheric cold plasma on the bond strength of fiber post
ELİF ŞEYMA KABAN
- Soğuk plazma uygulamasının sabit protetik restorasyonların tamirindeki etkinliğinin incelenmesi
Investigation of the effectiveness of non-thermal plasma application on repair of fixed prosthetic restorations
MEHMET KÖSE
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş Hekimliğiİzmir Katip Çelebi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ÖZLEM ÇÖLGEÇEN
- Devital beyazlatma ajanlarının atmosferik soğuk plazma güç kaynağı ile aktivasyonunun beyazlatma ve renk stabilitesi üzerine etkinliğinin incelenmesi
Evaluation of the effectiveness of atmospheric low temperature power source activated bleaching agents on bleaching efficacy and color stability
BURAK ÇELİK
Doktora
Türkçe
2015
Diş Hekimliğiİzmir Katip Çelebi ÜniversitesiEndodonti Ana Bilim Dalı
DOÇ. DR. İSMAİL DAVUT ÇAPAR
PROF. DR. NECDET ERDİLEK
- Atmosferik basınç soğuk plazmanın restoratif diş tedavisinde kullanımının araştırılması
Investigation of the use of atmospheric pressure cold plasma in restorative dental treatment
SÜLEYMAN KORKUT BALCI
Yüksek Lisans
Türkçe
2023
Diş HekimliğiIsparta Uygulamalı Bilimler ÜniversitesiBiyomedikal Mühendisliği Ana Bilim Dalı
DOÇ. DR. ALİ GÜLEÇ