Bi-2212 süperiletken sistemine SiO2 katkılanarak elde edilen yeni sistemlerin mekanik performansının deneysel ve teorik yaklaşımlarla incelenmesi
Investigation of the mechanical performance of new systems obtained by adding SiO2 to Bi-2212 superconducting system by experimental and theoretical approaches
- Tez No: 865668
- Danışmanlar: PROF. DR. YUSUF ZALAOĞLU
- Tez Türü: Yüksek Lisans
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2024
- Dil: Türkçe
- Üniversite: Osmaniye Korkut Ata Üniversitesi
- Enstitü: Lisansüstü Eğitim Enstitüsü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 62
Özet
Bi-2212 süperiletken inorganik kristal sistemine 0.00, 0.01, 0.03, 0.05 gibi değişen oranlarda SiO2 katkılanarak elde edilen yeni süperiletken anayapılarının yapısal ve mekanik karakteristikleri sırasıyla X-Işını Kırınımı (XRD) ve Vickers mikrosertlik analizleriyle detaylı olarak incelemeye tabi tutulmuştur. Tez kapsamında hazırlanan tüm örneklerin X-ışını analizi sonucunda Bi-2212 süperiletkenlik fazının diğer fazlara oranla daha baskın olduğu görülmekle birlikte tüm örnekler için hesaplanan örgü parametrelerinin de Bi-2212 anayapısının örgü parametreleriyle de uyum içerisinde olduğu görülmüştür. Hazırladığımız numunelerin endüstriyel ve teknolojik uygulamaları için bilinmesi gereken E, Y, KIC, C11, B ve D gibi karakteristik mekanik parametreler yüke bağlı Vickers mikrosertlik ölçümleri ile tespit edilmiştir. Ayrıca, tüm örnekler için girinti test yükü miktarının artması ile Vickers mikrosertlik değerlerinin artma eğilimde olduğu ve RISE davranışı gösterdiği gözlemlenmiştir. Dahası, yüke bağımlı Vickers mikrosertlik ölçümlerinden yararlanarak ve Meyer yasası, PSR modeli, MPSR modeli, EPD modeli, Hays-Kendall modeli ve IIC modeli gibi altı farklı teorik model ile hazırladığımız tüm örneklerin yükten bağımsız mikrosertlik değerleri hesaplandı. Teorik modeller yarımıyla hesaplanan yükten bağımsız mikrosertlik ölçümleri yüke bağımlı mikrosertlik ölçümleriyle karşılaştırıldı. Sonuç olarak, üretimini gerçekleştirdiğimiz tüm örnekler için IIC modelinin numunelerin yükten bağımsız mikrosertlik değerlerinin belirlenmesinde en başarılı ve uygun teorik yaklaşım olduğu görülmüştür.
Özet (Çeviri)
The structural and mechanical characteristics of the new superconducting substructures obtained by doping the Bi-2212 superconducting inorganic crystal system with SiO2 at varying ratios of 0.00, 0.01, 0.03, 0.05 were investigated in detail by X-Ray Diffraction (XRD) and Vickers microhardness analyses, respectively. As a result of the X-ray analysis of all the samples prepared within the scope of the thesis, it was observed that the Bi-2212 superconducting phase was more dominant than the other phases, and the lattice parameters calculated for all samples were also found to be in agreement with the lattice parameters of the Bi-2212 framework. Characteristic mechanical parameters such as E, Y, KIC, C11, B and D, which should be known for industrial and technological applications of the prepared samples, were determined by load-dependent Vickers microhardness measurements. In addition, it was observed that Vickers microhardness values tended to increase with the increase in the amount of indentation test load for all samples and showed RISE behaviour. Furthermore, using the load-dependent Vickers microhardness measurements and six different theoretical models such as Meyer's law, PSR model, MPSR model, EPD model, Hays-Kendall model and IIC model, the load-independent microhardness values of all prepared samples were calculated. Load-independent microhardness measurements calculated with half of the theoretical models were compared with load-dependent microhardness measurements. As a result, the IIC model was found to be the most successful and appropriate theoretical approach for determining the load-independent microhardness values of the samples for all the samples produced.
Benzer Tezler
- Kobalt-difüzyonunun, konvansiyonel katı hal reaksiyonu tekniği ile üretilen Bi-2212 süperiletken seramiklerin mekanik, süperiletken ve yapısal özellikleri üzerine etkisi
Effect of cobalt-diffusion on mechanical, superconducting and structural properties of Bi-2212 superconducting ceramics produced by conventional solid-state reaction technique
İLKER ÖZ
Yüksek Lisans
Türkçe
2019
Makine MühendisliğiBolu Abant İzzet Baysal ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. GÜRCAN YILDIRIM
PROF. DR. CABİR TERZİOĞLU
- Investigation of structural, superconducting and magnetic properties of bi1.6-xlaxpb0.5sr2.0-yeuyca1.1cu2.1o8+& ceramics by experimental and theoretical approaches
Bi1.6-xlaxpb0.5sr2.0-yeuyca1.1cu2.1o8+& seramiklerinin yapısal, süperiletkenlik ve manyetik özelliklerinin deneysel ve teorik yaklaşımlarla incelenmesi
YUSUF ZALAOĞLU
Doktora
İngilizce
2015
Fizik ve Fizik MühendisliğiAbant İzzet Baysal ÜniversitesiFizik Bölümü
PROF. DR. OSMAN GÖRÜR
PROF. DR. CABİR TERZİOĞLU
- Bi-2212 süperiletken ana yapısına farklı oranlarda TiB2 katkılanmasıyla oluşan yeni sistemlerin yapısal ve mekanik özelliklerinin incelenmesi
Investigation of structural and mechanical properties of new systems obtained by TiB2 addition at different rates to Bi-2212 superconducting matrix
EMRAH ATILGAN
Yüksek Lisans
Türkçe
2023
Fizik ve Fizik MühendisliğiOsmaniye Korkut Ata ÜniversitesiFizik Ana Bilim Dalı
DOÇ. DR. YUSUF ZALAOĞLU
- Süper iletken BSCCO whiskerlerin büyüme mekanizması ve farklı katkılamalara bağlı olarak elektriksel ve manyetik özellikleri
Growth mechanism of superconductor BSCCO whiskers and their electrical and magnetic properties depending on different doping elements
SERDAR ALTIN
Doktora
Türkçe
2009
Fizik ve Fizik Mühendisliğiİnönü ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. M. EYYUPHAN YAKINCI
- Gd2O3 katkılanmış Bi-2223 süperiletken seramiklerin yapısal karakterlerinin saptanması
Determination of the characteristics of Bi-2223 superconductor ceramics with Gd2O3 additions
YELDA KADIOĞLU
Yüksek Lisans
Türkçe
2010
Fizik ve Fizik MühendisliğiDokuz Eylül ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. KEMAL KOCABAŞ