Beyazlatma ve antioksidan ajanların CAD/CAM ve estetik restoratif materyallerin fiziksel özellikleri üzerindeki etkileri
Effects of bleaching and antioxidant agents on the physical properties of CAD/CAM and aesthetic restorative materials
- Tez No: 818881
- Danışmanlar: DR. ÖĞR. ÜYESİ MERVE GÜRSES
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Antioksidanlar, Askorbik asit, CAD/CAM, Dental estetik, Dental materyaller, Dental restorasyon, Diş beyazlatma, Hidrojen peroksit, Mikrosertlik, Yüzey pürüzlülüğü, Antioxidants, Ascorbic acid, CAD/CAM, Dental aesthetics, Dental materials, Dental restoration, Tooth bleaching, Hydrogen peroxide, Microhardness, Surface roughness
- Yıl: 2023
- Dil: Türkçe
- Üniversite: Selçuk Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Restoratif Diş Tedavisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu in vitro çalışmanın amacı, üç farklı universal kompozit materyale (G-aeniel A'chord; GCA, Filtek Ultimate; FU, Clearfil Majesty ES-2; CM) ve iki rezin esaslı CAD/CAM bloğa (Lava Ultimate; LU, GC Cerasmart; GCC) ofis tipi (OB) ve ev tipi (HB) beyazlatma ajanları ve sonrasında askorbik asit (AA) uygulamasının materyallerin pürüzlülük, mikrosertlik ve renk değişimi gibi fiziksel özellikleri üzerindeki etkilerini değerlendirmektir. Kompozit materyallerden her biri 2 mm kalınlığında ve 8 mm çapında disk şeklinde; CAD/CAM bloklardan ise her biri 14x7x2 mm kalınlığında dikdörtgen prizması şeklinde örnekler hazırlanmıştır. Kompozit ve CAD/CAM materyaller, uygulanan beyazlatma ajanının tipine göre (ev ve ofis tipi) iki alt gruba ayrılmıştır (n=30). Beyazlatma sonrası tüm örneklere AA uygulanmıştır. Tüm örneklerin başlangıç (I), beyazlatma sonrası (B) ve beyazlatma+askorbik asit uygulaması sonrası (BA) yüzey pürüzlülük, mikrosertlik ve renk değerleri ölçülüp kaydedilmiştir. Örneklerin yüzey özelliklerini incelemek için AFM (Atomik Kuvvet Mikroskobu) ve SEM (Taramalı Elektron Mikroskobu) görüntüleri alınmıştır. İstatistiksel analiz için 3-Yönlü Mixed ANOVA ve Bonferroni düzeltmesi uygulanmıştır. Anlamlılık seviyesi %5 olarak belirlenmiştir. Tüm materyallerin yüzey pürüzlülük değerleri ev ve ofis tipi beyazlatma sonrası başlangıç ölçümlerine göre düşüş göstermiştir. CM'nin HB grubunun BA; LU'in HB grubunun B; GCC'ın hem OB hem de HB grubunun B Ra değerleri I'dan anlamlı olarak düşük bulunmuştur. Tüm materyallerin her iki beyazlatma sonrası mikrosertlik değerleri anlamlı olarak azalmıştır (p<0.05). Materyallerin renk değişim değerleri ise beyazlatma yöntemine göre değişkenlik göstermektedir. LU'in yalnızca HB grubunda ΔE2 (BA-I) ΔE1'den (B-I) anlamlı olarak yüksektir (p=0.047). AA uygulaması; CM'nin HB grubunda Ra değerlerini anlamlı olarak azaltmıştır. CM ve GCC'ın HB gruplarında mikrosertlik değerlerini anlamlı olarak arttırmıştır. Beyazlatma ajanları ve askorbik asit uygulaması, materyallerin fiziksel özelliklerini etkilemiştir. Beyazlatma işlemleri sonrası askorbik asit uygulaması ile materyallerin fiziksel özellikleri ya değişmemiş ya da iyileşmiştir. Çalışmanın sonuçlarına göre antioksidan ajan uygulamasının beyazlatma ajanlarının negatif etkilerini iyileştirebileceği klinisyenler tarafından göz önünde bulundurulabilir.
