The effects of different surface treatments on shear bond strength of polyetheretherketone (PEEK) and polyetherketoneketone (PEKKTON) materials to veneering composite
Polyetheretherketone (PEEK) ve polyetherketoneketone (PEKKTON) materyalleri üzerine farklı yüzey işlemleri uygulanarak veneerlenmiş kompozit ile arasındaki makaslama kuvvetinin değerlendirilmesi
- Tez No: 772094
- Danışmanlar: DR. ÖĞR. ÜYESİ BURCU BAL
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: PEEK, PEKKTON, kumlama, SEM, makaslama bağlanma kuvveti, Dental materyaller, Dental stres analizi, Diş kaplamaları, Mikroskopi-elektron taramalı, Polietereterketon, Polieterketonketon, Yüzey işleme tekniği, PEEK, PEKKTON, air abrasion, SEM, shear bond strength, Dental materials, Dental stress analysis, Dental veneers, Microscopy-electron scanning, Polyetheretherketone, Polyetherketonketone, Surface handling technique
- Yıl: 2022
- Dil: İngilizce
- Üniversite: Yeditepe Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Protetik Diş Tedavisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu in vitro çalışmanın amacı, PEEK ve PEKKTON materyalleri ile veneerlenmiş kompozit arasındaki makaslama kuvveti üzerinde dört farklı yüzey işlemi ve termosiklus işleminin etkilerini değerlendirmektir. Gereç ve Yöntem: 115 PEEK ve 115 PEKKTON diski yüzey işlemlerine göre 5 gruba ayrıldı; yüzey işlemi uygulanmayan grup (kontrol), 50 µm'lik Al2O3 ile kumlama uygulanan grup, 110 µm'lik Al2O3 ile kumlama uygulanan grup, 3M Cojet ile silika kaplama uygulanan grup, %98'lik sülfürik asit uygulanan grup. Yüzey pürüzlülüğü profilometre ve taramalı elektron mikroskobu (SEM) ile incelenmiştir. PEEK ve PEKKTON yüzeylerine visio.link adeziv ve ardından GC Gradia veneerlenmiş kompozit uygulanmış ve ışıkla sertleştirilmiştir. Ardından tüm gruplar termosiklus işlemi uygulanıp uygulanmamasına göre iki alt gruba daha ayrılmıştır (n=11). Makaslama bağlanma kuvveti ölçülmüştür ve başarısızlık analizi yapılmıştır. Veriler, İki Yönlü ANOVA, Üç Yönlü ANOVA kullanılarak değerlendirildi. Bulgular: PEEK (1.325 µm) ve PEKKTON örneklerinde en yüksek yüzey pürüzlülük değerleri 110 µm'lik Al2O3 ile kumlama gruplarında görülmüştür (p<0.05). PEEK örneklerinde en yüksek makaslama bağlanma kuvveti değerlerine sahip grup 50 µm'lik Al2O3 ile kumlama grubu iken, PEKKTON örneklerinde en yüksek değerler 110 µm'lik Al2O3 ile kumlama grubunda gözlenmiştir (p<0.05). Termosiklus sonrası tüm gruplarda makaslama bağlanma kuvveti değerleri azalmıştır. PEEK örneklerinde en çok adeziv kopma görülürken PEKKTON örneklerinde karma kopma görülmüştür. Sonuç: PEEK ve PEKKTON örneklerinde yüzey pürüzlülüğü ve makaslama bağlanma kuvveti açısından en etkili yüzey işlemi Al2O3 partikülleri ile kumlama olmuştur. Termosiklus uygulanmış örneklerde bağlantı kuvveti azalmıştır.
Özet (Çeviri)
Purpose: The purpose of this in vitro study was to evaluate the effects of four different surface treatments and thermocycling process on shear bond strength between PEEK/PEKKTON and indirect composite. Materials and Methods: 115 PEEK and 115 PEKKTON discs were divided into five groups according to surface treatment methods; no treatment (control), air abrasion with 50 µm Al2O3, air abrasion with 110 µm Al2O3, silica coating with 3M Cojet, etching with 98% sulfuric acid.. The surface roughness was examined with profilometer and scanning electron microscopy (SEM). After surface treatments, Visio.link adhesive with GC Gradia veneering composite was applied on PEEK and PEKKTON surfaces and light-cured. Then, all groups were divided into two subgroups according to whether thermocycling process was applied or not (n=11). Shear bond strength was measured and failure analysis was performed. The data were analyzed using a Two-Way ANOVA, Three-Way ANOVA. Results: The highest surface roughness values in PEEK and PEKKTON samples were seen in the air abrasion with 110 µm Al2O3 groups (p<0.05). In the PEEK samples, the group with the highest shear bond strength values was in the air abrasion with 50 µm Al2O3 group, while the highest values in the PEKKTON samples were observed in the air abrasion with 110 µm Al2O3 group (p<0.05). Shear bond strength values decreased in all groups after thermocycling. Adhesive failure is the most common in PEEK samples, while mixed failure in PEKKTON samples. Conclusions: In the samples of PEEK and PEKKTON, the most effective surface treatment in terms of surface roughness and shear bond strength is air abrasion with Al2O3 particles. The bond strength decreased in the thermocycled samples.
Benzer Tezler
- Seramik birleştirme teknolojisi ve yapısal seramiklerin lehimlenmesi
Ceramic foining technology and brazing of structural ceramics
OSMAN AKKOCA
- Farklı porselen türlerinde, asitle pürüzlendirme ve silan bağlantı ajanlarının rezin siman-porselen bağlantı kuvvetleri üzerine etkileri
The Effects of acid etching and silane coupling agents on the bond strenght of resin cement-porcelain, when used with different types of porcelain
ALEV İNAN
- Smear kaldıran bir yüzey ajanı uygulamasının pulpada oluşturabileceği değişikliklerin incelenmesi ve üç yapıştırma simanının dentine bağlantısı üzerindeki etkisinin karşılaştırılması
Investigation of changes occured on dentin-pulp complex treated with a smear removal agent and comparison of effects of three luting cements to dentinal bonding
İLGÜN ÇALIŞKAN
Doktora
Türkçe
1997
Diş HekimliğiGazi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. SEVDA SUCA
- Adesiv körülerde kullanılan metallerde farklı yüzey pürüzlendirme işlemlerinin tutuculuğa olan etkilerinin incelenmesi
Evaluation of effects of different surface treatment on retention in different alloys used for adhesive bridges
SAİP DENİZOĞLU
Doktora
Türkçe
1999
Diş HekimliğiAtatürk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. LÜTFÜ İHSAN ALADAĞ
- Yüzey işlemleri ve silan/ bonding ajanı uygulamalarının porselen yapay diş-protez kaidesi bağlantısına olan etkinlikleri
Effects of surface treatment and silane/ bonding agents on bond strength of denture base resin to porcelain denture teeth
YEŞİM ERDEM ERMİŞ
Doktora
Türkçe
2001
Diş Hekimliğiİstanbul ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF.DR. HALUK KESKİN
- Carisolv jelinin çürük süt dişleri üzerindeki etkisinin in vivo ve in vitro olarak incelenmesi
Investigation of the effets of carisolv gel on decidious carious teeth: in vivo and in vitro study
GÜLÇİN FATMA BULUT