Üniversal adezivlerin farklı biyoaktif materyal ve dentin kompleksine bağlanma dayanıklılığına etkisi
Effect of universal adhesives on the shear bond strength of different bioactive materials and dentine complex
- Tez No: 700161
- Danışmanlar: PROF. DR. NURAY ATTAR
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2021
- Dil: Türkçe
- Üniversite: Hacettepe Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 110
Özet
Bu in vitro çalışmanın amacı; restoratif diş hekimliğinde pulpa kaplaması veya kaide olarak sıklıkla kullanılan biyoaktif materyaller olan kalsiyum silikat dolduruculu rezin içerikli liner (TheraCal LC), rezin modifiye cam iyonomer siman (Riva LC), geleneksel cam iyonomer siman (Riva SC) ve mineral trioksit agregatın (BioMTA+) kompozit restorasyonlar altında kullanıldığında, farklı üniversal adeziv sistemlerin (Single Bond Üniversal Adeziv, 3M ve Prime&Bond Üniversal, Dentsply), bu biyoaktif materyal ve dentin kompleksine bağlanma dayanıklılıklarının incelenmesidir. Kesme bağlanma dayanıklılığı analizlerinin yapılması için çekilmiş insan molar dişleri separe yardımıyla köklerinden ayrılmış ve akrilik bloklar içine yerleştirilmiştir. Bukkal yüzeylerinde dentin dokusu açığa çıkarılan örnekler rastgele 8 gruba ayrılmıştır (G1: Theracal LC + Single Bond (SB) (T-SB), G2: Riva LC + SB (RLC-SB), G3: Riva SC + SB (RSC-SB), G4: BioMTA+ + SB (M-SB), G5: Theracal LC + Prime&Bond (PB) (T-PB), G6: Riva LC + PB (RLC-PB), G7: Riva SC 4 PB (RSC-PB), G8: BioMTA+ + PB (M-PB)) (n=10). 1 mm çapındaki fissür frezlerle dentin dokusu içerisinde 1 mm çapında ve 1 mm derinliğinde su soğutması altında preparasyonlar yapılmış, 80 adet örnek içindeki preparasyonlar eşit sayıda olacak şekilde (n=20) bahsedilen 4 farklı biyomateryal ile doldurulmuştur. Dentin ve biyomateryal kompleksini kaplayacak şekilde 15 sn süreyle %37 ortofosforik asit uygulaması yapılmış ve suyla yıkanıp kurutulmuştur. Hazırlanan örneklerin yarısına Single Bond Üniversal Adeziv (3M), diğer yarısına ise Prime&Bond Üniversal (Dentsply) adeziv sistemi uygulanarak 2 mm yükseklik ve 2 mm çapındaki kompozit bloklar bağlanmıştır. Hazırlık aşaması tamamlanan örnekler 37C'de 48 saat süreyle distile suda bekletilmiştir. Örnekler, 37C, 5C ve 55C'lerde 10.000 termal siklus döngüsüne maruz bırakılmıştır. Bu işlemleri takiben, tüm örneklere üniversal test cihazında 0,5 mm/dk kafa hızı ile başarısızlık meydana gelene kadar yük uygulanmıştır. Kırılan örnekler x10 büyütmeli bir stereomikroskop yardımıyla kırılma tiplerinin analizi için incelenmiştir. Elde edilen veriler T-testi ve iki yönlü ANOVA testleriyle analiz edilmiştir. Kesme bağlanma dayanıklılık verilerinin değerlendirilmesinin sonucunda, en yüksek bağlanma dayanıklılığını Theracal LC göstermiştir (p Riva LC> Riva SC> BioMTA+ şeklinde sıralanabilir. Kullanılan iki farklı üniversal adezivin bağlanma dayanıklılığına etkisi karşılaştırıldığında istatistiksel olarak anlamlı bir fark bulunmamıştır (p>0,05). Kırılma tipi sonuçlarına göre, Theracal LC ve Riva LC için adeziv başarısızlık, BioMTA+ için koheziv başarısızlık en yaygın görülen kırılma tipi olmuştur.
