İndirek restorasyonların rezin kaplama uygulanmış diş yüzeyine adezyonunda ısıtılmış kompozit kullanımının bağlanma dayanım değerleri ve film kalınlığı üzerine etkilerinin incelenmesi

Effects of preheated composite on bond strength and film thickness for luting of indirect restorations to resin-coated tooth surfaces

  1. Tez No: 838764
  2. Yazar: SEVDE KURŞUN
  3. Danışmanlar: PROF. DR. NESLİHAN TEKÇE
  4. Tez Türü: Diş Hekimliği Uzmanlık
  5. Konular: Diş Hekimliği, Dentistry
  6. Anahtar Kelimeler: bond strength, immediate dentin sealing, preheated composite, indirect restoration, luting
  7. Yıl: 2023
  8. Dil: Türkçe
  9. Üniversite: Kocaeli Üniversitesi
  10. Enstitü: Diş Hekimliği Fakültesi
  11. Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 88

Özet

Amaç: Kompozit rezinler indirekt adeziv restorasyonların simantasyonu için tercih edilmektedir. Bununla birlikte, rezin simana alternatif bir materyal olup olamayacakları açık bir sorudur. Bu in vitro çalışmanın amacı, indirekt adeziv restorasyonların simantasyonu için kompozit rezin kullanımının mikrotensil bağlanma dayanımı (μ-TBS) ve film kalınlığı üzerine etkilerini değerlendirmektir. Yöntem: Bu çalışmada, 15 adet çekilmiş çürüksüz molar diş kullanıldı (N=15). Dişler, simantasyon için kullanılan materyallere göre rastgele üç deney grubuna ayrıldı (n=5). Kontrol grubu olarak RelyX Ultimate Clicker Adhesive Resin Cement (3M ESPE, St Paul, MN, ABD) (Grup-1) (RLX), Deney grupları olarak; Clearfil Majesty ES-2 kompozit (Kuraray, Kuraray Noritake Dental Inc., Okayama, Japonya) oda sıcaklığında (Grup-2) (ES-2) veya 65 °C'ye ısıtılmış olarak (Grup-3) (PH-ES-2) kullanıldı. Lava Ultimate CAD/CAM rezin bloklardan (3M ESPE) 4 mm kalınlığında alınan kesitler, hazırlanan diş yüzeylerine, oluşturulan gruplara göre simante edildi. 37 °C yapay tükürük içerisinde 24 saat bekletildikten sonra örnekler etüvden alındı. Mikrotensil bağlanma dayanım testi (μ-TBS) için tüm örneklerden kesit alanı 1 mm² olan çubuklar elde edildi. Elde edilen çubuklar μ-TBS cihazında test edildi, bağlanma dayanım değerleri megapaskal (MPa) cinsinden kaydedildi. Örneklerin kopma tipleri stereomikroskop altında incelenerek belirlendi. Film kalınlığı testi için 1 mm kalınlığında kompozit bloklar hazırlandı. Lava Ultimate rezin bloklardan alınan kesitler, hazırlanan kompozit bloklar ile simante edildi (n=6). Simantasyon sonrası örneklerden 1 mm kalınlığında dilimler alındı. Bu dilimler stereomikroskop altında ×40 büyütme ile incelenerek siman tabakasının film kalınlığı ölçüldü. Veriler tek yönlü varyans analizi (ANOVA), Kruskal Wallis Testi, Tukey ve Dunn testleri ile analiz edildi (p

Özet (Çeviri)

