Tuzlu su yaşlandırmasının cıvata bağlantılı halloysit nanotüp–epoksi/bazalt fiber nanokompozitlerin düşük hızlı darbe davranışlarına etkisi

The effect of salty water aging on low velocity impact behaviors of bolted halloysite nanotube-epoxy/basalt fiber nanocomposites

  1. Tez No: 550463
  2. Yazar: HALİL BURAK KAYBAL
  3. Danışmanlar: PROF. DR. AHMET AVCI
  4. Tez Türü: Doktora
  5. Konular: Makine Mühendisliği, Mechanical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2019
  8. Dil: Türkçe
  9. Üniversite: Konya Teknik Üniversitesi
  10. Enstitü: Lisansüstü Eğitim Enstitüsü
  11. Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 170

Özet

Bu tez çalışmasında, bazalt fiber takviyeli epoksi matris (epoksi/BF) kompozit ve halloysit nanotüp (HNT) katkılı bazalt fiber takviyeli epoksi matris (HNT-epoksi/BF) nanokompozit malzeme üretimi hem el yatırması hem de vakum infüzyon yönteminin birlikte kullanılmasıyla gerçekleştirilmiştir. Ayrıca epoksi matris içinde kullanılan HNT 'nin en verimli oranı, epoksi nanokompozit numunelerin çekme testi sonucunda ağırlıkça % 2 oranında bulunmuştur. ASTM standartlarına göre malzemelerin uygun cıvata bağlı montajları yapılmıştır. Cıvata bağlı epoksi/BF kompozit ve HNT-epoksi/BF nanokompozit malzemeler, 2, 4 ve 6 ay tuzlu suya maruz kalacak şekilde yaşlandırmaya bırakılmıştır. Yaşlandırma sonrasında numunelerin yük altındaki davranışlarını incelemek, meydana gelen hasar türlerini görmek ve yük taşıma kapasitelerini bulmak için çekme testi uygulanmış ve yaşlandırılmamış numuneler ile kıyaslanmıştır. Numunelere 15 J, 20 J ve 25 J enerji seviyelerinde vurucunun cıvata bağlı numuneler üzerine iki farklı bölgeye düşürülmesiyle düşük hızlı darbe testi oda sıcaklığında yapılmış ve birbirleriyle kıyaslanmıştır. Kompozit ve nanokompozit numunelerin çekme ve darbe testleri sonrası tuzlu suyun etkisi numuneler üzerinde araştırılmıştır. Numunelerin yüzeylerinde ve kırılma bölgelerinde oluşan hasarlar optik ve SEM görüntüleri alınarak incelenmiştir. HNT 'nin epoksi polimer içerisine takviye edilmesiyle, epoksi nanokompozit malzemenin çekme dayanımı, elastiklik modülü ve tokluk özelliklerinde artış olmuştur. Bu durum, bazalt fiberlerin HNT takviyeli epoksinin, bazalt fiberlere matris olarak taşınması ile devam etmiştir. Cıvata bağlantılı HNT-epoksi/BF nanokompozit malzemeler gerçekleştirilen çekme ve darbe testi sonrasında epoksi/BF kompozit malzemeye göre daha üstün bir performans göstermiştir. HNT takviyesi ile HNT-epoksi/BF nanokompozit malzemenin yaşlandırma sonrasında tuzlu sudan etkilenmesi epoksi/BF kompozit malzemeye nispeten daha az olmuştur. Bu durum, HNT 'nin tuzlu suya karşı tampon vazifesi gördüğünü ön plana çıkarmıştır. Ayrıca optik ve SEM görüntüleri incelendiğinde epoksi/BF kompozit numunelerde aynı şartlar altında daha fazla hasar yoğunluğu meydana gelmiştir.