Özet (Çeviri)
The aim of this in vitro study study is to examine the effect of different universal adhesive systems (Single Bond Universal Adhesive, 3M and Prime&Bond Universal, Dentsply) on bond strength of four different bioactive materials frequently used as pulp coating or base material under composite restorations in restorative dentistry; calcium silicate filled resin-containing liner (TheraCal LC), resin-modified glass ionomer cement (Riva LC), glass ionomer cement (Riva SC) and mineral trioxide aggregate (BioMTA+) and dentin complex to composite restorations. Extracted human molar teeth were separated from their roots and placed in acrylic blocks for shear bond strength analysis. Samples with exposed dentin tissue on their buccal surfaces were randomly divided into 8 groups (G1: Theracal LC + Single Bond (SB) (T-SB), G2: Riva LC + SB (RLC-SB), G3: Riva SC + SB (RSC-SB), G4: BioMTA+ + SB (M-SB), G5: Theracal LC + Prime&Bond (PB) (T-PB), G6: Riva LC + PB (RLC-PB), G7: Riva SC 4 PB (RSC-PB), G8: BioMTA+ + PB (M-PB)) (n=10). Preparations with 1 mm diameter and 1 mm depth were made in the dentin tissue under water cooling using 1 mm diameter fissure burs and the preparations in all 80 samples were filled with 4 different biomaterials in equal numbers (n=20). 37% orthophosphoric acid was applied for 15 seconds the dentin and biomaterial complex and washed with water and dried. Single Bond Universal Adhesive (3M) was applied to half of the prepared samples, the other half was treated with Prime&Bond Universal (Dentsply) adhesive system and 2 mm high and 2 mm diameter composite blocks were bonded to the biomaterial dentin complex. Once the preparation phase was completed, samples were kept in distilled water at 37°C for 48 hours. The samples were exposed to 10,000 thermal cycles at 37C, 5C ve 55C. Following these procedures, load was applied to all samples in the universal test device with a head speed of 0.5 mm/min until failure occurred. Fractured samples were examined for the analysis of fracture types with the aid of a x10 magnification stereomicroscope. Obtained data were analyzed with T-test and two-way ANOVA tests. As a result of the evaluation of shear bond strength data, Theracal LC showed the highest bond strength (p Riva LC> Riva SC> BioMTA+. When the effects of two different universal adhesives on bond strength was compared, no statistically significant difference was found (p>0.05). According to the results of the fracture type analysis, adhesive failure for Theracal LC and Riva LC and cohesive failure for BioMTA+ was the most common type of fracture.
Benzer Tezler
- Farklı biyoaktif pulpa kaplama materyallerinin sertleşme zamanlarının dental adezivler ile olan bağlanma dayanımına etkisinin değerlendirilmesi
Evaluation of the effect of setting times on shear bond strength of different bioactive pulp capping materials to dental adhesives
ASLIHAN KANAT
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiMarmara ÜniversitesiEndodonti Ana Bilim Dalı
DOÇ. DR. DİLEK TÜRKAYDIN
- Komplike olmayan kron kırıklarının tedavisinde insizal fragmanınreataçmanında kullanılan universal adezivlerin farklı uygulamatekniklerinin ve ph'larının kırılma dayanımı üzerine etkisininaraştırılması
The effect of different application techniques and ph values of universaladhesives used in the reattachment of incisal fragment of non-complicated crownfractures on fracture strength
ZEYNEP BAĞDATLI
Diş Hekimliği Uzmanlık
Türkçe
2024
Diş HekimliğiHacettepe ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. UZAY KOÇ VURAL
- Farklı üniversal adezivlerin remineralize mineye etkisinin makaslama bağlanma dayanımı ve SEM/EDX analizi ile değerlendirilmesi
Evaluation of the effect of different universal adhesives on remineralized enamel by shear bond strength and SEM/EDX analysis
BEYZA ARSLANDAŞ DİNÇTÜRK
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiGazi ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ CEMİLE KEDİCİ ALP
- Esnek rezin nanoseramik CAD/CAM blokların tamirinde uygulanan farklı yüzey işlemleri ve farklı universal adezivlerin bağlanma dayanımına etkisi
Effect of different surface treatments and universal adhesives on the repair bond strength of flexible resi̇n nano-ceramic CAD/CAM blocks
İBRAHİM DOĞAN
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiOndokuz Mayıs ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. EMEL KARAMAN
- Titanyum altyapı üzerinde kullanılan seramik abutmentların bağlantısına farklı universal adeziv sistemlerin etkisi
The effect of different universal adhesive systems on the bonding of ceramic abutments and titanium bases
HÜSNİYE YILDIRIM
Diş Hekimliği Uzmanlık
Türkçe
2020
Diş HekimliğiOrdu ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ AYÇA TULGA