Omurga çökme kırıklarında kifoplasti uygulaması için kemik tozu takviyeli kafes yapıların tasarımı
Design of bone powder enhanced cage structures for kyphoplasty in vertebral compression fractures
- Tez No: 981742
- Danışmanlar: PROF. DR. ŞEHİME GÜLSÜN TEMEL
- Tez Türü: Yüksek Lisans
- Konular: Biyomühendislik, Bioengineering
- Anahtar Kelimeler: Cerrahi meş, Kemik çimentoları, Spinal kırıklar, Surgical mesh, Bone cements, Spinal fractures
- Yıl: 2025
- Dil: Türkçe
- Üniversite: Bursa Uludağ Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Biyomalzemeler Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Osteoporoz veya travmaya bağlı omurga çökme kırıkları, omurganın yapısal bütünlüğünü bozarak cerrahi müdahale gerektirebilir. Kifoplasti, kırık omurun yüksekliğini balon yerleştirme ve kemik çimentosu enjeksiyonu ile geri kazandırmayı amaçlayan minimal invaziv bir tedavidir. Bu çalışmanın odağı, polimetilmetakrilat (PMMA) esaslı kemik çimentolarında sızdırmazlık ve mekanik destek sunan biyouyumlu yüzeyler geliştirmektir. Bu doğrultuda, biyobozunur polibütilen süksinat (PBS) kullanılarak elektroçekim yöntemiyle nanolif kafes yapılar üretilmiş ve selülozik kupro tekstil yüzeyleri kullanılmıştır. Elektroçekim için %10 PBS çözeltisi kloroform-dimetilformamid karışımında hazırlanmış, %3 kemik tozu eklenmiştir. İşlem 1.0 mL/saat besleme hızı, 12 cm uç-toplayıcı plaka mesafesi ve 20 kV gerilim altında gerçekleştirilmiştir. Elde edilen nanolifli yüzeyler taramalı elektron mikroskobu (SEM) ile incelenmiş ve lifler üzerinde belirgin“boncuklanma”(beading) gözlemlenmiştir. Bu boncuklu morfolojiye rağmen, lif oluşumunun genel olarak homojen olduğu belirlenmiştir. Bu yapıların, PMMA çimentosu uygulamalarında sızıntıyı azaltabileceği ve mekanik stabiliteyi destekleyebileceği düşünülmektedir. Ancak boncuklanmanın kemik hücrelerinin tutunması ve çoğalması gibi biyolojik yanıtları nasıl etkileyeceği, detaylı in vitro ve in vivo çalışmalarla aydınlatılmalıdır. Kupro tekstil yüzeyleri, PBS nanolif kafes yapılar ve PMMA kemik tozu içeren yapıların biyouyumluluğu WST-1 deneyi ile değerlendirilmiştir. Her üç malzeme grubu da kifoplasti uygulamalarında umut vaat eden adaylardır. Ancak klinik etkinliğin doğrulanması için boncuklu nanolif morfolojisinin hücresel etkileşimleri de dahil olmak üzere ileri düzey nicel ve in vivo çalışmalara ihtiyaç duyulmaktadır.
Özet (Çeviri)
Osteoporotic or trauma-induced vertebral compression fractures compromise spinal structural integrity, often necessitating surgical intervention. Kyphoplasty, a minimally invasive treatment, aims to restore fractured vertebral body height through balloon placement followed by bone cement injection. This study focuses on developing biocompatible surfaces that provide sealing and mechanical support, particularly for polymethylmethacrylate (PMMA)-based bone cements. In this context, nanofiber scaffold structures were produced using biodegradable polybutylene succinate (PBS) via electrospinning, and additionally tested on cellulosic cupro textile surfaces. For the electrospinning process, a 10% w/v PBS solution was prepared in a chloroform-dimethylformamide mixture, with 3% bone powder added. The process was conducted at a feeding rate of 1.0 mL/hour, a tip-collector plate distance of 12 cm, and a voltage of 20 kV. Morphological examination of the resulting nanofibrous surfaces by scanning electron microscopy (SEM) revealed significant“beading”formation on the fibers. Despite this beaded morphology, the overall fiber formation was determined to be homogeneous. These structures are thought to potentially reduce leakage in PMMA cement applications and support mechanical stability. However, how this beading affects biological responses such as bone cell adhesion and proliferation needs to be elucidated through detailed in vitro and in vivo studies. The biocompatibility of cupro textile surfaces, PBS nanofiber scaffold structures, and PMMA bone powder-containing structures was evaluated using the WST-1 assay. All three material groups are considered promising candidates for kyphoplasty applications. Nevertheless, including the cellular interactions with the beaded nanofiber morphology, further quantitative and in vivo studies are required to clinically validate their efficacy.
Benzer Tezler
- Perkütan vertebral güçlendirme tekniklerinin radyolojik ve klinik olarak etkinliğinin retrospektif analizi
Başlık çevirisi yok
YASİN YETİŞYİĞİT
Tıpta Uzmanlık
Türkçe
2016
NöroşirürjiBaşkent ÜniversitesiBeyin ve Sinir Cerrahisi Ana Bilim Dalı
PROF. DR. MEHMET NUR ALTINÖRS
- Omur çökme kırıklarında gövde güçlendirmesinin kemiğin yeniden şekillenmesine etkisinin retrospektif olarak değerlendirilmesi
Retrospective evaluation of the effect of trunk strengthening on bone remodeling in spinal collapse fractures
ILGAR BINNAT
Tıpta Uzmanlık
Türkçe
2023
NöroşirürjiDokuz Eylül ÜniversitesiBeyin ve Sinir Cerrahisi Ana Bilim Dalı
PROF. DR. REŞAT SERHAT ERBAYRAKTAR
- Torakolomber omurga kırıklarında posterior kısa segment füzyon sonuçları
The results of posterior short segment fusion in thoracolumbar spine fractures
TURGUT DİNÇAL
Tıpta Uzmanlık
Türkçe
2004
Ortopedi ve Travmatolojiİstanbul ÜniversitesiOrtopedi ve Travmatoloji Ana Bilim Dalı
DOÇ. DR. ÖNDER AYDINGÖZ
- Osteoporotik femur proksimal bölge kırıklarında cerrahi tedavi sonrası bifosfonat kullanılmasının kemik yoğunluğuna etkisi
Effect of using post surgery biphosphonate to the density of bone in osteoporotic femur proximal regional fractures
BARIŞ KILINÇ
Tıpta Uzmanlık
Türkçe
2003
Ortopedi ve TravmatolojiGazi ÜniversitesiOrtopedi ve Travmatoloji Ana Bilim Dalı
PROF. DR. ŞAHAP ATİK
- Anstabil torakolumber vertebra kırıkların tedavisinde kısa-segment pedikül fiksasyon uygulamalarının araştırılması
Unstable thoracolumber vertebra fracturesshort-segment pedicle fixation in treatmentresearch of its applications
CİHANGİR ERTÜRK
Tıpta Uzmanlık
Türkçe
2023
NöroşirürjiRecep Tayyip Erdoğan ÜniversitesiBeyin ve Sinir Cerrahisi Ana Bilim Dalı
PROF. DR. AYHAN KANAT