Seramik karo atıkları ve pirinç alaşımı tesisi baca tozu katkılı betonların üretimi ve fotokatalitik özelliklerinin incelenmesi
Production of concrete incorporating ceramic tile waste and brass alloy plant flue dust and investigation of photocatalytic properties
- Tez No: 997563
- Danışmanlar: DOÇ. DR. SAVAŞ ÖZTÜRK
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Baca tozu, Beton, Fotokatalitik, Flue dust, Concrete, Photocatalytic
- Yıl: 2026
- Dil: Türkçe
- Üniversite: Manisa Celal Bayar Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Metalurji ve Malzeme Mühendisliği Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu tez kapsamında, pirinç üretiminde baca filtrasyonu sonucu atık olarak elde edilen baca tozu çinko oksit (ZnO) içerikli atık yer karosu agregalı kendi kendini temizleyen sürdürülebilir betonun mekanik ve fotokatalitik özellikleri incelenmiştir. Çalışma 2 grup numune üzerinden yürütülmüştür. Birinci grup referans olarak TS-EN 196-1 standart kum ve sırasıyla 0-%5-%10-%20 ZnO içerikli dört farklı numunedir. İkinci grup seramik yer karosu agrega içerikli aynı ZnO oranlarına sahip numunelerdir. Agrega olarak kullanılmış olan atık yer karosu, kaba öğütme sonrası ince öğütme yapılmıştır, elek analiz sonucu yüzde oranları; TS-EN 196-1 standart kum yüzdeleri ile aynı oranlarda kullanılmıştır. Her iki numune grubu hazırlanırken TS-EN197-1:2012 CEM IV/B(W-P) 32,5N standart çimento kullanılmıştır. Elde edilmiş numunelerin mekanik dayanımının belirlenmesi için; basınç dayanım testi ve eğme testi uygulanmıştır. Üretilmiş olan numune betonun yoğunluk tayini Arşimet testi ile yapılmıştır. Üretilen betonun morfolojik özellikleri Taramalı Elektron Mikroskobu (SEM) ile belirlenmiştir. Numunelerin fotokatalitik özellikleri; organik bir kirlilik olan metilen mavisinin suda çözündürülmesi ile elde edilmiş çözelti içerisine alınan numunelerin UV-a ve UV-b ortamlarında bekletilmesi sonrası yapılan UV spektrometre ölçümleri ile belirlenmiştir.
Özet (Çeviri)
Within the scope of this thesis, the mechanical and photocatalytic properties of a self-cleaning, sustainable concrete produced using waste floor-tile aggregate and flue dust containing zinc oxide (ZnO)—obtained as a by-product from flue filtration during brass production—were investigated. The study was conducted on two groups of samples. The first group consisted of four samples prepared with TS-EN 196-1 standard sand and containing 0%, 5%, 10%, and 20% ZnO, respectively, serving as reference specimens. The second group comprised samples incorporating ceramic floor-tile aggregates with the same ZnO ratios as the first group. The waste floor tiles used as aggregate were subjected first to coarse grinding and then fine grinding; particle size distribution determined through sieve analysis was adjusted to match the proportions of TS-EN 196-1 standard sand. For both sample groups, TS-EN 197-1:2012 CEM IV/B(W-P) 32.5N standard cement was used in specimen preparation. To determine the mechanical performance of the produced specimens, compressive strength tests and flexural strength tests were performed. The density of the produced concrete specimens was determined using the Archimedes test. The morphological characteristics of the concrete were examined using Scanning Electron Microscopy (SEM). The photocatalytic properties of the samples were evaluated by immersing them in an aqueous solution of methylene blue—an organic pollutant—and subsequently measuring UV spectrometer readings following exposure to UV-A and UV-B environments
Benzer Tezler
- Hayriye (Kayseri) nefelin-siyenit intrüzyonunun petrografik ve jeokimyasal incelenmesi
Petrographical and geochemical investigation of Hayriye (Kasyseri) nepheline-syenite intrusion
H.MUSTAFA ÖZKAN
- CO2-sodyum silikat bağlı kum sistemlerine etki eden parametrelerin incelenip maça ve kalıp özelliklerinin geliştirilmesi
The Investigation of the parameters effecting the mold and core made of CO2-sodium silicate bonded sands for improving the properties
ORHAN ŞERİF KOMAÇ
- Hisersan A.Ş. artıklarından kaolen kazanma olanaklarının araştırılması
Başlık çevirisi yok
SABİHA ÖNÇEK
- Simav-Dağardı feldspatlarının zenginleştirilme olanaklarının araştırılması
Başlık çevirisi yok
EROL OKUR