Farklı görünüm oranlı bazalt liflerle üretilen yüksek dayanımlı betonun performans özelliklerinin incelenmesi
Investigation of the performance characteristics of high strength concrete produced with basalt fibers with different appearance ratio
- Tez No: 677744
- Danışmanlar: DOÇ. DR. MERAL OLTULU
- Tez Türü: Yüksek Lisans
- Konular: İnşaat Mühendisliği, Civil Engineering
- Anahtar Kelimeler: Bazalt lif, lif takviyeli yüksek dayanımlı beton, çentikli kiriş, eğilme dayanımı, kırılma enerjisi, aşınma dayanımı, Basalt fiber, Fiber reinforced high strength concrete, notched beam, bending strength, fracture energy, abrasion resistance
- Yıl: 2021
- Dil: Türkçe
- Üniversite: Atatürk Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 98
Özet
Amaç: Bu çalışmada, geleneksel betona farklı görünüm oranlarında (160, 630 ve 1263) bazalt lifler ilave edilerek betonun mekanik, fiziksel ve performans özelliklerinin iyileştirilmesi amaçlanmıştır. Yöntem: Liflerin görünüm oranları parametre olarak seçilmiş başta taze ve sertleşmiş beton deneyleri olmak üzere basınç, yarmada çekme, eğilme dayanımı, kırılma enerjisi ve aşınma dayanımı gibi betonun özellikleri üzerine etkileri araştırılmıştır. Kırılma enerjilerinin belirlenmesinde RILEM 50-FMC tarafından önerilen deney yöntemi, aşınmaya karşı dirençlerinin ölçülmesinde TS 2824 EN 1338'de belirtilen Böhme deneyi uygulanmıştır. Deneyler hacimce %0-0,025-0,05-0,10-0,15-0,20 oranlarında ve 3 mm - 12 mm - 24 mm uzunluklarında bazalt lifler kullanılarak üretilen yüksek dayanımlı beton numuneler üzerinde yapılmıştır. Bulgular: Bazalt liflerin çimento hamurunda homojen dağılmasının önemli olduğu düşünülmektedir. Deney sonuçlarına göre liflerin betona ilavesi ile beton numunelerin aşınma dayanımının %1 ile %14 arasında, eğilme dayanımının %2 ile %25 arasında, yarmada çekme dayanımının %2 ile %13 arasında arttığı gözlenmiştir. Tüm gruplar arasında BF3/0,025 kodlu numunede en iyi aşınma direnci sonucu elde edilirken, eğilme ve yarmada çekme dayanımlarında BF24/0,05 kodlu numunede en iyi sonuçlar elde edilmiştir. Sonuç: Çalışmada genel olarak betona ilave edilen farklı görünüm oranlarında bazalt lifler betonun birim ağırlığının ve basınç dayanımının azalmasına sebep olmuştur. Bunun yanında liflerin ilavesi betonun yarmada çekme, eğilmede çekme, kırılma enerjisi ve aşınma direncine olumlu yönde katkıda bulunduğu görülmektedir. Betonlarda, bazalt lif kullanımının, betonun mekanik ve performans özelliklerini iyileştirdiği belirlenmiştir.
Özet (Çeviri)
Purpose: In this study, it is aimed to improve the mechanical, physical and performance properties of concrete by adding basalt fibers in different aspect ratios (160, 630 and 1263) to conventional concrete. Method: The appearance ratios of the fibers were selected as a parameter, and the effects on the properties of concrete such as compression, tensile splitting, flexural strength, fracture energy and abrasion resistance were investigated, especially in fresh and hardened concrete tests. The test method recommended by RILEM 50-FMC for determining the fracture energies, Böhme test specified in TS 2824 EN 1338 was applied to measure their resistance to abrasion. The experiments were carried out on high strength concrete specimens produced using basalt fibers in the ratio of 0-0.025-0.05-0.10-0.15-0.20% by volume and 3 mm – 12 mm - 24 mm lengths. Findings: It is thought that it is important that the basalt fibers are homogeneously distributed in the cement paste. According to the test results, it was observed that the abrasion resistance of the concrete samples increased between 1% and 14%, the bending strength between 2% and 25%, and the split tensile strength between 2% and 13% with the addition of fibers to the concrete. Among all groups, the best results were obtained in the sample coded BF3/0,025 in abrasion resistance, while the best results were obtained in the sample coded BF24/0,05 in bending and splitting tensile strength. Results: In the study, basalt fibers with different aspect ratios added to the concrete in general caused a decrease in the unit weight and compressive strength of the concrete. In addition, it is seen that it contributes positively to tensile in splitting, tensile in bending, fracture energy and abrasion resistance. It has been determined that the use of basalt fiber in concretes improves the mechanical and performance properties of concrete.
Benzer Tezler
- Burdur ili mermer sektörünün kurumsal ve ekonomik yapısı
İnstitutional and economic structure of marble sector in burdur
AHMET SARITAŞ
- Ratlarda dört farklı mesh materyalinin paravajinal dokudaki histopatolojik ve mekanik özelliklerinin değerlendirilmesi
İnvesti̇gati̇on of hi̇stopathologi̇c and mechani̇cal featuresof four di̇sti̇nct mesh materi̇als on the paravagi̇nal ti̇ssues i̇n rats
GÜLHAN GÜNEŞ ELÇİ
Tıpta Uzmanlık
Türkçe
2015
FizyopatolojiYüzüncü Yıl ÜniversitesiKadın Hastalıkları ve Doğum Ana Bilim Dalı
PROF. DR. ALİ KOLUSARI
- 30 hirsut vakanın etiyopatogenezinin araştırılması ve uygun şekilde sınıflandırılması
Başlık çevirisi yok
İLHAN SATMAN
Tıpta Uzmanlık
Türkçe
1983
Endokrinoloji ve Metabolizma Hastalıklarıİstanbul ÜniversitesiPROF.DR. SEVİM DEVRİM
- Çerçideresi taşocağı malzemesinin beton ve asfalt agregası olarak kullanılabilirliğinin incelenmesi
Investigation of usability of Çerçideresi colliery material as cocrete and asphalt aggregate
AHMET YİĞİT
Yüksek Lisans
Türkçe
2005
Maden Mühendisliği ve MadencilikCumhuriyet ÜniversitesiMaden İşletme Ana Bilim Dalı
Y.DOÇ.DR. SELİM DURUTÜRK
- Estetik ve fonksiyonel rinoplasti operasyonu için başvuran hastalarda antropometrik analiz
Anthropometric analysis in patients applied for aesthetic and functional rhinoplasty operation
ERCAN ÇELİKKALELİ
Tıpta Uzmanlık
Türkçe
2021
Plastik ve Rekonstrüktif CerrahiVan Yüzüncü Yıl ÜniversitesiPlastik Rekonstrüktif ve Estetik Cerrahi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ YILMAZ SULTANOĞLU