Tekrarlanan fırınlamanın farklı tip lityum disilikat seramiklerin renk ve mekanik özellikleri üzerindeki etkisi

Effect of repeated firing on color and mechanical properties of different types of lithium disilicate ceramics

  1. Tez No: 1008103
  2. Yazar: GÜLER SAFRAN ÇİÇEK
  3. Danışmanlar: DOÇ. DR. MERYEM GÜLCE SUBAŞI
  4. Tez Türü: Diş Hekimliği Uzmanlık
  5. Konular: Diş Hekimliği, Dentistry
  6. Anahtar Kelimeler: Bükülme Dayanım, Fırınlama, Kontrastlık Oranı, Lityum Disilikat Seramik, Renk Değişim, SEM, Translüsensi, Flexural Strength, Firing, Contrast Ratio, Lithium Disilicate Ceramic, Color Change, SEM, Translucency
  7. Yıl: 2025
  8. Dil: Türkçe
  9. Üniversite: Kütahya Sağlık Bilimleri Üniversitesi
  10. Enstitü: Diş Hekimliği Fakültesi
  11. Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
  12. Bilim Dalı: Protetik Diş Tedavisi Bilim Dalı
  13. Sayfa Sayısı: Belirtilmemiş.

Özet

Amaç: Tekrarlanan fırınlamanın farklı tip lityum disilikat seramiklerin renk ve bükülme dayanımı üzerindeki etkisinin incelenmesidir. Gereç ve Yöntem: Lityum disilikat (LD), nano lityum disilikat (NLD), virgilit içeren lityum disilikat (VLD) seramik (n=45) kesildi (18x4x1,2 mm). Kristalizasyon fırınlaması sonrası 1'er örnek SEM ile incelendi. Örnekler 4 gruba [kontrol (K), fırınlama (F) (1, 2, 3)] (n=11) ayrıldı. Her gruptan 1'er örnek SEM ile incelendi. Başlangıç ve fırınlamalar sonrası renk (ΔE, başlangıç ve fırınlama sonrası TP ve KO, TP fark) ve bükülme dayanım verileri elde edildi (n=10). ΔE, TP fark ve fırınlama sonrası KO değerleri 2 yönlü Robust ANOVA ile, başlangıç TP ve KO değerleri Kruskal-Wallis H testi ile, fırınlama sonrası TP değerleri 2 yönlü ANOVA ile, bükülme dayanım değerleri 2 yönlü Robust ANOVA ve Weibull analizi ile ve gruplar arasındaki ilişki Spearman ve Pearson korelasyon analizi ile incelendi. Bulgular: Kristalizasyon fırınlaması sonrası LD düzgün, NLD ve VLD pürüzlü yüzeye sahipti. Fırınlama sonrası seramiklerde delik gözlendi. ΔE değerleri, seramik, fırınlama ve seramik*fırınlama tipinden (p<0,001), başlangıç TP ve KO, TP fark ve bükülme dayanım verileri seramik tipinden (p≤0,017), fırınlama sonrası TP değerleri seramik ve fırınlama tipinden (p≤0,002) ve fırınlama sonrası KO değerleri seramik ve seramik*fırınlama tipinden etkilendi (p<0,001). Başlangıç ve fırınlama sonrası TP ve CR değerleri arasında, LD-K, VLD-1F, VLD-2F ve VLD-3F'in ΔE ile TP fark değerleri arasında, VLD-3F'in ΔE ile bükülme dayanım değerleri arasında ve NLD-1F'nin TP fark ile bükülme dayanım değerleri arasında negatif anlamlı korelasyon belirlendi. ΔE ve TP fark değerleri için NLD-1F'de pozitif anlamlı korelasyon belirlendi. Sonuç: Klinik uygulamada translüsensi önemli ise NLD ve VLD, bükülme dayanımı önemli ise LD'nin kullanılması önerilebilir. VLD'de tekrarlanan fırınlamalardan kaçınılmalıdır.

