Kinetics of polyurethane formation reaction between glycidyl acide polymer (GAP) and desmodur N-100

Glisidil azid polimeri (GAP) ve desmodur N-100 arasındaki poliüretan oluşum tepkimesinin kinetiği

  1. Tez No: 82662
  2. Yazar: SEMA KESKİN
  3. Danışmanlar: PROF. DR. SAİM ÖZKAR
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya, Chemistry
  6. Anahtar Kelimeler: Glisidil azid polimeri (GAP), poliüretan, kinetik, izosayanat, Desmodur N-100, dibütiltin dilorat (DBTDL) vı, Glycidyl azide polymer (GAP), polyurethane, kinetics, isocyanate, Desmodur N-100, dibutyltin dilaurate (DBTDL) IV
  7. Yıl: 1999
  8. Dil: İngilizce
  9. Üniversite: Orta Doğu Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 80

Özet

oz GLISroiL AZID POLİMERİ (GAP) VE DESMODUR N-100 ARASINDAKİ POLİÜRETAN OLUŞUM TEPKİMESİNİN KİNETİĞİ KESKİN, Sema Yüksek Lisans, Kimya Bölümü Tez Yöneticisi: Prof. Dr. Saim Özkâr Temmuz 1999, 80 sayfa Bu tezde glisidil azid polimer (GAP) ve bir poliizosayanat olan Desmodur N-100 arasındaki poliüretan oluşum tepkimesinin kinetiği nicel FTIR ile gözlenmiştir. Poliüretan oluşumu İR spekturumunda 2274 cm“1 'deki NCO geriliminin soğurma bandındaki değişikliğin ölçümü ile izlenmiştir. Tepkime %40-50 dönüşüme kadar ikinci dereceden bir tepkimedir. 55-80°C arasında değişen bir aralıkta elde edilen kinetik verilerin değerlendirilmesinden Arrhenius aktivasyon enerjisi (Ea), aktivasyon entalpisi (AH*), ve aktivasyon entropileri (AS*) sırası ile 47kJ/mol, 44kJ/mol and -196 J.mol^K”1 olarak bulunmuştur. Şu anda kullanılmakta olan yakıt bağlayıcıları ile karşılaştırıldığında tepkimenin yavaş olduğu ve bunun da bir sertleştirme katalizörünün kullanımını gerekli kıldığı saptanmıştır. Serleştirme katalizörü olarak dibütiltin dilorat (DBTDL) kullanılmıştır. GAP ve Desmodur N-100 arasındaki poliüretan oluşum tepkimesinin kinetik olarak incelenmesi göstermiştir ki tepkime katalizör kullanıldığında oldukça hızlanmakta ve katalizör derişimini sabit tutmak kaydıyla yine ikinci derece kinetiğine uymaktadır. Katalizörderişimine bağlı olarak katalizörlü tepkimenin hızı üzerine yapılan bir çalışma katalitik yoldan ilerleyen tepkimenin DBTDL katalizörü derişimine göre derecesinin ve hız sabitinin tespit edilmesini sağlamıştır. Katalitik yoldan ilerleyen tepkimenin hız sabiti 60°C'de 4,37 L-mol'^s“1 iken aynı sıcaklıkta katalizörsüz tepkimenin hız sabiti 3,88x1ü”6 L-moı'^s"1 olarak belirlenmiştir.

