Resiprokasyon hareketi ile çalışan orijinal, replika benzeri ve sahte nikel titanyum eğelerin döngüsel yorgunluk dirençlerinin karşılaştırılması: in vitro çalışma
Comparison of the cyclic fatigue resistance of original, replica-like and counterfeit nickel-ti̇tanium files operating in reciprocating motion: N vitro study
- Tez No: 907798
- Danışmanlar: DOÇ. DR. ELİF BAHAR ÇAKICI
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2024
- Dil: Türkçe
- Üniversite: Ordu Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Endodonti Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 154
Özet
Amaç: Bu çalışmanın amacı resiprokasyon hareketi ile çalışan orijinal, replika benzeri ve sahte nikel titanyum eğelerin tasarım özelliklerinin, vücut sıcaklığında döngüsel yorgunluğa karşı dirençlerinin ve metalurjik özelliklerinin karşılaştırılmasıdır. Gereç ve Yöntem: Orijinal (Reciproc Blue R25), replika benzeri (Recip-One Files Blue R25) ve sahte (Reciproc Blue R25) eğe sistemlerinin yer aldığı 4 grup için toplamda 100 adet nikel titanyum eğe çalışma kapsamında kullanıldı. Eğelerin tasarım özelliklerini değerlendirmek için: stereomikroskop ile üretim hataları karşılaştırıldı; taramalı elektron mikroskobundan (SEM) alınan verilerle uç tasarımı incelendi, taper ve uç çap değerleri Image J programıyla ölçülerek karşılaştırıldı; dijital kumpas ile de 18-20 mm ölçüm çizgilerinin hassasiyetleri incelendi. Döngüsel yorgunluk testi vücut sıcaklığında (37°C), 60° kurvatür eğimi ve 5 mm kurvatür yarıçapı değerlerinde oluşturulan yapay kanalda gerçekleştirildi. Örneklerin metalurjik özellikleri diferansiyel taramalı kalorimetre (DSC) ve enerji dağılım spektrometresi (SEM-EDS) aracılığıyla incelendi. Verilerin normalliği Shapiro-Wilk testi ile değerlendirildi. Normal dağılan veriler için one-way ANOVA, normal dağılım göstermeyen veriler için Kruskal-Wallis testi yapıldı. Post hoc testi olarak Games-Howell ve Bonferroni testi kullanıldı. Anlamlılık seviyesi %5 olarak belirlendi. Bulgular: Sahte eğe sistemleri (Cf1, Cf2) diğer gruplardan stereomikroskop altında üretim hataları izlenmesiyle ayırt edilebilmiştir. Orijinal eğe sistemi (Of) ve replika benzeri eğe sistemi (Rf) pasif uç tasarımı sergilerken, sahte eğe sistemleri SEM altında aktif uç tasarımı sergilemiştir. Rf grubu eğeleri Of grubuna benzer uç çapı ve taper değerleri gösterirken, Cf1 grubu eğeler Of grubuna kıyasla düşük taper ve uç çap değerleri göstermiştir. Sahte eğe sistemleri diğer gruplara kıyasla 0.1 mm' den yüksek ölçüm çizgilerinden sapma göstermiştir. Döngüsel yorgunluk test sonuçlarına göre kırılma süreleri gruplar arasında benzerlik göstermiştir. DSC sonuçları vücut sıcaklığında Of grubu eğelerin östenit fazda yer aldığını gösterirken, diğer grup eğeler ise martensit fazda yer almıştır. SEM-EDS sonuçlarına göre gruplar arasında nikel- titanyum oranları benzerlik göstermiştir. Sonuçlar: Orijinal, replika benzeri ve sahte eğe sistemlerinin karşılaştırıldığı bu çalışmada döngüsel yorgunluğa karşı direnç ve nikel-titanyum seviyelerinde gruplar arasında benzerlik gözlenirken, tasarım özellikleri ve DSC sonuçları farklılık göstermektedir. Sahte eğe sistemleri iddia edilen taper ve uç çap değerlerini karşılamamış, incelenen verilerde bu sistemlerin standart sapma değerleri diğer gruplara kıyasla yüksek seyretmiştir. Standardizasyonu olmayan bu sistemlerin, orijinal sistemlere göre güvenilir olmadığı kabul edilebilir.
