3B materyallerin ve posterior kompozit rezinin yüzey pürüzlülüğü, mikrosertlik ve renklenme özelliklerinin incelenmesi
Investigation of surface roughness, micro-hardness and color properties of 3D materials and posterior composite resin
- Tez No: 891527
- Danışmanlar: DR. ÖĞR. ÜYESİ BİLGE ERSÖZ
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: 3B yazıcı, Eklemeli üretim, Kompozit rezin, Renklenme, Yüzey pürüzlülüğü, Yüzey sertliği, Üç boyutlu yazıcı, 3D printing, Additive manufacturing, Composite resin, Discoloration, Surface roughness, Surface hardness, Three dimensional printer
- Yıl: 2024
- Dil: Türkçe
- Üniversite: Sağlık Bilimleri Üniversitesi
- Enstitü: Gülhane Diş Hekimliği Fakültesi (ankara)
- Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Restoratif Diş Tedavisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu çalışmanın amacı, iki farklı 3B baskılı rezin materyalin (Formlabs Permanent Crown, Asiga Crowntec) ve geleneksel kompozit rezin materyalin (FiltekZ250) yüzey pürüzlülüğü, renk stabilitesi ve mikrosertlik özelliklerini değerlendirmektir. Materyallerin performansları, farklı çözeltilere maruz bırakılarak incelenmiştir. Materyal ve Metot: Çalışmada, iki farklı 3B baskılı rezin (Formlabs Permanent Crown, Asiga Crowntec) ve 1 adet geleneksel mikrohibrit kompozit rezin (FiltekZ250) kullanılarak 10 mm çap ve 2 mm kalınlıkta toplam 120 adet numune hazırlandı. Bu materyaller, distile su, kahve, çay ve kola gibi farklı solüsyonlarda bekletilerek başlangıçta, 7. günde ve 30. günde ölçümler yapılmıştır. Yüzey pürüzlülüğü ölçümleri optik profilometre (Zeiss Smartproof 5) ile, renk değişimleri spektrofotometre (VITA Easyshade V) ile, ve mikrosertlik değerleri Vickers mikrosertlik ölçme cihazı (Shimadzu HMV-G) ile belirlenmiştir. Bulgular: Numunelerin solüsyonlara maruz kalmaları sonucu, yüzey pürüzlülüğü açısından en düşük değeri FiltekZ250 geleneksel kompozit gösterirken, en yüksek yüzey pürüzlülüğünü ise Formlabs 3B materyal grubu göstermiştir. Renk stabilitesi testlerinde, Formlabs ve Asiga 3B materyal grupları daha iyi performans sergilerken, FiltekZ250 kompozit materyal grubu en yüksek ΔE değerlerine sahip olmuştur (p<0,05). Mikrosertlik açısından, FiltekZ250 kompozit materyal grubu en yüksek değerleri gösterirken (p<0,01), Formlabs ve Asiga 3B materyal grupları daha düşük mikrosertlik değerleri göstermiştir. Varyans analizi için iki yönlü ANOVA kullanılmıştır. Sonuç: Bu çalışmadan elde edilen veriler doğrultusunda klinikte sıklıkla kullanılan geleneksel kompozitlere kıyasla 3B materyaller daha iyi renk stabilitesi göstermiştir. Ancak mikrosertlik ve yüzey pürüzlülüğü açısından geleneksel kompozitler üstünlüğünü korumaktadır. 3B materyallerin daha yaygın klinik kullanımları için mikrosertlik özelliklerinin gelişmesi gerekmektedir.
Özet (Çeviri)
Objective: The aim of this study is to evaluate the surface roughness, color stability, and microhardness properties of two different 3D-printed resin materials (Formlabs Permanent Crown, Asiga Crowntec) compared to a conventional composite resin material (FiltekZ250). The performance of these materials was assessed after exposure to various solutions. Materials and Methods: A total of 120 samples were prepared using two different 3D-printed resins (Formlabs Permanent Crown, Asiga Crowntec) and one conventional microhybrid composite resin (FiltekZ250), with dimensions of 10 mm in diameter and 2 mm in thickness. These materials were immersed in different solutions, including distilled water, coffee, tea, and cola, and measurements were taken initially, on day 7, and on day 30. Surface roughness was measured using an optical profilometer (Zeiss Smartproof 5), color changes were assessed with a spectrophotometer (VITA Easyshade V), and microhardness was determined using a Vickers microhardness tester (Shimadzu HMV-G). Results: After exposure to the solutions, the conventional composite FiltekZ250 exhibited the lowest surface roughness, while the highest surface roughness was observed in the Formlabs 3D material group. In color stability tests, the Formlabs and Asiga 3D material groups demonstrated better performance, whereas the FiltekZ250 composite group had the highest ΔE values (p<0.05). Regarding microhardness, the FiltekZ250 composite group showed the highest values (p<0.01), while the Formlabs and Asiga 3D material groups had lower microhardness values. Conclusion: The findings from this study suggest that, compared to conventional composites, 3D-printed materials show better color stability. However, conventional composites continue to excel in microhardness and surface roughness. For 3D materials to be more widely used in clinical practice, their microhardness properties need improvement.
Benzer Tezler
- 3 boyutlu yazıcı sistemleri ile üretilen kompozit restorasyonların klinik performanslarının direkt kompozit restorasyonlarla karşılaştırılması
Clinical performance assessment: Composite restorations produced by 3d printing systems and direct composite restorations
HATİCE KARAGÖZOĞLU
Diş Hekimliği Uzmanlık
Türkçe
2026
Diş HekimliğiSivas Cumhuriyet ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
PROF. DR. DİĞDEM EREN
- Çeşitli rezin kompozit materyallerin fiziksel özelliklerinin in vivo ve in vitro olarak karşılaştırılması
Comparison of physical properties of different resin composite materials, in vivo and in vitro
ALİ RIZA ÇETİN
Doktora
Türkçe
2009
Diş HekimliğiSelçuk ÜniversitesiDiş Hastalıkları ve Tedavisi Ana Bilim Dalı
PROF. DR. NİMET ÜNLÜ
- Üç farklı teknikle üretilen posterior adeziv restorasyonların mekanik özelliklerinin İn-vitro incelenmesi
In-vitro evaluation of the mechanical properties of posterior adhesive restorations fabricated using three different techniques
GÖZDE ACAR
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiEge ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. CEM PEŞKERSOY
- Fiberle güçlendirilmiş kompozit rezinlerin renk ve opasitesinin geleneksel kompozit rezinlerle karşılaştırılması
Comparison of color and opacity of fiber-reinforced composite resins with traditional composite resins
MURAT FURKAN KOCAOĞLU
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş Hekimliğiİzmir Katip Çelebi ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
PROF. DR. ESRA UZER ÇELİK
- Derin marjin elevasyonu uygulanan dişlerde farklı pulpal build-up materyalleri kullanılarak üretilen 3B baskı endokronların kırılma dayanımı
Fracture resistance of 3D-printed endocrowns fabricated using different pulpal build-up materials in teeth restored with deep margin elevation
SENA OKUT
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiSelçuk ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
PROF. DR. NEVİN ÇOBANOĞLU