Asidik alüminyum klorür çözeltisinden demirin solvent ekstraksiyonla uzaklaştırılması
Removal of iron from acidic aluminum chloride solution by solvent extraction
- Tez No: 744362
- Danışmanlar: PROF. DR. MURAT ERDEMOĞLU
- Tez Türü: Yüksek Lisans
- Konular: Maden Mühendisliği ve Madencilik, Mining Engineering and Mining
- Anahtar Kelimeler: Asidik alüminyum klorür çözeltisi, Demir uzaklaştırma, Solvent ekstraksiyon, D2EHPA, Alüminyum klorür, Demir uzaklaştırma prosesleri, Çözücü özütlemesi, Acidic aluminum chloride solution, Iron removal, Solvent extraction, D2EHPA, Aluminum chloride, Iron removal processes
- Yıl: 2022
- Dil: Türkçe
- Üniversite: İnönü Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Maden Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Cevher Hazırlama Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Yüksek asit konsantrasyonlu çözeltilerde demirin seçici olarak uzaklaştırılması, endüstriyel üretimde önemli bir role sahiptir. Bu tez çalışmasında, asidik alüminyum klorür çözeltisinden demirin solvent ekstraksiyonla uzaklaştırılması araştırılmıştır. Organik faz olarak kerosen içerisinde di 2-etilhekzil fosforik asit (D2EHPA) kullanılmıştır. Yapay çözeltilerde reaksiyon süresi, organik/sulu faz oranı (O/S) hidroklorik asit, D2EHPA, demir, alüminyum, potasyum ve sodyum konsantrasyonlarının demir uzaklaştırma üzerindeki etkileri incelenmiştir. Hidroklorik asit ve D2EHPA konsantrasyonlarının artmasıyla demir uzaklaştırma verimi artmıştır. Yapay çözeltilerde yapılan çalışmalar, klorür konsantrasyonunun demir uzaklaştırma üzerinde etkili olduğunu göstermiştir. Ekstraksiyon adımlarının sayısını belirlemek için yapılan çalışmalar sonucunda McCabe-Thiele diyagramı elde edilmiştir. McCabe-Thiele diyagramına göre; organik/sulu faz oranı (O/S) 1/1 iken, >91% verimle demiri uzaklaştırmak için iki aşamanın gerekli olduğu belirlenmiştir. 2 M HCl yüklü liç çözeltisinde hacimce % 20 D2EHPA konsantrasyonu ve 1/1 organik/sulu faz oranı ile 30 dakika oda sıcaklığında gerçekleştirilen çalışmalarda demir uzaklaştırma % 95,58'e ulaşmıştır. FT-IR spektrumu Fe (III)'ün D2EHPA ile kompleks oluşturduğunu ve sulu fazdan organik faza geçtiğini göstermiştir. Sonuçlar asidik alüminyum klorür çözeltisinden yüksek seçiciliğe sahip D2EHPA kullanımıyla, % 2'den daha az alüminyum kaybı ile demirin başarılı bir şekilde uzaklaştırıldığını göstermiştir.
Özet (Çeviri)
The selective removal of iron in high acid concentration solutions has an important role in industrial production. In this thesis, the removal of iron from acidic aluminum chloride solution by solvent extraction was investigated. Di 2-ethylhexyl phosphoric acid (D2EHPA) in kerosene was used as the organic phase. The effects of reaction time, organic/aqueous phase ratio (O/S), hydrochloric acid, D2EHPA, iron, aluminum, potassium and sodium concentrations on iron removal were investigated in artifıcial solutions. The ıron removal efficiency increased with increasing hydrochloric acid and D2EHPA concentrations. Studies in artifıcial solutions show that the chloride concentration has an effect on iron removal. As a result of the studies carried out to determine the number of extraction steps, the McCabe-Thiele diagram was obtained. According to the McCabe-Thiele diagram; While the organic/aqueous phase ratio (O/S) is 1/1, it has been determined that two stages are required theoretically to remove iron with >91% efficiency. Iron removal reached 95.58% in studies carried out at room temperature for 30 minutes with 20% vol. D2EHPA concentration and 1/1 organic/aqueous phase ratio in 2 M HCl pregnant leaching solution (real solution). The FT-IR spectrum reveals that Fe(III) forms a complex with D2EHPA and passes from the aqueous phase to the organic phase. The results showed that with the use of high selectivity D2EHPA from the acidic aluminum chloride solution successfully removal of iron with less than 2% aluminum loss.
Benzer Tezler
- Corrosion and corrosion protection properties of binary Fe-Al alloys-intermetallics
İkili Fe-Al alaşımlarının-intermetaliklerinin korozyon ve korozyondan koruma özellikleri
BURCU EROĞLU
Yüksek Lisans
İngilizce
2021
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. MUSTAFA KAMİL ÜRGEN
- Nanoceria katalizörü ile üretilen reaktif türlerin süpürülme etkinliğinin ölçümü için yöntem geliştirilmesi
Development of a novel method to measure the scavenging activity of reactive species produced using nanoceria as a catalyst
GÖZDE MEDİHA KAMER
Doktora
Türkçe
2019
Kimyaİstanbul Teknik ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. BİRSEN DEMİRATA ÖZTÜRK
- Aluminyum 7075 alaşımının sodyum klorür ortamında çukur korozyonuna amino asit ve hidroksi karboksilik asitlerle nitrat iyonunun etkisi
Başlık çevirisi yok
AYSEL YURT
Yüksek Lisans
Türkçe
1997
KimyaEskişehir Osmangazi ÜniversitesiKimya Ana Bilim Dalı
DOÇ.DR. GÖZEN BEREKET
- Alünitli kaolenlerin kimyasal yöntem ile sülfat giderilmesi, alünütli kaolenlerin potasyum sülfat ve alüminyum sülfat üretiminde kullanılması
The removal of sulphate from alunitic kaolins by chemical method the utilization in potassium sulphate and alüminium sulphate production
MİNE ÖZDEMİR
Doktora
Türkçe
1995
KimyaEskişehir Osmangazi ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF.DR. HALİL ÇETİŞLİ
- Diğer metallerle karşılaştırmalı olarak piritin (FeS2) korozyon davranışı üzerinde bazı maddelerin etkisi
Investigation of the corrosion behaviour of pyrite by comparison with other metals
ESMA SEZER