Farklı yüzey bitirme işlemleri uygulanan farklı içerik ve kristalizasyon özelliklerine sahip lityum disilikat seramiklerin renk ve yüzey özelliklerinin incelenmesi

Investigation of color and surface properties of lithium disilicate ceramics with different compositions and crystallization characteristics subjected to different surface finishing treatments

  1. Tez No: 1020675
  2. Yazar: ATALAY ÖMER KAZANCI
  3. Danışmanlar: PROF. DR. MERYEM GÜLCE SUBAŞI
  4. Tez Türü: Diş Hekimliği Uzmanlık
  5. Konular: Diş Hekimliği, Dentistry
  6. Anahtar Kelimeler: Lityum Disilikat Seramik, Renk Değişim, SEM, Translüsensi, Yüzey Bitirme İşlem, Yüzey Pürüzlülük, Color Change, Lithium Disilicate Ceramic, SEM, Surface Finishing Treatment, Surface Roughness, Translucency
  7. Yıl: 2026
  8. Dil: Türkçe
  9. Üniversite: Kütahya Sağlık Bilimleri Üniversitesi
  10. Enstitü: Diş Hekimliği Fakültesi
  11. Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: Belirtilmemiş.

Özet

Amaç: Farklı yüzey bitirme işlemleri uygulanan farklı tip lityum disilikat seramiklerin optik ve yüzey özelliklerinin incelenmesidir. Gereç ve Yöntem: Lityum disilikat (LD), virgilit içeren lityum disilikat (VLD), nano lityum disilikat (NLD) ve fonksiyonel geçişli lityum disilikat (FGLD) seramikler (n=34) kesildi (kalınlık=1,5 mm). LD ve NLD'nin kristalizasyon fırınlaması sonrası 1'er örnek SEM ile incelendi (n=4). Örnekler 3 alt gruba [kontrol (K), cila+polisaj (C+P), glaze (G)] ayrıldı (n=11). Her gruptan 1'er örnek SEM ile incelendi. Kalan örnekler (n=10) termal olarak yaşlandırıldı (10 000 devir). Renk, translüsensi ve pürüzlülük ölçümleri yaşlandırma öncesi ve sonrası gerçekleştirildi. Başlangıç ve yaşlandırma sonrası TP00 ve pürüzlülük, ∆TP00, ΔE00 ve pürüzlülük fark değerleri 2 yönlü Robust ANOVA ile ve gruplar arasındaki ilişki Spearman ve Pearson korelasyon analizi ile incelendi. Bulgular: Kristalizasyon fırınlaması sonrası LD ve NLD, tüm seramiklerin G grupları düzgün yüzeye sahipti. ΔE00, başlangıç ve yaşlandırma sonrası TP00 ve başlangıç pürüzlülük değerleri sırasıyla seramik tipinden, seramik ve seramik*yüzey işlem tipinden, ve seramik*yüzey işlem tipinden etkilendi (p<0,001). ∆TP00, yaşlandırma sonrası pürüzlülük ve pürüzlülük fark değerleri seramik ve yüzey işlem tipinden etkilenmedi. Tüm seramikler klinik olarak kabul edilebilir ΔE00 değerlerine sahipti. NLD'nin ΔE00 değeri algılanabilir iken, diğer seramiklerin ΔE00 değerleri algılanamaz idi. Klinik olarak tüm seramiklerin, LD'nin K, VLD, NLD ve FGLD'nin tüm yüzey işlem gruplarının ∆TP00 değerleri algılanamaz ve kabul edilebilir iken, LD'nin C+P ve G gruplarının ∆TP00 değerleri algılanabilir ve kabul edilebilir idi. Başlangıç ve yaşlandırma sonrası TP00 ve pürüzlülük değerleri arasında negatif anlamlı korelasyon, ΔE00 ve ∆TP00 değerleri arasında pozitif anlamlı korelasyon belirlendi. Sonuç: Klinik uygulamada tüm seramikler ve yüzey bitirme işlemleri (C+P, G) kullanılabilir. Translüsensinin önemli olduğu durumlarda NLD ve FGLD seramikler tercih edilebilir.

