Kompozit rezinlere uygulanan farklı modeling likitlerin kompozitlerin mikrosertlik, renk değişimi ve bükülme dayanım değerleri üzerine etkilerinin incelenmesi
Investigation of the effects of different modeling liquids applied to composite resins on the microhardness, color change and flexural strength values of composites
- Tez No: 932817
- Danışmanlar: PROF. DR. NESLİHAN TEKÇE
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: ModelKng LKquKd, ComposKte ResKn, MKcrohardness, Color Change, Flexural Strengt
- Yıl: 2025
- Dil: Türkçe
- Üniversite: Kocaeli Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Kompozit rezinlerle birlikte kullanılan 5 farklı modeling likitin, kompozitlerin mikrosertlik, renk değişimi ve bükülme dayanım değerleri üzerine etkilerinin değerlendirilmesidir. Yöntem: Bu araştırmada, bir üniversal kompozit rezin olan G-aenial A'CHORD (GC Corp., Tokyo, Japonya) ile modelasyon likiti olarak Modeling Resin (Bisco Inc, ABD), Wetting Resin (Ultradent Products, ABD), Signum Liquid (Heraeus Kulzer, Almanya), Estenia C&B Modeling Liquid ( Kuraray Noritake Inc., Tokyo, Japonya) ve Modeling Liquid (GC Corp., Tokyo, Japonya) kullanılarak, mikrosertlik ve renk değişimi parametreleri için 10x2x2mm ölçülerinde disk şeklinde, bükülme dayanımı parametreleri için 24x2x2mm ölçülerinde dikdörtgen kompozit örnekler hazırlanmıştır (n=12). Hazırlanan numuneler 24 saat distile suda bekletildikten sonra ölçümler gerçekleştirilmiştir. İstatistiksel değerlendirme IBM SPSS 29.0 (IBM Corp., Armonk, NY, USA) ile yapılmıştır. Gruplar arası karşılaştırmalar Kruskal-Wallis testi ile yapıldı. Çoklu karşılaştırmalarda Dunn testi kullanılmıştır. Hipotez testlerinde p<0,05 istatistiksel önemlilik için yeterli kabul edilmiştir. Bulgular: Yapılan değerlendirme sonucunda renk değişim ölçümlerinde gruplar arasında istatistiksel olarak anlamlı bir fark saptanmamıştır (p>0,05). Mikrosertlik ölçümlerinde gruplar arasında en yüksek ortanca değerleri kontrol grubunda görülmüştür. Kontrol grubu ile Modeling Resin, Signum Liquid, Modeling Liquid ve Estenia C&B Modeling Liquid arasında istatistiksel olarak anlamlı farklılık tespit edilmiştir (p<0,05). Diğer gruplar arasında ise ikili karşılaştırmada istatistiksel olarak anlamlı bir farklılık gözlenmemiştir. Bükülme dayanımı sonuçlarında Estenia C&B Modeling Liquid, Modeling Resin, Signum Liquid ve Modeling Liquid 'e göre istatistiksel açıdan anlamlı bulunmuştur (p<0,05). Sonuç: Farklı modeling likitlerin, renk değişimi değerleri arasında bir farklılık yoktur. Ancak kompozitlerin mikrosertlik değerleri likit kullanımıyla negatif etkilendiği için uzun dönemde restorasyonlarda klinik başarısızlıklara neden olabilir. Anahtar KelJmeler: ModelKng LKkKt, KompozKt RezKn, MKkrosertlKk, Renk DeğKşKmK, Bükülme Dayanımı
Özet (Çeviri)
Purpose: To evaluate the effects of 5 different modeling liquids used with composite resins on the microhardness, color change and flexural strength values of the composites. Method: In this study, 10x2x2mm disc shaped composite specimens were prepared for microhardness and color change parameters and 24x2x2mm rectangular composite specimens were prepared for flexural strength parameters using G-aenial A'CHORD (GC Corp., Tokyo, Japan), a universal composite resin, and Modeling Resin (Bisco Inc, USA), Wetting Resin (Ultradent Products, USA), Signum Liquid (Heraeus Kulzer, Germany), Estenia C&B Modeling Liquid (Kuraray Noritake Inc., Tokyo, Japan) and Modeling Liquid (GC Corp., Tokyo, Japan) as modeling liquids (n=12). The prepared samples were kept in distilled water for 24 hours and then the measurements were performed. Statistical evaluation was performed using IBM SPSS 29.0 (IBM Corp., Armonk, NY, USA). Comparisons between groups were made using the Kruskal-Wallis test. Dunn's test was used for multiple comparisons. In hypothesis tests, p<0.05 was considered sufficient for statistical significance. Results: As a result of the evaluation, no statistically significant difference was found between the groups in color change measurements (p>0.05). In microhardness measurements, the highest median values between the groups were seen in the control group. A statistically significant difference was found between the control group and Modeling Resin (Bisco), Signum Liquid (Kulzer), Modeling Liquid and Estenia C&B Modeling Liquid (Kuraray Noritake) (p<0.05). No statistically significant difference was observed between the other groups in the pairwise comparison. In the flexural strength results, Estenia C&B Modeling Liquid was found to be statistically significant compared to Modeling Resin, Signum Liquid and Modeling Liquid (p<0.05). Conclusion: There is no difference between the color change values of different modeling liquids. However, since the microhardness values of composites are negatively affected by the use of liquids, it may cause clinical failures in restorations in the long term.
Benzer Tezler
- Modelasyon likitlerinin kompozit rezinlerden monomer salınımlarına etkileri
Effects of modelling liquids on monomer release from composite resins
DORUKCAN YILDIRIM
Diş Hekimliği Uzmanlık
Türkçe
2024
Diş HekimliğiTokat Gaziosmanpaşa ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. EMİNE ŞİRİN KARAARSLAN
DOÇ. DR. HÜSEYİN HATIRLI
- Viscoelastic effects on structure and dynamics of liposomes in polymeric matrices
Polimerik matrislerde lipozomların yapısı ve dinamikleri üzerindeki viskoelastik etkiler
SELCAN KARAZ
Yüksek Lisans
İngilizce
2023
Kimya MühendisliğiKoç ÜniversitesiKimya ve Biyoloji Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ERKAN ŞENSES
PROF. DR. SEDA KIZILEL
- ODTÜ Beden Eğitimi ve Spor bölümü 1985-1986 programının öğrencilerin fizyolojik kapasitelerine etkisi
Başlık çevirisi yok
ALİ AHMET DOĞAN
Yüksek Lisans
Türkçe
1986
Eğitim ve ÖğretimGazi ÜniversitesiBeden Eğitimi ve Spor Ana Bilim Dalı
DOÇ. DR. EYYUP GÜNAY İSBİR
- Bornova koşullarında 23 melez mısır çeşidinde adaptasyon ve verimlilik araştırması
Başlık çevirisi yok
FERDAN ÇİFTÇİ
- Komposit volanların optimum tasarımı
Başlık çevirisi yok
İSMAİL ÇAĞLIÖZ
Yüksek Lisans
Türkçe
1987
Makine MühendisliğiErciyes ÜniversitesiMakine Ana Bilim Dalı
YRD. DOÇ. DR. İBRAHİM UZMAY