Karbotermal sentezleme metodu ile elde edilen silisyum oksi nitrür tozundan 0'-sialon üretimi
O'-sialon production from silicon oxynitride powder obtained by carbothermal synthesis method
- Tez No: 542516
- Danışmanlar: PROF. SEMRA KURAMA
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Mühendislik Bilimleri, Seramik Mühendisliği, Metallurgical Engineering, Engineering Sciences, Ceramic Engineering
- Anahtar Kelimeler: Si2N2O, karbotermal sentez, O'SiAlON, mekanik özellikler, Si2N2O, carbothermal synthesis, O'SiAlON, mechanical properties
- Yıl: 2018
- Dil: Türkçe
- Üniversite: Anadolu Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 57
Özet
Si2N2O; düşük ısı iletkenliği, hava mükemmel oksidasyon direnci, yüksek eğilme mukavemeti ve düşük dielektrik sabiti ve kaybını koruyabilen gelişmiş bir mühendislik malzemesi olarak silikon-oksijen-azot sisteminde önemli bir bileşiktir. Bu mükemmel özelliklere sahip olan Si2N2O, çeşitli uygulamalarda umut verici bir adaydır. Örneğin, çubuk benzeri morfoloji veya fiber içeren tozlar, mühendislik materyal matrisinde kırılma tokluğunun takviyesinde fayda sağlayacaktır. Aksine, düşük en-boy oranı olan tozlara göre düşük dielektrik sabiti ve kaybı gerektiren alanlarda kullanım için daha uygun olacaktır. Burada, morfoloji kontrollü Si2N2O tozlarının sentezinin, daha da geliştirilmesi ileri teknoloji alanında genişletilmiş uygulamalarını önemli derecede etkilemektedir. Son zamanlarda karbon nano katmanlarla yüzey kaplı inorganik parçacıklardan oluşan çekirdek-kabuk yapılandırılmış tozlar konusunda çalışmalar görülmektedir. Bu tozlar inorganik parçacık yüzeyleri üzerindeki organik polimerlerin yerinde polimerleştirilmesi, ardından düşük sıcaklıkta piroliz yoluyla sentezlenmesi şeklinde yapılmaktadır. Önerilen bu projede, karbotermal sentez yöntemi kullanılarak silikon oksinitrit tozu üretimi sağlanmıştır. Böylece, yüksek sıcaklık uygulamaları için O'SiAlON seramiklerin üretiminde ince ve saf toz kullanılmıştır. Bu yöntem O'-SiAlON için kullanılacak başlangıç tozlarının ekonomik ve kolay bir şekilde üretilmesinde yararlı olacaktır.
Özet (Çeviri)
Si2N2O is a significant compound in silicon–oxygen–nitrogen system, as an advanced engineering material which can keep low thermal conductivity, excellent oxidation resistance in air, high flexural strength, and low dielectric constant and loss. Having these excellent properties, Si2N2O has been a promising candidate in varied applications. For example, the powders with rod-like morphology or fiber will benefit the reinforcement of fracture toughness in engineering material matrix. On the contrary, the powders with low aspect ratio will be more suitable to use in areas requiring relative low dielectric constant and loss. Herein, synthesizing morphology-controllable Si2N2O powders crucially affects their further development and extended applications. Recently, core-shell structured powders composed of inorganic particles that were surface coated with carbon nano layers were reported. These powders were synthesized through in situ polymerization of organic polymers on inorganic particle surfaces followed by low temperature pyrolysis. By using carbothermal method production of silicon oxynitride powder had been achieved. Therefore, fine and pure powder had been used for production O'SiAlON ceramics for high temperature application. This method will be useful for production of procure powders for O'-SiAlON as economically and easy.
Benzer Tezler
- Synthesis of next-generation silicon/graphite anode materials via molten salt-assisted magnesiothermic reduction for lithium-ion batteries
Lityum iyon piller için erimiş tuz yardımlı magnezyotermik indirgeme yoluyla yeni nesil silisyum- grafit anot malzemelerinin sentezi
BURAK FEDAKAR
Yüksek Lisans
İngilizce
2023
Enerjiİstanbul Teknik ÜniversitesiEnerji Bilim ve Teknoloji Ana Bilim Dalı
PROF. DR. NİLGÜN YAVUZ
- Synthesis and characterization of hafnium boride-based ceramic powders
Hafniyum borür-esaslı seramik tozlarının sentezlenmesi ve karakterizasyonu
NAZLI AKÇAMLI
Doktora
İngilizce
2016
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. İSMAİL DUMAN
- Synthesis of alon, MgAlON and MgAl2O4 powders using thermo-chemical method
Termo-kimyasal yöntemle alon, MgAlON ve MgAl2O4 toz üretimi
HAMZA BOUSSEBHA
Doktora
İngilizce
2023
Metalurji MühendisliğiSakarya ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ALİ OSMAN KURT
- Lityum iyon pillerde katot aktif madde olarak kullanılan lifepo4 bileşiğinin iletkenliğinin artırılması
Improving the conductivity of lifepo4 as cathode active materials used for lithium ion batteries
SERKAN ŞEN
- Development and characterization of high entropy (HfTiZrMn/Cr)B2 based ceramics
Yüksek entropi (HfTiZrMn/Cr)B2 bazlı seramiklerin geliştirilmesi ve karakterizasyonu
İLAYDA SÜZER
Yüksek Lisans
İngilizce
2022
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. DUYGU AĞAOĞULLARI