Etanolün ve oksidasyon ürünlerinin demirli malzeme üzerindeki etkilerinin araştırılması

Investigation the effects of ethanol and it's oxidation products on iron base material

  1. Tez No: 97529
  2. Yazar: EMEL SAYGIN
  3. Danışmanlar: PROF.DR. KADRİYE KAYAKIRILMAZ, PROF.DR. MEHMET ERBİL
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya, Chemistry
  6. Anahtar Kelimeler: Elektrooksidasyon, Korozyon, Polarizasyon Direnci, inhibitor, Electrooxidation, Corrosion, Polarisation Resistance, Inhibitor
  7. Yıl: 2000
  8. Dil: Türkçe
  9. Üniversite: Niğde Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 105

Özet

m ÖZET ETANOLUN ve OKSİDAS YON ÜRÜNLERİNİN DEMİRLİ MALZEME ÜZERİNDEKİ ETKİLERİNİN ARAŞTIRILMASI SAYGIN Emel Niğde Üniversitesi Fen Bilimleri Enstitüsü Kimya Ana Bilim Dalı Danışman : Prof. Dr. Kadriye KAYAKIRILMAZ Ortak Danışman : Prof. Dr. Mehmet ERBİL Ağustos 2000 105 Sayfa Etanolun ve oksidasyon ürünlerinin inhibisyon etkinliğini saptamak amacıyla yapılan bu çalışmada, farklı elektroliz hücrelerinde kimyasal bileşimi bilinen demir anot, platin katot kullanılarak 0,1 M Na2S04 çözeltisinde, 0,1 M Na2S04 + 0,1 M etanol çözeltisinde ve alkolün oksidasyon ürünlerini içeren 0,1 M Na2S04 çözeltisinde akım - potansiyel eğrisinden polarizasyon dirençleri hesaplanmış, uygulanan farklı potansiyellerde akım-zaman değişimleri incelenmiş ve demirli malzemenin kütle kaybı saptanmıştır. Etanolun oksidasyon ürünlerini elde etmek için anot ve katotta platin elektrotlar kullanılarak oluşturulan elektroliz devresinde, 0,1 M Na2S04 + 0,1 M etanol çözeltileri ferklı potansiyellerde (0,669 V, 0,859 V ve 0,979 V) farklı sürelerde (10, 20 ve 30 dakika) potansiyel uygulanmıştır. Aynı deneyler asetaldehit ve asetik asitle hazırlanan elektrolit çözeltiler kullanılarak da yapılmıştır. Bu deneylerden elde edilen sonuçlara göre, etanol ve oksidasyon ürünlerinin bulunduğu çözeltilerde kütle kaybı, 0,1 M Na2S04 çözeltisindeki kütle kaybından daha az olmuştur. Oksidasyona uğratılmış alkollü çözeltilerde elde edilen sonuçlara göre inhibisyon etkinliği konusunda belirli bir düzenlilik saptanamamıştır. 0,1 M Na2S04IV çözeltisinde Rp“1 değeri 714 uA/V.cm2 iken, etanollü çözeltide bu değer 400 uA/V.cm2 bulunmuştur. Oksidasyona uğratılmış etanol çözeltilerinde elde edilen Rp”1 değerleri, 0,1 M Na2S04 çözeltisinde elde edilen Rp“1 değerinden daha düşük olmuştur. En düşük Rp”1 değeri 0,979 V potansiyelde 20 ve 30 dakika süreyle oksidasyon uygulanmış etanol çözeltilerinde elde edilmiştir. 0,1 M Na2SÛ4 + 0,1 M asetaldehit çözeltilerinde elde edilen Rp“1 değeri 0,1 M Na2SÛ4 + 0,1 M asetik asit çözeltisinde elde edilen Rp”1 değerinden daha düşük bulunmuştur. Elde edilen bulgulara göre, alkolün ve oksidasyon ürünlerinin elektrot yüzeyinde adsorplanarak korozyonu belirli oranda önlediği sonucuna varılmıştır. 0,1 M Na2SÜ4 + 0,1 M etanol çözeltisine oksidasyon uygulama süresi ve potansiyeli inhibisyon etkinliğini olumlu yönde etkilemiştir.