Özet (Çeviri)

ABSTRACT KINETICS OF POLYURETHANE FORMATION REACTION BETWEEN GLYCIDYL AZIDE POLYMER (GAP) AND DESMODURN-100 KESKİN, Sema M. S., Department of Chemistry Supervisor: Prof. Dr. Saim Özkâr July 1999, 80 pages In this thesis, kinetics of the polyurethane formation reaction between glycidyl azide polymer (GAP) and a polyisocyanate, Desmodur N-100, was studied in bulk state by using quantitative FTIR spectroscopy. The polyurethane formation was followed by monitoring the change in intensity of the absorption band at 2274 cm“1 for NCO stretching in the JJR. spectrum. The reaction was shown to obey a second order kinetics upto 40-50% conversions. The activation parameters could be obtained from the evaluation of kinetic data at different temperatures in the range of 55-80°C. Arrhenius activation energy (Ea), activation enthalpy (AH*), and activation entropy (AS*) were found to be 47 kJ-mol”1, 44 kJ-mol“1, inand -196 J-mol^-K”1, respectively. The reaction was found to be slow compared to that of the currently used propellant binder, which necessitated the use of a curing catalyst. Dibutyltin dilaurate (DBTDL) was used as the curing catalyst. The kinetic study of the polyurethane formation between GAP and Desmodur-N 100 showed that the reaction is enormously speeded up in the presence of the catalyst and the reaction obeys the second order kinetics provided that the catalyst concentration is kept constant. An investigation on the rate of the catalysed reaction depending on the catalyst concentration delivered the order of the reaction with respect to the DBTDL catalyst concentration and the rate constant for the catalytic pathway of the reaction. The rate constant for the catalytic pathway was established to be 4.37 L-mol^-s“1 at 60°C while the uncatalysed reaction has a rate constant of 3.88X10”6 L-mol'V1 at the same temperature.

Benzer Tezler

  1. Tez No

    93394

    Kinetic study of the reaction between hydroxyl-terminated polybutadiene and isophorone diisocyanate in toluene by fourier transform infrored spectroscopy

    Toluen çözeltisinde hidroksil uçlu polibutadien ile isoforondiisosiyanat arasındaki tepkimenin FTIR spektroskopisi ile kinetik incelenmesi

    A. SERENAY TARHAN

    Yüksek Lisans

    İngilizce

    İngilizce

    2000

    KimyaOrta Doğu Teknik Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. SAİM ÖZKAR

  2. Tez No

    397229

    Kinetic studies on polyurethane formation reactions with infrared and raman spectroscopy: effect of reaction solvent and reaction conditions on prepolymer formation

    Infrared ve raman spektroskopisi kullanılarak poliüretan sentezi üzerine kinetik çalışmalar: organik çözücünün ve reaksiyon koşullarının prepolimer reaksiyonları üzerindeki etkisi

    ARMEN YILDIRIM

    Yüksek Lisans

    İngilizce

    İngilizce

    2015

    KimyaKoç Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    PROF. DR. İSKENDER YILGÖR

  3. Tez No

    131432

    Kompozit roket yakıtlarında polimerizasyon kinetiğine katkı maddelerinin etkisi

    The Effect of the additives used in solid propellant on polymerization kinetics of the composite propellant

    HATİCE ÜRTİŞ

    Doktora

    Türkçe

    Türkçe

    2003

    Kimya MühendisliğiAnkara Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. HASİP YENİOVA

  4. Tez No

    321333

    Elektrostatik eğirme yöntemi ile polibütilen süksinat esaslı nanoliflerin hazırlanması, karakterizasyonu ve doxorubicin salımında kullanımı

    The preparation and characterization of polybutylene succinate based nanofibers via electrospinning and their use for doxorubicin release

    ESRA KILIÇ

    Yüksek Lisans

    Türkçe

    Türkçe

    2012

    KimyaHacettepe Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. NURSEL PEKEL BAYRAMGİL

  5. Tez No

    837060

    5-fluorourasil için polimer/biyoseramik ve grafen oksit içerikli ilaç taşıyıcı malzeme üretimi ve kinetik çalışmaları

    Production and kinetic studies of polymer/bioceramic and graphene oxide containing drug carrier materials for 5-fluorouracil

    EBRU KAHRAMAN

    Doktora

    Türkçe

    Türkçe

    2023

    Kimya Mühendisliğiİstanbul Teknik Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. GÜLHAYAT SAYGILI

Geri Dön