Farklı yüzey işlemlerinin monolitik zirkonya materyalinin mekanik özelliklerine etkisi
Effect of different surface treatments on the mechanical properties of monolithic zirconia material
- Tez No: 672030
- Danışmanlar: DR. ÖĞR. ÜYESİ FATMA AYŞE ŞANAL
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental materyaller, Dental stres analizi, Hidroflorik asit, Mekanik özellikler, Yüzey işleme tekniği, Zirkonyum, Dental materials, Dental stress analysis, Hydrofluoric acid, Mechanical properties, Surface handling technique, Zirconium
- Yıl: 2020
- Dil: Türkçe
- Üniversite: Bolu Abant İzzet Baysal Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmanın amacı, yüzey işlemi olarak kumlama ve hidroflorik asit (HF) uygulanmasının güncel monolitik zirkonya materyalinin erken ve geç dönem siman bağlantısına, biaksiyel eğme dayancına, t-m faz dönüşümüne etkilerinin incelenmesidir. Disk şeklinde (12×1,2 mm) sinterlenmiş monolitik zirkonya örnekler (VITA YZ XT, Vita Zahnfabrik, Bad säckingen, Almanya) Grup C (kumlama), Grup K20HF (kumlama+%20 HF), Grup K40HF (kumlama+%40 HF), Grup 20HF (%20 HF), Grup 40HF (%40 HF) olacak şekilde 5 gruba bölünerek ilgili yüzey işlemleri uygulandı. Her gruptan birer örneğe X-ışını diferaksiyonu (XRD) ve Taramalı Elektron Mikroskobu (SEM) analizleri yapıldı. Tüm gruplardan yaşlandırılmış ve yaşlandırılmamış yedişer örneğe makaslama bağlanma dayanımı testi (SBSt) uygulandıktan sonra birer örnek SEM'le analiz edildi. Elde edilen veriler sırasıyla SBS1 ve SBS2 değerleri olarak kaydedildi. Her bir grup için yaşlandırılmış ve yaşlandırılmamış yedişer örneğe biaksiyal eğme testi (BFSt) uygulandı, yaşlandırılan örneklerden birer tanesine XRD ve SEM analizi yapıldı. Elde edilen veriler sırasıyla BFS1 ve BFS2 değerleri olarak kaydedildi. Veriler 2-yönlü varyans analiziyle (ANOVA), gruplar arası farklılıklar Tukey HSD testiyle değerlendirildi. En yüksek SBS değerleri kumlama (Grup C) işlemi için, en düşük SBS değerleri Grup 40HF için kaydedildi, bu fark yaşlandırılmamış gruplar için anlamlıydı (P<0,05). Kumlama işlemi BFS1 ve BFS2 değerlerini anlamlı olarak düşürdü (P<0,05). BFS2 değerleri, BFS1 değerlerinden yüksek bulundu (P<0,05). Hiçbir grupta yapay yaşlandırma öncesi ve sonrası monoklinik faza rastlanmadı. Kumlama, %20 HF ve %40 HF için SBS değerleri arasında fark bulunamadı. Kumlama, monolitik zirkonya materyalinin dayancını HF uygulanmasına göre daha fazla azaltmaktadır. HF uygulaması kumlama yöntemine alternatif bir yüzey işlemi olarak düşünülebilir.
Özet (Çeviri)
The aim of this study is to investigate the effects of sandblasting and hydrofluoric acid (HF) application as a surface treatment on early and late period of cement bonding, biaxial flexural strength and t-m phase transformation of a current monolithic zirconia material. Disc-shaped (12×1.2 mm) sintered monolithic zirconia samples (XT, VITA YZ, Vita Zahnfabrik, Bad sackingen, Germany) were divided into 5 groups as Group C (sandblasting), Group K20HF (sandblasting+20% HF), Group K40HF (sandblasting+40% HF), Group 20HF (20% HF), Group 40HF (40% HF) then related surface treatments were applied. X-ray differentiation (XRD) and scanning electron microscopy (SEM) analyses were performed on one sample from each group. After the shear bond strength test (SBSt) was applied to seven aged and non-aged samples from all groups, one sample from each group was analyzed with SEM. The data obtained were recorded respectively as SBS1 and SBS2 values. Biaxial flexural strength test (BFSt) was applied to seven aged and non-aged samples, then XRD and SEM analysis were performed on one sample from each of the aged groups. The data obtained were recorded respectively as BFS1 and BFS2 values. Data were evaluated by 2-way analysis of variance (2-way ANOVA), and differences between groups were evaluated by Tukey HSD test. The highest SBS values were recorded for sandblasting (Group C), while the lowest SBS values were recorded for group 40HF, and this difference was significant for non-aged groups (P<0.05). Sandblasting significantly reduced BFS1 and BFS2 values (P<0.05). BFS2 values were higher than BFS1 values (P<0.05). No monoclinic phase was observed before and after artificial aging in any group. No difference was found between SBS values for sandblasting, 20% HF, and 40% HF. Sandblasting reduced the strength of the monolithic zirconia material more than HF application. The HF application can be considered as an alternative surface treatment method to the sandblasting.
Benzer Tezler
- Farklı itriyum içerikli monolitik zirkonya materyaline uygulanacak farklı bitirme işlemlerinin materyalin mekanik özelliklerine etkisi
The effect of different finishing processes applied to monolithic zirconia material with different yttrium content on the mechanical properties of the material
RUMEYSA BAYKAN
Diş Hekimliği Uzmanlık
Türkçe
2026
Diş HekimliğiKaradeniz Teknik ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ELİF AYDOĞAN AYAZ
- Zirkonya içerikli farklı seramik materyallerin optik özelliklerinin incelenmesi
Investigation of the optical properties of different ceramic materials containing zirconia
FATMA ŞEHİDE ERCAN
Diş Hekimliği Uzmanlık
Türkçe
2024
Diş HekimliğiUşak ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ AYSILA TEKELİ ŞİMŞEK
- Sinterizasyon hızının ve klinik uyumlamanın monolitik zirkonya restorasyonların optik, mekanik, mikro yapısal ve yüzey özellikleri üzerindeki etkisinin ı̇ncelenmesi
Impact of sintering speed and clinical adjustment on translucency, mechanical, microstructural, and surface properties of monolithic zirconia restorations
ÖZGE GÜLMEZ
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiAtatürk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. ESRA KUL
- Zirkonyum esaslı 3 farklı tüm porselen sisteminde, yüzey işlemlerinin, ortalama yüzey pürüzlülüğüne ve bükülme dayanıklılığına etkisinin araştırılması ve X-ray difraktometre yüzey analizleri ile incelenerek değerlendirilmesi
The effect of surface treatment of 3 different zirconia based full ceramics on mean surface roughness and flexural strength and the determination of the effects of surface treatment of the zirconia systems by X-ray difractometer surface analyse
SEÇİL KARAKOCA
Doktora
Türkçe
2008
Diş HekimliğiGazi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. HANDAN YILMAZ
- Farklı yüzey işlemi uygulanmış zirkonyum oksit esaslı alt yapıların üst yapı porselenine olan bağlanma dayanımının değerlendirilmesi
Evaluation of bond strength between veneering porcelains and different surface treated zirconium oxide based frameworks
NEVRİYE AKSU
Doktora
Türkçe
2015
Diş HekimliğiKaradeniz Teknik ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. LÜTFÜ İHSAN ALADAĞ