In vitro evaluation of cyclic fatigue resistance, bending resistance, and the microhardness of different niti alloy rotary ınstruments
Farkli niti alaşımlarından yapılmış döner aletlerin döngüsel yorgunluk direncinin, bükülme direncinin, ve mikrosertliğinin in vitro değerlendirilmesi
- Tez No: 690261
- Danışmanlar: DOÇ. DR. ELİF DELVE BAŞER CAN, PROF. DR. MERİÇ KARAPINAR KAZANDAĞ
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Mekanik özellikler, NiTi döner aletler, vücut sıcaklığı, irigasyon, sterilizasyon, Mechanical properties, NiTi rotary instruments, body temperature, irrigation, sterilization
- Yıl: 2021
- Dil: İngilizce
- Üniversite: Yeditepe Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Endodonti Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 195
Özet
Bu çalışma Protaper Next (PTN), Hyflex CM, EdgeFile, and XP-endoShaper kanal eğelerinin mekanik özelliklerinin incelenmesi ve ısı, sodium hipoklorit (NaOCl) ve sterilizasyonun bu eğelerin döngüsel yorgunluk direnci üzerinde etkilerinin tek kurvatürlü ve S şekilli kanallarda analiz edilmesi. Dört farklı tip Nikel-Titanyum (NiTi) döner alet: Protaper Next X3 (30/0.07), Hyflex CM (30/0.04), EdgeFile X7 (30/0.04) ve XP-endoShaper (30/0.01) değerlendirildi. Her tip döner alet, döngüsel yorgunluk testi sırasında aşağıdaki gibi 4 gruba (n=20/her grup; 10/alt grup) ayrıldı: Grup 1 (kontrol grubu); oda sıcaklığında, NaOCl solüsyonuna daldırılmayan ve otoklav sterilizasyonuna girmeyen yeni aletlerden oluşturuldu. Grup 2; vücut sıcaklığında %5'lik NaOCl solüsyonuna daldırılan ve sterilizasyona girmeyen, Grup 3; vücut sıcaklığında %5'lik NaOCl solüsyonuna daldırılan ve bir defa sterilizasyona giren aletlerden oluşturuldu. Grup 4; vücut sıcaklığında %5'lik NaOCl solüsyonuna daldırılan ve 5 defa sterilizasyona giren aletleri içerdi. Aletlerin kırılıncaya kadar gerçekleştirdiği tur sayısı (KKTS) hesaplandı. Aletlerin kırık yüzeyleri tarama elektron mikroskobu ile (SEM) incelendi. Aletler cantilever-bükülme testi kullanılarak bükülme direnci açısından test edildi. Vickers mikrosertliği, aletlerin enine kesitinde 300-g yük ve 15 saniye bekleme süresi ile ölçüldü (n=20/ her marka). İstatistiksel analiz, döngüsel yorulma testi için üç yönlü varyans analizi (ANOVA) ve Bonferroni'nin post hoc analizi ve eğilme direnci ve mikrosertlik testleri için tek yönlü varyans analizi (ANOVA) ve Games-Howell post hoc analizi kullanılarak yapıldı. İstatistiksel anlamlılık düzeyi p< 0.05 olarak belirlendi. Sonuç şunu gösteriyor,tüm aletlerin KKTS farkları istatistiksel olarak anlamlıdır (p0.05) test edilen tüm aletlerde, çevre koşullarından (p < 0.05) PTN and Hyflex CM hariç (p>0.05) test edilen tüm aletlerde anlamlı olarak etkilenmiştir. Açı ve kurvatür lokasyonu dışında (p 0.05) kırık parçanın uzunluğunda istatistiksel bir fark yoktur (p < 0.05). Bükülme direnci değerlerinde sıralama; PTN > HCM > EdgeFile > XP-endoShaper şeklindedir. Mikrosertlik testinin en düşük değerden en yükseğe doğru sıralaması: Hyflex CM 0.05). Sonuç olarak EdgeFile, yorulma direnci açısından diğer aletleri önemli ölçüde geride bırakmıştır, EdgeFile'ı XP-endoShaper takip etmektedir. PTN dışındaki tüm eğeler, daha zorlu kanallarda KKTS bakımından önemli bir düşüş göstermiştir. EdgeFile ve XP-endoShaper'ın KKTS vücut sıcaklığı ve NaOCl solüsyonu içerisine daldırmasından negatif yönde etkilenirken, sterilizasyon EdgeFile'ın KKTS'nı olumlu etkilemiş fakat XP-endoShaper üzerinde yıkıcı etkileri olmuştur. Diğer aletlerle karşılaştırıldığında en fazla esnekliği XP-endoShaper gösterirken onu EdgeFile izlemiştir. PTN ve EdgeFile diğer aletlere göre daha fazla aşınma direnci göstermiştir.