Özet (Çeviri)

Aim: To investigate the effect of repeated firing on the color and flexural strength of different types of lithium disilicate ceramics. Material and Method: Lithium disilicate (LD), nano lithium disilicate (NLD), and virgilite containing lithium disilicate (VLD) ceramics (n=45) were cut (18×4×1.2 mm). After crystallization firing, 1 specimen was examined with SEM. Specimens were divided into 4 groups [control (C), firing (F) (1, 2, 3)] (n=11). One specimen from each group was examined with SEM. Before and after firings, color (ΔE, initial and post-firing TP and CR, TP difference) and flexural strength data were obtained (n=10). ΔE, TP difference, and post-firing CR values by 2-way Robust ANOVA, initial TP and CR values by Kruskal-Wallis H test, post-firing TP values by 2-way ANOVA, flexural strength values by 2-way Robust ANOVA and Weibull analysis, and relationship between groups by Spearman and Pearson correlation analyses were analyzed. Results: After crystallization firing, LD had smooth, NLD and VLD had rough surface. After firing, pores were observed in ceramics. ΔE values were affected by ceramic, firing, and ceramic*firing type (p<0.001), initial TP and CR, TP difference, and flexural strength values were affected by ceramic type (p≤0.017), post-firing TP values were affected by ceramic and firing type (p≤0.002), and post-firing CR values were affected by ceramic and ceramic*firing type (p<0.001). Negative significant correlations were determined between initial and post-firing TP and CR values, between ΔE and TP difference values of LD-C, VLD-1F, VLD-2F, and VLD-3F, between ΔE and flexural strength values of VLD-3F, and between TP difference and flexural strength values of NLD-1F. For ΔE and TP difference values, positive significant correlation in NLD-1F was determined. Conclusion: In clinical practice, if translucency is important, NLD and VLD, and if flexural strength is important, LD can be recommended. Repeated firings should be avoided in VLD.

Benzer Tezler

  1. Tez No

    828623

    Tekrarlanan fırınlamanın farklı tip yüksek translusens monolitik zirkonya materyallerinin translusensi ve iki eksenli bükülme dayanımına olan etkisi

    Effect of repeated firing on the translucency and biaxial flexural strength of different types of high translucency monolithic zirconia materials

    SEDA YILDIZLAR

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2023

    Diş HekimliğiSelçuk Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    DOÇ. DR. TUBA YILMAZ SAVAŞ

  2. Tez No

    912038

    Tekrarlanan fırınlama işleminin zirkonya kronların marjinal uyum ve optik özelliklerine etkisinin araştırılması

    Investigation of the effect of repeated firing on the marginal fit and optical properties of zirconia crowns

    AYŞEGÜL ÜÇDAL ASLAN

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2024

    Diş HekimliğiUşak Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    DOÇ. DR. BENGİSU YILDIRIM

  3. Tez No

    303225

    Zirkonyum dioksit alt yapı üzerine uygulanan farklı yüzey işlemlerinin ve tekrarlanan fırınlamanın üst yapı porseleninin bağlanma dayanımına etkisinin in-vitro olarak incelenmesi

    In-vitro evaluation of the effect of different surface treatments and repeated firing on their bond strength to two veneer ceramics to zirconia

    SİNEM SAVRAN ÇAKIR

    Doktora

    Türkçe

    Türkçe

    2011

    Diş Hekimliğiİstanbul Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. BÜLENT ŞERMET

  4. Tez No

    571418

    Farklı yöntemler ve kalınlıklarda hazırlanan implant üstü metal altyapıların kenar ve iç uyumlarına tekrarlanan fırınlamanın etkisi

    Effect of repeated firings on the marginal and internal adaptation of implant supported metal ceramic restorations fabricated with different thicknesses and fabrication method

    ABDURRAHMAN ÖĞÜNÇ

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2019

    Diş Hekimliğiİnönü Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ GÜLER YILDIRIM AVCU

  5. Tez No

    530719

    Monolitik lityum disilikat cam seramik bloklardan, farklı kalınlıkta üretilen indirekt restorasyonların glaze işlemi için farklı sayıda fırınlama sonucunda renk değişikliğinin ve mekanik özelliklerinin değerlendirilmesi

    Evaluating of color changes and mechanical characteristics of different thicknesses of indirect restorations which produced by monolithic lithium disilicate glass ceramic blocks due to different firing times for glaze.

    AGAJAN RAHMANOV

    Doktora

    Türkçe

    Türkçe

    2018

    Diş HekimliğiDicle Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. REMZİ NİĞİZ

Geri Dön