Güncel post materyallerinin (PEEK, fiber, döküm metal) farklı ferrule koşullarında kırılma dayanımlarının incelenmesi
Investigation of fracture strength of current post materials (PEEK, fiber, cast metal) under different ferrule conditions
- Tez No: 842192
- Danışmanlar: PROF. DR. FUNDA BAYINDIR
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Ferrule, Kırılma dayanımı, Peek post, Dental materyaller, Dental postlar, Fiber post, Polietereterketon, Ferrule, Fracture strength, Peek post, Dental materials, Dental posts, Fiber post, Polyetheretherketone
- Yıl: 2023
- Dil: Türkçe
- Üniversite: Atatürk Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Günümüzde kullanılmakta olan güncel post materyallerinin kırılma dayanımları; post materyalinin kırılma tipini büyük ölçüde etkilemektedir. Bu çalışmada, post materyali olarak kullanımı henüz yaygınlaşmamış olan peek postların kırılma dayanımlarının; oluşacak kırık paterni üzerine etkisinin incelenmesi amaçlanmıştır. Materyal ve Metot: Çalışmada; 66 adet çekilmiş üst santral kesici insan dişi kullanıldı. Metal, fiber ve peek materyallerinden 6 grup (CP-0, CP-1, FP-0, FP-1, PP-0 ve PP-1) oluşturulacak şekilde post üretimleri yapıldı (n=11). Daha sonrasında örnekler 0.2 cm/min hızda zirkonyum kuron kaplamanın palatinal bölgesinden dişin uzun aksı ile 135̊ derece açı yapacak şekilde kırılma dayanımı testine tabi tutuldu. Örnekler, kırık tiplerine göre onarılabilir ve onarılamaz şeklinde sınıflandırıldı. Verilen istatistik analizinde ANOVA testi kullanıldı. Post-hoc testler Tukey ve Tamhane's T2 testi kullanılarak yapıldı. Kategorik değişkenler arasındaki kıyaslamalarda ise Pearson Ki-kare testi ve Fisher-Freeman-Halton testi kullanıldı. İstatistiksel anlamlılık düzeyi p<0.05 olarak alındı. Bulgular: Fraktür dayanımı test sonuçlarına göre, metal kişisel post kullanılan gruplar (CP-0 VE CP-1) diğer tüm gruplardan yüksek kırılma dayanımı göstermiştir. Optik mikroskop incelemesi sonuçlarına göre; ferrule preparasyonu yapılmış olan peek post grubunda (PP-0) onarılabilir tipte kırık görülme oranı diğer gruplardan (CP-0, CP-1, FP-0 ve PP-0) anlamlı derecede yüksek bulunmuştur. (p<0.05) Ferrule preparasyonu yapılmış olan fiber (FP-1) ve peek (PP-1) post grupları arasında anlamlı bir fark bulunmamaktadır. (p>0.05) Sonuç: Ferrule etkisi bulunmayan durumda, kullanılan materyal fark etmeksizin kırıklar katastrofik karakterdedir. Post materyali olarak peek kullanımı, oluşan kırıkların onarılabilir seviyede kalmasına katkı sağlamaktadır.
Özet (Çeviri)
Aim: Fracture strength of peek posts, which have not yet become widespread as a post material; It was aimed to examine its effect on the fracture pattern that will occur. Material and method: In the study; 66 extracted upper central incisor human teeth were used. Posts were produced in 6 groups from metal, fiber and peek materials (n = 11). Afterwards, the samples were subjected to the fracture strength test at a speed of 0.2 cm/min. Specimens were classified according to fracture type as repairable or non-reparable. ANOVA test were used in the given statistical analysis. Post-hoc tests were performed using Tukey and Tamhane's T2 test. After the ANOVA test was used for post-hoc tests. Pearson Chi-square test and Fisher-Freeman-Halton test were used for comparisons between categorical variables. Statistical significance level was taken as p<0.05. Results: Metal post cores showed higher fracture strength than all other groups. According to the results of optical microscope examination; The incidence of repairable fractures in the peek post group (PP-0), which had ferrule preparation, was found to be significantly higher than the other groups). (p<0.05) There was no significant difference between the ferrule-prepared fiber (FP-1) and peek (PP-1) post groups. (p>0.05) Conclusion: In the absence of the ferrule effect, fractures are catastrophic, regardless of the material used. The use of peek as a post material contributes to keeping the fractures at a repairable level.
Benzer Tezler
- Futbolcularda sanal gerçeklik antrenmanının teknik beceri antrenman yükü ve mental yorgunluğa etkisi
The effect of virtual reality training on technical skills training load and mental fatigue in football players
EMRE GÜRBÜZ
Doktora
Türkçe
2024
SporManisa Celal Bayar ÜniversitesiBeden Eğitimi ve Spor Ana Bilim Dalı
PROF. DR. MURAT TAŞ
- Levan bazıı hidrojellerin dental pulpa kaynaklı mezenkimal kök hücreler üzerindeki rejeneratif etkinliklerinin karşılaştırılması
Comparison of the regenerative activities of levan-based hydrogels on dental pulp-derived mesenchymal stem cells
EZGİ ALTUNTAŞ ALPMAN
Doktora
Türkçe
2026
Diş HekimliğiMarmara ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
PROF. DR. CAFER TÜRKMEN
- Foreign language teachers' interactions with their students on learning management systems
Yabancı dil öğretmenlerinin öğretim yönetim sistemleri üzerinden öğrencileri ile etkileşimleri
NECLA BURÇİN GİRİTLİOĞLU
Yüksek Lisans
İngilizce
2023
Eğitim ve Öğretimİstanbul Medeniyet ÜniversitesiYabancı Diller Eğitimi Ana Bilim Dalı
PROF. DR. SELAMİ AYDIN
- Çocuk diş hekimliğinde kullanılan restorasyon materyallerinin sitotoksik, genotoksik ve antimikrobiyal etkinliklerinin karşılaştırılması
Comparison of cytotoxic, genotoxic and antimicrobial effect of restoration materials used in pediatric dentistry
CEREN KAPLAN DİNÇ
Doktora
Türkçe
2024
Diş HekimliğiSağlık Bilimleri ÜniversitesiÇocuk Diş Hekimliği Ana Bilim Dalı
DOÇ. DR. ÖZLEM MARTI AKGÜN
- Güncel ölçü maddelerinin farklı mekanik testler ve ıslanabilirlik açısından değerlendirilmesi
Evaluation of current impression materials in terms of different mechanical tests and wettability
ZİŞAN ÇAPAR
Doktora
Türkçe
2024
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. NECLA DEMİR