Objective: Although composite resins can be used for luting indirect adhesive restorations, there is an open question as to whether they can be an alternative material to resin cement. This in vitro study aimed to evaluate the microtensile bond strength (μ-TBS) and film thickness (FT) of preheated composite resin used as a luting agent for indirect adhesive restorations. Method: Fifteen sound caries-free extracted molars were used in this study (N=15). The teeth were randomly divided into three experimental groups according to the type of luting agents (n=5). RelyX Ultimate Clicker resin cement (3M ESPE, St Paul, MN, USA) at room temperature (RLX) as the control group, and Clearfil Majesty ES-2 composite resin (Kuraray, Kuraray Noritake Dental Inc., Okayama, Japan) both at room temperature (ES-2) and preheated to 65 °C (PH-ES-2) were used. The 4-mm thick resin block (Lava Block, 3M ESPE) was bonded with resin cement or composite resin according to the created groups. After 24-hour storage in 37 °C artificial saliva, all specimens were sectioned into beams at 1 mm² for μ-TBS. The beams were tested in μ-TBS device, bond strength values were recorded. Failure modes were determined by examining under a stereomicroscope. For the film thickness test, composite blocks were prepared and bonded with resin blocks using the materials mentioned above. These samples were cut into 1-mm thick slices. Film thicknesses were measured under a stereomicroscope at ×40 magnification. Data were analyzed using the 1-way ANOVA, Kruskal-Wallis, Tukey, and Dunn test (α0.05). The result of the film thickness test showed that the RLX group showed the thinnest film layer, followed by the PH-ES-2 group. The thickest film layer was observed in the ES-2 group. Conclusions: Indirect adhesive restorations bonded with preheated composite resin showed similar bond strength values to resin cement. Preheating the composite reduced the film thickness.

Benzer Tezler

  1. Rezin coating materyaline uygulanan farklı yüzey işlemlerinin rezin siman-rezin coating arasındaki bağlanma dayanımı üzerine olan etkisinin in vitro incelenmesi

    Effect of surface treatments on bonding between resin coating and resin cement

    ELİF TÜRKEŞ

    Yüksek Lisans

    Türkçe

    Türkçe

    2011

    Diş HekimliğiYeditepe Üniversitesi

    Diş Hastalıkları ve Tedavisi Ana Bilim Dalı

    DOÇ. DR. ESRA CAN

  2. A comparison of flexural strength of peek restorations with varying core and composite resin thickness

    Farklı altyapı ve kompozit rezin kalınlıklarına sahip peek restorasyonlarının bükülme dayanımlarının karşılaştırılması

    PINAR KARAMUSTAFALIOĞLU

    Doktora

    İngilizce

    İngilizce

    2020

    Diş HekimliğiYeditepe Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. ENDER KAZAZOĞLU

  3. Çeşitli adesif yapıştırıcı ajanların farklı indirekt restorasyonlarına olan bağlanma kuvvetlerinin in-vitro incelenmesi

    Bond strength of various adhesive cements to indirect composite resins: An in-vitro study

    AYLİN ÇİLİNGİR

    Doktora

    Türkçe

    Türkçe

    2011

    Diş Hekimliğiİstanbul Üniversitesi

    Diş Hekimliği Bölümü

    PROF. DR. YAVUZ GÖMEÇ

  4. Direkt ve indirekt yöntemlerle uygulanan üç yüzlü kompozit restorasyonların termomekanik yükleme sonrası kenar uyumu ve mikrosızıntı açısından değerlendirilmesi

    Evaluation of mod restorations which are prepared with direct and indirect methods in terms of thermomechanical post-loading edge compatibility and microleakage

    AYŞE ASLI ŞENOL

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2020

    Diş HekimliğiMarmara Üniversitesi

    Restoratif Diş Tedavisi Ana Bilim Dalı

    DOÇ. DR. PINAR YILMAZ ATALI

  5. Bilgisayar destekli tasarım ve üretim (CAD/CAM) ile üç farklı materyalden üretilen tek kronların klinik performansı: Bir yıllık başlangıç sonuçlarının değerlendirilmesi

    Clinical performance of computer aided design and manufacturing (CAD/CAM) single crowns made from three different materials with one year preliminary results

    DİLER ÇETİN

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2018

    Diş HekimliğiHacettepe Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    DOÇ. DR. GÜLİZ AKTAŞ