Özet (Çeviri)
Aim: The aim of this study is to compare the design features, cyclic fatigue resistance at body temperature, and metallurgical properties of original, replica-like, and counterfeit nickel-titanium files operating in reciprocating motion. Materials and Methods: A total of 100 nickel-titanium files, comprising four groups of original (Reciproc Blue R25), replica-like (Recip-One Files Blue R25), and counterfeit (Reciproc Blue R25) systems, were used in this study. To evaluate the design features of the files, manufacturing defects were compared using a stereomicroscope; tip designs were examined through data obtained from scanning electron microscopy (SEM), and taper and tip diameter values were measured and compared using the ImageJ software. The accuracy of the 18-20 mm measurement lines was assessed using a digital caliper. The cyclic fatigue test was conducted at body temperature (37°C) in an artificial canal with a 60° curvature angle and a 5 mm curvature radius. The metallurgical properties of the samples were analyzed via differential scanning calorimetry (DSC) and energy-dispersive X-ray spectroscopy (SEM-EDS). The normality of the data was assessed using the Shapiro-Wilk test. For normally distributed data, a one-way ANOVA was performed, and for non-normally distributed data, the Kruskal-Wallis test was used. Post hoc analysis was conducted using the Games-Howell and Bonferroni tests. The significance level was set at 5%. Results: The counterfeit file systems (Cf1, Cf2) were distinguishable from the other groups through the observation of manufacturing defects under a stereomicroscope. While the original file system (Of) and the replica-like file system (Rf) exhibited passive tip designs, the counterfeit file systems showed active tip designs under SEM analysis. The Rf group files demonstrated similar tip diameter and taper values to the Of group, whereas the Cf1 group files displayed lower taper and tip diameter values compared to the Of group. The counterfeit file systems exhibited deviations of over 0.1 mm from the measurement lines compared to the other groups. The cyclic fatigue test results indicated that the fracture times were similar across the groups. DSC results revealed that the Of group files were in the austenite phase at body temperature, while the other group files remained in the martensitic phase. According to SEM-EDS analysis, the nickel-titanium ratios were similar across all groups. Conclusion: In this study, which compared original, replica-like, and counterfeit file systems, similarities were observed in cyclic fatigue resistance and nickel-titanium levels among the groups, while differences were noted in design features and DSC results. The counterfeit file systems did not meet the claimed taper and tip diameter values, and the data examined showed that the standard deviation values of these systems were higher compared to the other groups. It can be concluded that these non-standardized systems are not as reliable as the original systems.
Benzer Tezler
- Rotasyon ve resiprokasyon hareketiyle çalışan tek eğe sistemlerinin kök kanallarının şekillendirilmesi ve yenilenmesinde çoklu kullanımlarının döngüsel yorgunluk dayanımına etkisinin incelenmesi
The examination of the effect of multiuse of single file systems working with rotation and reciprocation systems during shaping and retreatment procedure of the root canals on the cyclic fatigue resistance
SEVGİ ERKAN
Diş Hekimliği Uzmanlık
Türkçe
2021
Diş HekimliğiSüleyman Demirel ÜniversitesiEndodonti Ana Bilim Dalı
PROF. DR. AYŞE DİLJİN KEÇECİ
- Rotasyonel ve resiprokasyon hareketi ile çalışan üç farklı niti eğe sistemi ile yapılan kanal tedavisi yenileme işleminin apikalden taşan debris miktarına etkisinin değerlendirilmesi
Resiprokasyon and rotational movement of working with three different niti root canal treatment system made with the aegean of the refresh operation from the amount of debris overflowing from the evaluation of the effect of apikal
ASİYE NUR DİNÇER
Doktora
Türkçe
2014
Diş HekimliğiErciyes ÜniversitesiDiş Hastalıkları ve Tedavisi Ana Bilim Dalı
DOÇ. ÖZGÜR ER
- Tam tur dönen ve resiprokasyon hareketi ile çalışan nikel titanyum döner eğelerin döngüsel yorgunluğuna kullanıcı tecrübesinin etkisinin araştırılması
Comparison of the effect of operator experience on cyclic fatigue resistance of reciprocating and rotating nickel-titanium rotary file systems
HANDE ÖZYÜREK
Diş Hekimliği Uzmanlık
Türkçe
2021
Diş HekimliğiKocaeli ÜniversitesiPedodonti Ana Bilim Dalı
DOÇ. DR. MESUT ELBAY
- Farklı Nİ-Tİ eğe sistemlerinin apikalden taşan debris miktarı üzerine etkileri
The effects of different Nİ-Tİ file systems on the amount of apical debris extrusion
FUNDA DENİZ ARIKAN
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiGazi ÜniversitesiEndodonti Ana Bilim Dalı
PROF. DR. ÖZGÜR TOPUZ
- Farklı endomotor eğelerinin farklı çalışma boylarında kullanılmasının foraminal deformasyona etkisi: Taramalı elektron mikroskobu çalışması
The effect of using different endomotor files in different working lengths at foraminal deformation: A scanning electron microscope study
FATMA NUREFŞAN GÜRSOY
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiBezm-i Alem Vakıf ÜniversitesiEndodonti Ana Bilim Dalı
DOÇ. DR. MEHMET BURAK GÜNEŞER