Özet (Çeviri)
In Vitro Evaluation of Cyclic Fatigue Resistance, Bending Resistance, and the Microhardness of Different NiTi Alloy Rotary Instruments. Yeditepe University Institute of Health Sciences. Faculty of Dentistry, Department of Endodontic, PhD Thesis, Istanbul. This study was conducted to compare the mechanical properties of the Protaper Next (PTN), Hyflex CM, EdgeFile, and XP -endoShaper, and to analyze the influence of the temperatures, sodium hypochlorite (NaOCl) immersion, and sterilization on the cyclic fatigue resistance of these instruments in a single and double (S- shape) canal curvatures. Four types of Nickel-Titanium (NiTi) rotary instruments: Protaper Next- X3 (30/0.07), Hyflex CM (30/0.04), EdgeFile- X7 (30/0.04), and XP-endoShaper (30/0.01) were evaluated. Each brand of the NiTi instruments was divided into 4 groups (n=20/each group; 10/subgroup) during the cyclic fatigue test as followed: Group 1 (control group) was composed of new instruments without immersed in NaOCl or subjected to autoclave sterilization at room temperature. Group 2 was composed of instruments with immersed in 5% NaOCl solution without sterilization at body temperature, Groups 3 was composed of instruments with immersed in 5% NaOCl solution and 1-time sterilization at body temperature. Groups 4 was composed of instruments immersed in 5% NaOCl solution with 5-times sterilization at body temperature. The number of cycles to failure (NCF) was calculated. The fracture surface of instruments was assessed by using a scanning electron microscope (SEM). The files were tested for bending resistance by using a cantilever- bending test (n=20/each brand). Vickers microhardness was measured on the cross-section of instruments with 300-g load and 15-second dwell time (n=20/each brand). Statistical analysis was carried out using a three-way analysis of variance (ANOVA) and Bonferroni's post hoc analysis for cyclic fatigue test, and one-way analysis of variance (ANOVA) and Games-Howell post hoc analysis for bending resistance and microhardness tests. The statistical significance level was established at p < 0.05. The results show that, the difference in the NCF of all the instruments was statistically significant (p < 0.05). The NCF of EdgeFile and XP -endoShaper were higher than Hyflex CM and PTN (p < 0.05) in all tested groups. The NCF was significantly influenced by the file types (p < 0.05) in all tested groups, angle and curvature locations (p < 0.05) in all tested files except PTN (p > 0.05), and surrounding medium conditions (p < 0.05) in all tested files except PTN and Hyflex CM (p > 0.05). No statistical difference in the length of the separated part at all tested groups (p > 0.05) except at angle and curvature locations (p < 0.05). The ranking in bending resistance values was as follows: PTN > HCM > EdgeFile > XP-endoShaper. The order of the microhardness test from lowest to highest values was as follows: Hyflex CM < XP-endoShaper < PTN and EdgeFile, and there was no statistical difference between PTN and EdgeFile (p > 0.05). In conclusion, EdgeFile significantly outperforms other brands in terms of fatigue resistance, followed by XP-endoShaper. All files except PTN showed a significant decrease in NCF in more challenging canals. The NCF of both EdgeFiles and XP-endoShaper is harmed by body temperature and NaOCl immersion, whereas sterilization has a favorable influence on EdgeFile's NCF but a detrimental one on XP- endoShaper's. In comparison to the other brands examined, XP-endoShaper demonstrated the most flexibility, followed by EdgeFile. When compared to other brands, PTN and EdgeFiles showed greater wear resistance.
Benzer Tezler
- Farklı glide path eğelerinin kullanma protokollerini değiştirerek kırılma dayanımlarının araştırılması: İn vitro bir çalışma
Evaluation of cyclic fracture strengths by changing the usage protocols of different glide path files
FATİH UÇAR
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiTokat Gaziosmanpaşa ÜniversitesiEndodonti Ana Bilim Dalı
DOÇ. DR. HÜDA MELİKE BAYRAM
- Farklı üretim işlemleri kullanılarak üretilmiş yeni nesil nikel-titanyum döner eğe sistemlerinin şekillendirme yeteneklerinin ve döngüsel yorgunluk dirençlerinin karşılaştırmalı olarak incelenmesi
Comparative evaluation of the shaping ability and cyclic fatique resistance of new generation nickel-titanium rotary file systems manufactured by different manufacturing processes
EMRAH KARATAŞLIOĞLU
Doktora
Türkçe
2015
Diş HekimliğiGaziantep ÜniversitesiEndodonti Ana Bilim Dalı
DOÇ. DR. CİHAN YILDIRIM
PROF. DR. TAYFUN ALAÇAM
- Estetik zirkonyum, polietereterketon ve polieterketonketon implant dayanakları üzerine yapılan lityum disilikatla güçlendirilmiş CAD/CAM monolitik cam seramik kronların yaşlandırma işlemi sonrası kırılma dayanımlarının ve kırılma tiplerinin in vitro değerlendirilmesi
Evaluation of fracture resistance and fracture types of titanium sub-structured zirconium, polyetheretherketone, polyetherketoneketone implant abutments restored with lithium disilicate reinforced monolithic CAD/CAM glass ceramic crowns after cyclic fatique loading
ALMİRA ADA DİKEN TÜRKSAYAR
Diş Hekimliği Uzmanlık
Türkçe
2019
Diş HekimliğiKırıkkale ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. SAADET SAĞLAM ATSÜ
- Farklı estetik abutmentların döngüsel yorulma yüklemesi sonrasında kırılma dayanımlarının değerlendirilmesi
The evaluation of the ftacture strenght of different esthetic abutment after cyclic fatique loading
BERNA BALCI
Yüksek Lisans
Türkçe
2015
Diş HekimliğiBezm-i Alem Vakıf ÜniversitesiAğız Diş ve Çene Cerrahisi Ana Bilim Dalı
PROF. DR. ASLIHAN ÜŞÜMEZ
- Ağartma işleminin temel metal alaşımı üzerindeki etkisinin in vitro değerlendirilmesi
In vitro evaluation of the effect of bleaching on base metal alloy
EVŞEN TAMAM
Doktora
Türkçe
2008
Diş HekimliğiAnkara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. A. KEVSER AYDIN