Saf aluminyumun 0,1M hidroklorik asit çözeltisindeki korozyonuna bazı heterosiklik bileşiklerin inhibitör etkisi
Inhibition effect of some heterocyclic compounds of pure aluminum in 0,1M hydrochloric acid solution
- Tez No: 84522
- Danışmanlar: PROF.DR. GÖZEN BEREKET
- Tez Türü: Doktora
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Alüminyum, Heterosiklik bileşikler, Korozyon, Çözeltiler, Aluminum, Heterocyclic compounds, Corrosion, Solutions
- Yıl: 1999
- Dil: Türkçe
- Üniversite: Eskişehir Osmangazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET Bu çalışmada, saf alüminyumun 0.1M HC1 ortamında korozyonuna benzotriazol, benzimidazol-2-tiyon ve benzoksazol-2-tiyon türevlerinin inhibitor etkisi potansiyostatik polarizasyon yöntemiyle araştırılmıştır. Bu amaçla heterosiklik bileşiklerin lxlO^M, 5xlO-5M, Ixl0-4M, 5xlO“4M, lxl03M derişimlerini içeren 0.1M HC1 çözeltilerinde korozyon potansiyelleri, Ekor, korozyon hızları, ikor, anodik ve katodik Tafel eğimleri, (3a, (3C inhibitor etkinlikleri, IE, ile kaplanma kesirleri, 0, saptanmıştır, inhibitor etkinlik sırası; benzotriazol türevleri için 5-nitro benzotriazol > 5-metil benzotriazol > 5-klor benzotriazol > benzotriazol şeklindedir. Benzimidazol-2-tiyon türevleri için ise benzimidazol-2-tiyon > 5-metil benzimidazol-2-tiyon > 5-klor benzimidazol-2-tiyon sırasını izlediği bulunmuştur. Diğer yandan benzoksazol-2-tiyon türevleri için inhibitor etkinlik sırası 5-metil benzoksazol-2-tiyon > benzoksazol-2-tiyon > 5-klor benzoksazol-2- tiyon > 5-nitro benzoksazol-2-tiyon sırasını izlediği bulunmuştur. Ayrıca bir diğer inhibitor etkinlik sırasının benzimidazol-2-tiyon > benzoksazol-2-tiyon > benzotiyazoI-2- tiyon şeklinde olduğu bulunmuştur. Heterosiklik bileşiklerin genellikle katodik inhibitor olduğu, inhibitor özelliklerinin alüminyum yüzeyinde adsorpsiyondan kaynaklandığı ve inhibitor etkinliklerinin moleküllerdeki yük yoğunlukları ile paralellik gösterdiği bulunmuştur. Adsorpsiyon izotermlerinden de adsorpsiyon serbest enerjileri, AGads ve adsorpsiyon denge sabitleri, Kads değerleri hesaplanmıştır. 0.1M HC1 ortamında heterosiklik bileşiklerin lxlO”3M ve lxl05M derişimlerini içeren çözeltilerde 20 °C, 30 °C, 40 °C, 50 °C ve 60 °C farklı sıcaklıklardaki korozyon hızları saptanmıştır. Farklı sıcaklıklardaki korozyon hızı değerlerinden aktivasyon enerjileri, Ea, aktivasyon entalpileri, AH*, aktivasyon entropileri, AS* gibi aktivasyon parametreleri belirlenmiştir. Belirlenen bu parametrelerden inhibitörlerin korozyonu önleme mekanizması açıklanmıştır.
Özet (Çeviri)
VI SUMMARY In this study inhibitive behaviour of benzotriazole, benzimidazole-2-tione, and benzoxazole-2-tione derivatives on the corrosion of pure aluminum in 0.1M HCi has been investigated by potentiostatic polarization technique. For this purpose corrosion potentials, Ecorr, corrosion rates, icorr, anodic and cathodic Tafel slopes, Pa, Pc, inhibition efficiencies, IE, surface coverages, 0, of these heterocyclic compounds were determined in 0.1M HCI solutions containing various concentrations (lxlO“5M, 5xlO~5M, lxl(HM, 5xlO~4M, lxlO_3M). The efficiency of benzotriazole derivatives was found to follow the order of 5-nitro benzotriazole > 5-methyl benzotriazole > 5-chloro benzotriazole > benzotriazole while the efficiency of benzimidazole-2-tione was found to follow the order of benzimidazole-2-tione > 5-methyl benzimidazole-2-tione > 5-chloro benzimidazoIe-2- tione. On the other hand efficiency of benzoxazole-2-tione was found to follow the order of 5-methyl benzoxazole-2-tione > benzoxazole-2-tione > 5-chloro benzoxazole-2-tione > 5-nitro benzoxazole-2-tione. Another inhibition order among these heterocyclic compounds was found to be as benzimidazole-2-tione > benzoxazole-2-tione > benzothiazole-2-ti one. It was observed that these heterocyclic compounds mainly behaves as cathodic inhibitor and inhibition actions were due to adsorption on metal surface which shows paralelisin with the total negative charge of each molecule from the adsorption isotherms values of adsorption free energies, AGads and values equilibrium constants, Kads, for the adsorption process. Corrosion rates in 0.1M HCI solutions containing lxI0~3M or 1x10”5M concentration of these heterocyclic compounds were determined at 20 °C, 30 °C, 40 °C, 50 °C, 60 °C. From the corrosion rates at different temperatures activation parameters of the corrosion process such as activation energies, Ea, activation enthalpies, AH* and activation entropies, AS* were determined. From these parameters possible mechanism of the corrosion and inhibition processes were proposed.
Benzer Tezler
- Chemical deintercalation and stability investigation of nanosized C/Li2MnSiO4 cathode material with different electrolytes
C/Li2MnSiO4 katot malzemesinin kimyasal deinterkalasyonu ve farklı elektrolitler ile kararlılığının incelenmesi
EKİN EŞEN
Yüksek Lisans
İngilizce
2015
Mühendislik Bilimleriİstanbul Teknik ÜniversitesiNanobilim ve Nanomühendislik Ana Bilim Dalı
PROF. DR. FİGEN KADIRGAN
- Bor ile modifiye edilmiş titanyum implant yüzeylerde bakteriyel adezyonun ve osteoblast aktivitesinin in vitro analizi
In vitro comparison of titanium surface conditioning via boron-compounds and sand-blasting acid-etching
MOHAMMED ALZBOUN
Doktora
Türkçe
2020
Diş Hekimliğiİstanbul ÜniversitesiOral İmplantoloji Ana Bilim Dalı
PROF. DR. AYŞE CANSU BAŞEĞMEZ
- Preparation of polyacrylonitrile grafted onto nano-clay for removal of aluminum from aqueous solutions
Poliakrilonitril aşılanmış nano-kil sentezi ve alüminyumun sulu ortamlardan uzaklaştırılmasında kullanılması
EDA KÜÇÜK
Yüksek Lisans
İngilizce
2022
Kimyaİstanbul Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF. DR. BAHİRE FİLİZ ŞENKAL
- Al-hava pili için verimli elektrot-elektrolit araştırılması
Investigation of efficient electrode-electrolyte for al-air battery
RASİHA NEFİSE MUTLU
- Hot cracking in welding of aluminum and some of its alloys
Alüminyum ve bazı aluminyum alaşımlarının kaynağında sıcak çatlama
H.FİLİZ CAYMAZ
Yüksek Lisans
İngilizce
1997
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ALPAY ANKARA