Doğal ve yapay elyaflar ile güçlendirilmiş puzolan ikameli alçı sıvaların fiziksel ve mekanik özelliklerinin belirlenmesi
Investigation of physical and mechanical properties of pozzolan substituted gypsum plasters strengthened with natural and artificial fibers
- Tez No: 809610
- Danışmanlar: PROF. DR. SERVET YILDIZ
- Tez Türü: Yüksek Lisans
- Konular: İnşaat Mühendisliği, Civil Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2023
- Dil: Türkçe
- Üniversite: Fırat Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Yapı Malzemeleri Bilim Dalı
- Sayfa Sayısı: 97
Özet
Ülkemizdeki zengin alçı taşı rezervi, kolay üretim yöntemleri ve düşük maliyetinden dolayı alçının daha geniş kullanım alanı bulması hem ekonomik açıdan hem de enerji tasarrufu açısından önemlidir; insanlık tarihinde kullanılan en eski yapı malzemelerinden biri olan alçı, iyi bir ses ve ısı yalıtkanı olmasına karşın düşük mekanik özellikleri ile karşımıza çıkmaktadır. Bu tez çalışmasında alçıya farklı oranlarda silis dumanı, yüksek fırın cürufu, kenevir lifi ve cam lifi eklenerek, mekanik özellikleri ve suya karşı direnci yüksek olan alçı sıvalar elde etmek hedeflenmiştir. Taguchi metodu kullanılarak karışım oranları belirlenmiş ve böylece daha az deney sayısı ile daha çok parametrenin analizi yapılmış, kapsamlı sonuçlar elde edilmiştir. Taguchi metodunun kullanılması zaman ve malzeme tasarrufu sağlaması açısından çalışmaya değer katmaktadır. Çalışmada silis dumanı ve yüksek fırın cürufu %0, %10, %20, %30 oranlarında, kenevir lifi ve cam lifi %0, %0,2, %0,4, %0,6 oranlarında kullanılmıştır. Su/bağlayıcı oranı 0.6 ve 0.7 olarak değişken tutulmuştur. Alçı sıvaların işlenebilirliğini test edebilmek için taze haldeki karışımlar üzerinde yayılma tablası ve priz süresi tayini deneyleri yapılmıştır. Üretilen alçı sıva numuneleri üzerinde ise eğilme dayanımı, basınç dayanımı, ultrases geçiş hızı, kapiler su emme ve birim ağırlık deneyleri yapılmış, sonuçlar Taguchi yöntemi ile analiz edilmiştir. Ayrıca üretilen numunelerin mikro yapı incelemelerinde SEM, EDS ve XRD analizlerinden faydalanılarak mineralojik ve morfolojik özellikler tanımlanmıştır. Elde edilen verilere göre puzolan katkısının; basınç ve eğilme dayanımlarında düşüşe sebep olduğu fakat kapiler boşlukları doldurmada iyileştirici etkisi olduğu belirlenmiştir. Lif katkısı arttıkça 7 ve 28 günlük eğilme dayanımı değerlerinde artış görülmüştür.
Özet (Çeviri)
Due to the rich gypsum reserve in our country, easy production methods and low cost, it is important for gypsum to find a wider area of use both in terms of economy and energy saving; plaster, which is one of the oldest building materials used in human history, is a good sound and heat insulator, but with low mechanical properties. In this thesis, it is aimed to obtain gypsum plasters with high mechanical properties and water resistance by adding silica fume, blast furnace slag, hemp fiber and glass fiber to gypsum at different rates. Mixing ratios were determined using the Taguchi method, and thus, more parameters were analyzed with less number of experiments, and comprehensive results were obtained. The use of the Taguchi method adds value to the study in terms of saving time and materials. In the study, silica fume and blast furnace slag were used at the rates of 0%, 10%, 20%, 30%, hemp fiber and glass fiber 0%, 0.2%, 0.4%, 0.6%. The water/binder ratio was kept variable as 0.6 and 0.7. In order to test the workability of gypsum plasters, spreading table and setting time tests were carried out on fresh mixtures. Flexural strength, compressive strength, ultrasound transmission rate, capillary water absorption and unit weight tests were performed on the produced gypsum plaster samples, and the results were analyzed by the Taguchi method. In addition, mineralogical and morphological properties were defined by using SEM, EDS and XRD analyzes in the microstructure examinations of the produced samples. According to the data obtained, the contribution of pozzolan; It has been determined that it causes a decrease in compressive and flexural strengths, but has a healing effect in filling capillary spaces. As the fiber additive increased, the flexural strength values of 7 and 28 days increased.
Benzer Tezler
- Bazalt fiber katkısının killi zeminlerin drenajsız kayma direncine etkisi
The effect of basalt fiber addition on undrained shear strength of clayey soils
PINAR OCAKBAŞI
Yüksek Lisans
Türkçe
2019
İnşaat MühendisliğiSakarya Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DOÇ. DR. SEDAT SERT
- Exural behavior of selfcompacting reinforced concrete beams incorporating steel fibers and nano-glass powder
Kendiliğinden yerleşen betonarmanın dış davranışıçelik lif içeren kirişler ve nanocam tozu
FIRAS MOHAMMED ABED ABED
Yüksek Lisans
İngilizce
2023
İnşaat MühendisliğiAltınbaş Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. ZEKİ HASGÜR
- Dimethyl phthalate treatment with zero-valent iron based advanced oxidation process
Dimetil ftalatın sıfır değerlikli demir bazlı ileri oksidasyon prosesleri ile arıtımı
ÇİĞDEM BİHTER YAZICI
Yüksek Lisans
İngilizce
2017
Çevre Mühendisliğiİstanbul Teknik ÜniversitesiÇevre Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. TUĞBA ÖLMEZ HANCI
- Investigation of self crimp method as applied to polypropylene fibers
Kendiliğinden kıvrılma metodunun polipropilen elyafına uygulanmasının üzerine araştırması
SERDAR KARAVELİ
Yüksek Lisans
İngilizce
2007
Tekstil ve Tekstil MühendisliğiGaziantep ÜniversitesiTekstil Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. MEHMET TOPALBEKİROĞLU
PROF. DR. ALİ DEMİR
- Farklı oryantasyon açılarına sahip jüt takviyeli kompozitlerin frezelenmesinin araştırılması
Investigation of milling of jute reinforced composites with different orientation angles
ALİ İMRAN KILIÇKAP
Yüksek Lisans
Türkçe
2018
Makine MühendisliğiBatman ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. YAHYA HIŞMAN ÇELİK