Özet (Çeviri)
The aim of this in vitro study was to evaluate the effects of the application of office (OB) and home (HB) bleaching agents followed by ascorbic acid (AA) to three different universal composite materials (G-aeniel A'chord; GCA, Filtek Ultimate; FU, Clearfil Majesty ES-2; CM) and two resin-based CAD/CAM blocks (Lava Ultimate; LU, GC Cerasmart; GCC) on their physical properties such as roughness, microhardness, and discoloration. Composite materials were prepared as disks, each 2 mm thick and 8 mm in diameter; CAD/CAM blocks were prepared as rectangular prisms, each 14x7x2 mm thick. The composite and CAD/CAM materials were divided into two subgroups according to the type of bleaching agent applied (home and office) (n=30). AA was applied to all specimens after bleaching. Surface roughness, microhardness, and color values of all samples were measured and recorded at baseline (I), after bleaching (B), and after bleaching+ascorbic acid treatment (BA). AFM (Atomic Force Microscopy) and SEM (Scanning Electron Microscopy) images were taken to examine the surface properties of the samples. For statistical analysis, 3-way Mixed ANOVA and Bonferroni correction were applied. The significance level was set at 5%. Surface roughness values of all materials decreased after home and office bleaching compared to initial measurements. BA of the HB group of CM; B of the HB group of LU; B Ra of both OB and HB group of GCC were found to be significantly lower than I. Microhardness values of all materials decreased significantly after both bleaching (p<0.05). The color change values of the materials varied according to the bleaching method. Only in the HB group of LU, ΔE2 (BA-I) was significantly higher than ΔE1 (B-I) (p=0.047). AA application significantly decreased Ra values in the HB group of CM. It significantly increased the microhardness values of CM and GCC in HB groups. Bleaching agents and ascorbic acid treatment affected the physical properties of the materials. The physical properties of the materials either remained unchanged or improved with the application of ascorbic acid after bleaching procedures. According to the results of the study, clinicians may consider that the application of antioxidant agents may improve the negative effects of bleaching agents.
Benzer Tezler
- Diş beyazlatıcı ve antioksidan ajanların etkilerinin dental pulp stem cell (DPSC) hücre dizisinde incelenmesi
The research of the effects of dental bleaching and antioxidant agents on dental pulp stem cell (DPSC) lineage
MUKADDES MERGEN DALYANOĞLU
Doktora
Türkçe
2016
Diş HekimliğiPamukkale ÜniversitesiFizyoloji Ana Bilim Dalı
PROF. DR. SEBAHAT TURGUT
- Devital beyazlatma uygulanmış dişlerde sodyum askorbat, alkol ve kalsiyum hidroksit uygulamalarının kompozit rezinin dentine bağlanma dayanımı üzerine etkilerinin karşılaştırmalı olarak değerlendirilmesi
The comparative evaluation of effects of sodium ascorbate, alcohol and calcium hydroxide applications on bond strength of the composite resin to dentin in devital bleaching applied teeth
BEYHAN BAŞKAN
Diş Hekimliği Uzmanlık
Türkçe
2020
Diş HekimliğiDicle ÜniversitesiEndodonti Ana Bilim Dalı
PROF. DR. ÖZKAN ADIGÜZEL
- Beyazlatılmış dentine adezivin bağlanma stabilitesinde yeşil çay kateşinlerinin etkisinin değerlendirilmesi
Evaluation of the effect of green tea catechins on the bond stability of adhesives to bleached dentin
CANSU YILDIRIM
Tıpta Uzmanlık
Türkçe
2026
Diş HekimliğiRecep Tayyip Erdoğan ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
PROF. DR. MUHAMMET KARADAŞ
- Farklı güncel adeziv sistem ve beyazlatma ajanlarının kullanımı ve antioksidan uygulamasının mine dokusunun bağlanma özelliği üzerine etkilerinin in vitro olarak değerlendirilmesi
Evaluation of the effects of different current adhesive systems and bleaching agents? usage and antioxidant treatment on the bond feature of enamel in vitro.
CEREN ÖZGE BİÇER
Doktora
Türkçe
2012
Diş HekimliğiHacettepe ÜniversitesiDiş Hastalıkları ve Tedavisi Ana Bilim Dalı
PROF. DR. NURAY ATTAR
- Beyazlatma işlemi sonrası yapılan kompozit restorasyonların bağlanma dayanımına antioksidan ajan ve bekletme süresinin etkisi
The effect of antioxidant and delayed bonding time on shear bond strength of composite restoration after bleaching procedure
NESLİHAN GÜLERYÜZ
Doktora
Türkçe
2011
Diş HekimliğiMarmara ÜniversitesiDiş Hastalıkları ve Tedavisi Ana Bilim Dalı
PROF. DR. CAFER TÜRKMEN