Alüminyum bronzların (cupral) tel erozyonda işlenebilirliğinin incelenmesi

Investigation of the machinability of aluminum bronzes on wire electro discharge machine

  1. Tez No: 856123
  2. Yazar: EROL AYDEMİR
  3. Danışmanlar: DOÇ. DR. MEHMET ALTUĞ
  4. Tez Türü: Yüksek Lisans
  5. Konular: Makine Mühendisliği, Mechanical Engineering
  6. Anahtar Kelimeler: Alüminyum bronz, Tel erozyon, Yüzey yanıt yöntemi, Box-benhken, İşlenebilirlik, Aluminum Bronze, Wire electrical discharge machining, Response surface methodology, Box-benhken, Machining
  7. Yıl: 2024
  8. Dil: Türkçe
  9. Üniversite: İnönü Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Uygulamalı Bilimler ve Teknoloji Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 49

Özet

Bu çalışmada, yüksek mukavemet, korozyon direnci ve biyofilm oluşumuna karşı yüksek direnç gibi özellikleriyle gemi pervaneleri, pompalar ve valfler gibi denizcilik uygulamalarında yaygın olarak kullanılan alüminyum-bronz alaşımının tel erozyonda işlenebilirliği incelenmiştir. Tel erozyon parametresi olarak puls ara süresi, yalıtkan sıvı, tel ilerleme hızı ve tel gerginliği seçilmiştir. Bu çalışmanın deneysel tasarımında Box-Behnken yanıt yüzey yöntemi kullanılmıştır. Deneyler, ONA-AF 25 yüksek hassasiyetli CNC Tel erozyon tezgâhında yapılmıştır. Elektrot olarak 0,25 mm çapında çinko kaplı pirinç tel kullanılmıştır. En düşük kerf değeri, puls ara süresi 50 µs, yalıtkan sıvı basıncı 15 bar, tel ilerleme hızı 8 m/dk, tel gerginliği 15 g olduğu deney koşullarında doğrusal kesim yöntemiyle 319 µ olarak elde edilmiştir. Yüzey pürüzlülüğü değerleri Mitutoyo SJ 210 yüzey pürüzlülük test cihazında ölçüldü. Deneysel sonuçlara göre; En düşük yüzey pürüzlülük değeri 1,44 µm olarak, puls ara süresinin 50 µs, yalıtkan sıvı basıncı 15 bar, tel ilerleme hızı 8 m/dk, tel gerginliği 15 g olduğu deney koşullarında döndürerek kesim yöntemiyle elde edilmiştir. En yüksek malzeme kaldırma oranı değeri, puls ara süresi 250 µs, yalıtkan sıvı basıncı 15 bar, tel ilerleme hızı 4 m/dk, tel gerginliği 15 g olduğu deney koşullarında döndürerek kesim yöntemiyle 0,319 µ olarak elde edilmiştir. Bu bağlamda işlenebilirlik çıktılarına göre farklı kesme prosesi ve kesme parametreleri uygulanmasının anlamlı ve etkili olduğu ortaya konulmuştur.

Özet (Çeviri)

In this study, the machinability of aluminum-bronze alloy, which is widely used in marine applications such as ship propellers, pumps, and valves, with its properties such as high strength, corrosion resistance, and high resistance to biofilm formation, has been investigated in wire electrical discharge machining. Time off, dielectric, wire feed, and wire tension were selected as wire electrical discharge machining parameters. Box-Behnken response surface methodology was used in the experimental design of this study. The experiments were carried out on an ONA-AF 25 high-precision CNC wire electrical discharge machining machine. Zinc-coated brass wire with a diameter of 0.25 mm was used as the electrode. The lowest kerf value was obtained as 319 µm with the linear cutting method under the experimental conditions where the time off was 50, dielectric was 15 bar, wire feed was 8 m/min, and wire tension was 15 g. Surface roughness values were measured on a Mitutoyo SJ 210 surface roughness tester. According to the experimental results; The lowest surface roughness value of 1.44 µm was obtained with the rotating cutting method under the experimental conditions where the time off was 50 µs, dielectric was 15 bar, wire feed was 8 m/min, and wire tension was 15 g. The highest material removal rate value of 0.319 µm was obtained with the rotating cutting method under the experimental conditions where the time off was 250, dielectric was 15 bar, wire feed was 4 m/min, and wire tension was 15 g. In this context, it has been revealed that the application of different cutting processes and cutting parameters is significant and effective according to the machinability outputs.

Benzer Tezler

  1. Alüminyum bronz alaşımlarında tane incelticilerin mikroyapı ve mekanik özelliklere etkisi

    The effect of grain refiners on the microstructure and mechanical properties of aluminum bronze alloys

    ALİ RIZA EKİCİ

    Yüksek Lisans

    Türkçe

    Türkçe

    2021

    Metalurji MühendisliğiFırat Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. MEHMET EROĞLU

  2. Alüminyum bronz alaşımlarının aşınma özelliklerinin incelenmesi

    Investigation of the wear properties of aluminum bronze alloys

    SEFA BACAK

    Yüksek Lisans

    Türkçe

    Türkçe

    2022

    Makine MühendisliğiSakarya Uygulamalı Bilimler Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. İBRAHİM ÖZSERT

  3. Alüminyum bronzu (Cu4Ni10Al4Fe) ingotlarının katılaşma yapılarının incelenmesi

    Examination of the solidify structures of the aluminium bronze (Cu4Ni10Al4Fe)

    YAHYA TAŞGIN

    Yüksek Lisans

    Türkçe

    Türkçe

    2001

    Metalurji MühendisliğiFırat Üniversitesi

    Metalurji Eğitimi Ana Bilim Dalı

    YRD. DOÇ. DR. MEHMET KAPLAN

  4. Nikel alüminyum bronz alaşımı ile pervane bağlantı göbeğinin (Hub) kum kalıba döküm yöntemiyle üretilmesi ve temperleme sıcaklığının özelliklerine etkisi

    Production of propeller hub with nickel aluminium bronze alloy by sand mould casting method and effect of tempering temperature on its properties

    YAĞMUR LALECİ

    Yüksek Lisans

    Türkçe

    Türkçe

    2024

    Metalurji MühendisliğiKırıkkale Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. RECEP ÇALIN

  5. Titanyum ilavesinin nikel alüminyum bronzunun yapı ve özelliklerine etkisi

    Effect of titanium addition on structure and properties of nickel aluminum bronze

    TURHAN ÜRÜN KOÇAK

    Yüksek Lisans

    Türkçe

    Türkçe

    2018

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ CEVAT FAHİR ARISOY