Özet (Çeviri)

SUMMARY INVESTIGATION THE EFFECTS OF ETHANOL AND IT'S OXIDATION PRODUCTS ON IRON BASE MATERIAL SAYGINEmel Niğde University Graduate School of Natural and Applied Sciences Department of Chemistry Supervisor : Prof. Dr. Kadriye KAYAKIRILMAZ Co- Adviser : Prof. Dr. Mehmet ERBİL August 2000 105 pages The aim of this study is to determine the inhibition effect of ethanol and it's oxidation product in 0.1 M NaîSO* solution by calculating the polarisation resistance's from current potential curves and observing current time variation at different potentials. Different electrolysis cells in which iron composition is known and platinum have been used as anode and cathode electrodes respectively, electrolysis was carried out in three different electrolyte solutions; 0. 1 M Na2S04 solution, 0. 1 M NaıSO* containing ethanol solution and a solution prepared with 0.1 M Na2S04 containing oxidation products of ethanol. In order to obtain the oxidation products of ethanol an electrolyse circuit in which the anode and the cathode were made of Pt electrodes were used. The electrolyte solutions were prepared from 0.1 M NaıSOt solution mixed with 0.1 M ethanol and different potentials (0.669 V, 0.859 V and 0.979 V) have been applied for different time intervals (10, 20 and 30 minutes). The same experiments have been repeated using the electrolyte solution prepared from acetaldehyde and acetic acids from these experiments, the weight loss in the solution containing ethanol was smaller than theVI weight loss in the 0.1 M NaıSGj solution. According to the results obtained from the solutions being oxidised with the alcohol, it has not been observed a clear regularity while the Rp“1 value for 0.1 M Na2S04 solution's 714 uA/ V.cm2 this value is 400 uA/ V. cm2 for ethanol solution Rp”1 values obtained from ethanol solutions being oxidised is smaller than the Rp“1 values obtained for 0.1 M Na2SC>4 solution. The smallest Rp”1 value has been obtained for ethanol solution being oxidised by applying 0.979 V potential between the electrodes for 20 minutes. Rp“1 value obtained from 0.1 M Na2S04 solution mixed with 0. 1 M acetaldehyde solution is smaller them the Rp”1 value obtained from 0. 1 M Na2SÜ4 solution mixed with 0. 1 M acetic acid solution. According to the experimental results; alcohol and it's oxidation product being adsorbed at the surface inhibits the corrosion to a certain ratio. Oxidation period and potential of 0.1 M Na2SÜ4 solution mixed with 0. 1 M ethanol, had positive effected on inhibition.

Benzer Tezler

  1. Tez No

    395632

    Alüminyum, demir ve krom ile aktive edilmiş MCM-41 ve SBA-15 katalizörlerinin geliştirilmesi ve etanolün seçici oksidasyon ve dehidrasyon reaksiyonlarında test edilmesi

    Development of aluminum, iron and chromium activated mcm-41 and sba-15 catalysts and testing of ethanol oxidation and dehydration reactions

    ARZU DİNLER

    Doktora

    Türkçe

    Türkçe

    2015

    Kimya MühendisliğiGazi Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. FATMA SUNA BALCI

    PROF. DR. TİMUR DOĞU

  2. Tez No

    689108

    Alkali doğrudan etanol yakıt hücresi için değerli metal içermeyen anot katalizörü geliştirilmesi

    Development of noble metal free anode catalyst for alkaline direct ethanol fuel cell

    CANAN ARSLAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2021

    Kimya MühendisliğiGebze Teknik Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. MAHMUT RAHİM BAYRAMOĞLU

  3. Tez No

    546331

    Removal of odor emissions from food fermentation and petrochemical production processes with using biological treatment methods

    Gıda fermentasyon ve petrokimya üretim sektörleri kaynaklı koku emisyonlarının biyolojik arıtma yöntemleri ile giderilmesi

    İLKER AKMIRZA

    Doktora

    İngilizce

    İngilizce

    2019

    Çevre Mühendisliğiİstanbul Teknik Üniversitesi

    Çevre Mühendisliği Ana Bilim Dalı

    PROF. DR. KADİR ALP

  4. Tez No

    421039

    Effects of pre-treatments on quality characteristics and oil yields of sesame seeds

    Susam tohumuna uygulanan ön işlemlerin kalite özellikleri ve yağ verimine etkisi

    GÜLŞAH KARATAŞ

    Yüksek Lisans

    İngilizce

    İngilizce

    2015

    Gıda Mühendisliğiİstanbul Teknik Üniversitesi

    Gıda Mühendisliği Ana Bilim Dalı

    DOÇ. DR. NEŞE ŞAHİN YEŞİLÇUBUK

    YRD. DOÇ. DR. HALİL MECİT ÖZTOP

  5. Tez No

    324024

    Yağlı tohumlara uygulanan ultrasonik destekli ön işlem ile soğuk pres yağlarında verim ve kalitenin arttırılması

    Improving the yield and quality of cold pressed oils by ultrasound assisted pretreatment of oilseeds

    EMİNE BUKET ŞERAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2011

    Kimya Mühendisliğiİstanbul Teknik Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. ZEYNEP SELMA TÜRKAY

Geri Dön