Farklı yüzey işlemleri ve iki farklı tamir kiti uygulamasının kompozit rezinin zirkonyum oksit altyapıya bağlanma dayancı üzerindeki etkilerinin incelenmesi
Evaluation of the effects of different surface treatments and application of two different repair kits on the bond strength of composite resin to zirconium oxide framework
- Tez No: 668720
- Danışmanlar: PROF. DR. YAKUP ŞİNASİ SARAÇ
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Alüminyum oksit kumlama, Er:YAG lazer, Makaslama bağlanma dayancı, Silika kaplama, Y-TZP, Dental bonding, Dental materyaller, Dental restorasyon, Kompozit reçineler, Zirkonyum, Aluminum oxide sandblasting, Er:YAG laser, Shear bond strength, Silica coating, Y-TZP, Dental bonding, Dental materials, Dental restoration, Composite resins, Zirconium
- Yıl: 2021
- Dil: Türkçe
- Üniversite: Ondokuz Mayıs Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu tez çalışmasının amacı; farklı yüzey işlemleri ve iki farklı tamir kiti uygulamasının, zirkonyum oksit altyapı ve kompozit rezin arasındaki bağlanma dayancı üzerindeki etkilerinin in vitro koşullarda incelenmesidir. Materyal ve Metot: Y-TZP seramik bloklardan 10x10x1 mm boyutlarında toplam 120 adet örnek hazırlandı. Yüzey işlemleri; silika kaplama (CoJet), 50 μm'lik Al2O3 ile kumlama, Er:YAG lazerle pürüzlendirme ve kontrol grubu olarak belirlendi. Ağız içi tamir setleri olarak Bisco ve GC seçildi. Hazırlanan seramik örnekler her bir grupta 15'er örneğin olduğu 8 alt gruba ayrıldı. Yüzey işlemlerinin uygulanmasından sonra tüm örneklere kompozit rezin (GC Gradia Direct Corporation ) uygulandı ve ardından termal devirlendirme işlemi yapıldı. Daha sonra universal test cihazına yerleştirilen örneklere makaslama kuvveti uygulandı ve bağlanma dayancı değerleri kaydedildi. Yüzey yapıları SEM'de, kırık tipleri ise stereomikroskop altında incelendi. Elde edilen değerler iki yönlü varyans analizi (ANOVA) ve Tukey HSD çoklu karşılaştırma test analizi ile istatistiksel olarak değerlendirildi. Bulgular: Her iki tamir kiti uygulaması için de en yüksek makaslama bağlanma dayancı silika kaplama grubunda izlenirken (p>0,001), en düşük değerleri gösteren kontrol ve Er:YAG lazer grupları arasında anlamlı bir fark bulunamadı (p<0,05). Hiçbir örnekte koheziv tip kırığa rastlanmazken, büyük oranda adeziv tip kırık oluştuğu belirlendi. Sonuç: Silika kaplama ve 50 μm'lik Al2O3 ile kumlama yöntemlerinin zirkonyum oksit ile kompozit rezin arasındaki bağlanma dayancı değerlerini her iki tamir kitinde de anlamlı derecede arttırdığı gözlendi. Er:YAG lazer yüzey işlemi uygulamasının ise bağlanma dayancı üzerinde olumlu bir etkisinin olmadığı görüldü.
Özet (Çeviri)
Purpose: The aim of this study was to evaluate the effects of different surface treatments and the application of two different repair kits on the bond strength of composite resin to zirconium oxide framework in invitro conditions. Material and Method: A total of 120 samples were prepared from Y-TZP ceramic blocks in 10x10x1 mm dimensions. Surface treatments were determined as silica coating (CoJet), sandblasting with 50 μm Al2O3, roughening with Er:YAG laser and control group. Bisco and GC were selected as intraoral repair sets. Ceramic samples were divided into 8 subgroups with 15 samples in each. After application of surface treatments, composite resin (GC Gradia Direct Corporation) were placed on to the treated surfaces. Then all samples were thermally cycled. A universal test device was used for shear bond strength test and bond strength values were recorded. Surface structures were examined by means of SEM and fracture types were examined by a Stereomicroscope. The data were statistically analysed by Two-Way Analysis of Variance (ANOVA) and Tukey HSD Multiple Comparison Test Analysis. Results: While the highest shear bond strength was observed in the silica coating group for both repair kit applications (p> 0.001), no significant difference was found between the control and Er:YAG laser groups showing the lowest values (p <0.05). It was determined that an adhesive type fracture occurred to a great extent though no cohesive type fracture was found in any of the samples. Conclusion: The results showed that the silica coating and sandblasting with 50 μm Al2O3 methods significantly increased the bond strength values between zirconium oxide framework and composite resin in both repair kits. It was observed that Er:YAG laser surface treatment application did not have a positive effect on bond strength.
Benzer Tezler
- Bazı esterlerin kinetik incelenmesi ve termodinamik parametrelerin belirlenmesi
Kinetic study and detesmination of thermodnamic parameters of some esters
İBRAHİM TAŞ
Yüksek Lisans
Türkçe
1986
Kimya MühendisliğiUludağ ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. MUSTAFA CEBE
- İzmir'de bazı yolların kapatılarak yaya bölgeleri oluşturma da kent peyzajını geliştirme açısından yeniden planlanması üzerinde araştırmalar
Başlık çevirisi yok
BAHAR TÜRKYILMAZ
Yüksek Lisans
Türkçe
1985
Şehircilik ve Bölge PlanlamaEge ÜniversitesiŞehir ve Bölge Planlama Ana Bilim Dalı
- Testosteron dihidrotestosteron ve östrojenin benign prostat hiperplazisindeki etyolojik rolleri
The roles of testosterone, dihydrotestosterone and estradiole on the etiology of benign prostatic hyperplasia
HALUK TOKUÇOĞLU
- Süt formüllerinin tüketim uygulamaları ve süt formüllerinin C vitamini içeriği ile pH değerleri
Başlık çevirisi yok
GÖNÜL VAROL
Yüksek Lisans
Türkçe
1986
Besin Hijyeni ve Teknolojisiİstanbul ÜniversitesiÇocuk Gelişimi Ana Bilim Dalı
DOÇ. DR. TÜRKAN KUTLUAY
- Türkiye'de aile planlaması çalışmalarında erkeklerin önemi, hastane personeli ile fabrika işçilerinin doğum kontrol yöntemlerine karşı tutum ve davranranışlarında farklılığın araştırılması
Başlık çevirisi yok
KAMİL MALKOÇLU
Yüksek Lisans
Türkçe
1987
Demografiİstanbul ÜniversitesiAile Sağlığı Ana Bilim Dalı
DOÇ. DR. DERİN KÖSEBAY