Özet (Çeviri)

Objective: To investigate the optical and surface properties of different types of lithium disilicate ceramics subjected to different surface finishing treatments. Material and Method: Lithium disilicate (LD), virgilite containing lithium disilicate (VLD), nano lithium disilicate (NLD), and functionally graded lithium disilicate (FGLD) ceramics (n=34) were cut (thickness=1.5 mm). After crystallization firing of LD and NLD, one specimen was examined with SEM (n=4). Specimens were divided to 3 subgroups [control (C), polishing (C+P), and glaze (G)] (n=11). One specimen from each subgroup was analyzed with SEM. Remaining specimens (n=10) were thermally aged (10 000 cycles). Color, translucency, and roughness measurements were performed before and after aging. Initial and post-aging TP00 and roughness, ∆TP00, ΔE00, and roughness change values by 2-way Robust ANOVA, and relationship between groups by Spearman and Pearson correlation analyses were analysed. Results: After crystallization firing, LD and NLD, G groups of all ceramics had smooth surface. ΔE00, initial and post-aging TP00, and initial roughness values were affected by ceramic type, ceramic and ceramic*surface treatment type, and ceramic*surface treatment type, respectively (p<0.001). ∆TP00, post-aging roughness and roughness change values were not affected by ceramic and surface treatment type. All ceramics had clinically acceptable ΔE00 values. ΔE00 value of NLD was perceptible, whereas ΔE00 values other ceramics were imperceptible. Clinically ∆TP00 values of all ceramics, K group of LD, all surface treatment groups of VLD, NLD, and FGLD were imperceptible and acceptable, whereas ∆TP00 values of C+P and G groups of LD were perceptible and acceptable. Negative significant correlations were determined between initial and post-aging TP00 and roughness values, positive significant correlation was determined between ΔE00 and ∆TP00 values. Conclusion: In clinical practice, all ceramics and surface finishing treatments (C+P, G) can be used. If translucency is important, NLD and FGLD ceramics may be preferred.

Benzer Tezler

  1. Tez No

    92377

    Bilişim sistemlerindeki gelişmelerin işletme yönetimine etkileri, yönetim bilişim sistemleri geliştirme ve bir uygulama örneği

    Effects of the evoluation of information systems on management, management information systems development and an example of its application

    ZUHAL TANRIKULU

    Doktora

    Türkçe

    Türkçe

    1999

    İşletmeİstanbul Üniversitesi

    İşletme Yönetimi ve Organizasyon Ana Bilim Dalı

    PROF. DR. EROL EREN

  2. Tez No

    669561

    Farklı yüzey bitirme işlemleri uygulanan CAD-CAM porselen bloklarının içeceklere bırakıldıktan sonraki renk ve yüzey değişimlerinin incelenmesi

    Investigation of color and surface changes of cad-CAM porcelain blocks applied different surface finishing processes after leaving to beverages

    MELEK KILIÇ AVŞAR

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2021

    Diş HekimliğiSivas Cumhuriyet Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. GİRAY BOLAYIR

  3. Tez No

    968234

    Farklı yüzey bitirme işlemleri uygulanan CAD/CAM seramik materyallerinin yüzey pürüzlülüğü ve bükülme dayanımının değerlendirilmesi

    Evaluation of surface roughness and flexural strength of CAD/CAM ceramic materials subjected to different surface finishing procedures

    MELİSA BALABAN

    Doktora

    Türkçe

    Türkçe

    2025

    Diş HekimliğiBiruni Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. ALİ KEMAL ÖZDEMİR

  4. Tez No

    547903

    Farklı bitirme işlemleri uygulanan CAD/CAM seramiklerin termal yaşlandırma sonrası renk stabilitelerinin değerlendirilmesi

    The evaluation of the color stability of CAD / CAM ceramics after different finishing procedures and thermal aging

    FUNDA SOYSAL

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2019

    Diş HekimliğiGaziantep Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ NERMİN DEMİRKOL

  5. Tez No

    564747

    Farklı bitirme ve cila işlemleri ile farklı beyazlatma tekniklerinin CAD/CAM materyallerin renk ve yüzey özellikleri üzerine etkileri

    The effects of different finishing and polishing processes and different whitening techniques on the color and surface properties of CAD/CAM materials

    HANİFE ŞEYMA AKMAN

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2019

    Diş HekimliğiKocaeli Üniversitesi

    Restoratif Diş Tedavisi Ana Bilim Dalı

    DOÇ. DR. NESLİHAN TEKÇE

Geri Dön