Özet (Çeviri)

In this thesis, production of basalt fiber reinforced epoxy matrix (epoxy/BF) composite and halloysite nanotube (HNT) addition basalt fiber reinforced epoxy matrix (HNT-epoxy/BF) nanocomposite material were performed by using both hand laying and vacuum infusion method. In addition, the most efficient ratio of HNT used in epoxy matrix was found to be 2 % by weight as a result of tensile test of epoxy nanocomposite specimens. According to ASTM standards, the appropriate bolt connection system of the materials was made. Bolted epoxy/BF composite and HNT-epoxy/BF nanocomposite materials were left to aging in salty water for 2, 4 and 6 months. After the aging, the tensile test was carried out to examine the behaviors of the specimens under load, to observe the types of damage occurring and to find their load bearing capacities and also compared with non-aged specimens. Moreover, the low velocity impact test at room temperature was performed to for two different zones on the bolted composites and nanocomposites. The tests were applied at the energy levels of 15 J, 20 J and 25 J and the results compared to each other. The effects of salty water were investigated after the tensile and impact tests of composite and nanocomposite materials. The damages on the surface and fracture areas of the specimens were examined with optical microscopy and SEM images. It is observed that by reinforcing the HNT into the epoxy polymer, the tensile strength, elastic modulus and toughness properties of the epoxy nanocomposite material were increased. This was continued with basalt fiber introduced to the HNT reinforced epoxy. The bolted HNT-epoxy/BF nanocomposite materials showed superior performance compared to epoxy/BF composite material after tensile and impact test. Furthermore, after ageing, HNT-epoxy/BF nanocomposite materials were affected from salty water relatively less than epoxy/BF composite materials. This situation was came into prominence the fact that HNT serves as a buffer against salty water. Lastly, the epoxy/BF composite specimens had more damage density under the same conditions, when the optical and SEM images were viewed.

Benzer Tezler

  1. Tuzlu su yaşlandırmasının halloysit nanotüp-epoksi/bazalt fiber nanokompozitlerin mekanik ve kırılma performansına etkisi

    Effect of salty water aging on mechanical and fracture performance of halloysite nanotube-epoxy/basalt fiber nanocomposites

    HASAN ULUS

    Doktora

    Türkçe

    Türkçe

    2019

    Makine MühendisliğiKonya Teknik Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. AHMET AVCI

  2. Influence of water aging on vibration-damping behavior of fiber reinforced composite laminates

    Su yaşlandırmasının elyaf takviyeli kompozit laminatların titreşim sönümleme davranışına etkisi

    MUHAMMET ENVER GÖKDEMİR

    Yüksek Lisans

    İngilizce

    İngilizce

    2018

    Makine MühendisliğiGaziantep Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    DOÇ. DR. ÖMER YAVUZ BOZKURT

  3. Effect o loading direction and long-term aging on fatique crack growth in A1-Li alloy 2090

    Yükleme doğrultusu ve uzun süreli yaşlandırmanın 2090 Alş-Li alaşımındaki çatlak büyüme tavrına etkisi

    MUSTAFA ANIK

    Yüksek Lisans

    İngilizce

    İngilizce

    1995

    Metalurji MühendisliğiOrta Doğu Teknik Üniversitesi

    PROF.DR. MUSTAFA DORUK

  4. Sınıf öğretmenlerinin mesleki kimliğinin oluşum/yapılandırmasının seçilmiş bazı değişkenler açısından incelenmesi

    Examining the formation/ construction of the professional identity of primary teachers in terms of some selected variable

    KÜBRA FIRAT

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    Eğitim ve ÖğretimFırat Üniversitesi

    Temel Eğitim Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ SEDA KERİMGİL ÇELİK

  5. Akışla şekillendirme uygulanmış AA7075 kalite alüminyum alaşımının mekanik ve korozyon özelliklerine retrogresyon ve yeniden yaşlandırma işleminin etkisi

    The effect of retrogression and reaging heat treatment on the mechanical and corrosion properties of a flow formed AA7075 aluminum alloy

    EDA URAL

    Yüksek Lisans

    Türkçe

    Türkçe

    2024

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. MURAT BAYDOĞAN