Farklı fiber destekli kompozit materyallerin ve restorasyon tekniklerinin endodontik tedavili premolarların kırılma direnci üzerine etkisi
The effect of different fiber-reinforced composite materials and restoration techniques on the fracture resistance of endodontically treated premolars
- Tez No: 1023963
- Danışmanlar: DR. ÖĞR. ÜYESİ GÖKHAN KARADAĞ
- Tez Türü: Tıpta Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Kırılma direnci, Fiber post, Kısa fiber destekli kompozit, Polietilen şerit fiber, Anatomik post, Fracture resistance, Fiber post, Short fiber-reinforced composite, Polyethylene ribbon fiber, Anatomical post
- Yıl: 2026
- Dil: Türkçe
- Üniversite: Kırıkkale Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmanın amacı; endodontik tedavi görmüş ve kalan koronal doku miktarı bakımından post-kor ile direkt restorasyon endikasyon sınırında yer alan (1,6 mm kritik duvar kalınlığı) dişlerde, farklı fiber post sistemlerinin ve fiberle güçlendirilmiş kompozit (FGK) üst yapı materyallerinin kırılma dayanımı ve kırık tipleri üzerindeki etkilerini in vitro olarak karşılaştırmalı değerlendirmektir. Çalışmada periodontal nedenlerle çekilmiş 120 adet tek köklü alt premolar diş kullanılmıştır. Numuneler rastgele 8 gruba (n=15) ayrılmıştır: Grup 1: Kontrol (CTRL) Grup 2: Konvansiyonel kompozit (COMP) Grup 3: EverX Flow + Kompozit (EXF) Grup 4: Ribbond + EverX Flow + Kompozit (RB-EXF) Grup 5: EverX Flow post + EverX Flow kor (EXF-Mon) Grup 6: Ribbond post + Ribbond + EverX Flow (RBP-EXF) Grup 7: Prefabrik fiber post + EverX Flow (pFP-EXF) Grup 8: Anatomik fiber post + EverX Flow (aFP-EXF) Kök kanal tedavileri ve ilgili post-restorasyon prosedürleri tamamlanan örneklere, ağız ortamını simüle etmek amacıyla termal siklus (5500 döngü, 5-55°C) uygulanmıştır. Biyomekanik direnç, universal test cihazında 45° açıyla 1 mm/dk hızda statik yükleme yapılarak Newton (N) cinsinden kaydedilmiştir. Kırık tipleri stereomikroskop altında incelenerek onarılabilir veya onarılamaz olarak kaydedilmiştir. Veriler tek yönlü varyans analizi (One-Way ANOVA) ve Bonferroni post-hoc testleri ile analiz edilmiştir. Grupların kırılma yükü değerleri arasında istatistiksel olarak anlamlı fark saptanmış (p<0,001) ve sağlam dişlerden oluşan CTRL grubunun en yüksek dayanımı sergilediği görülmüştür. Deney grupları arasında fiber post içeren pFP-EXF ve aFP-EXF grupları, COMP ve postsuz fiber gruplarına göre anlamlı derecede yüksek kırılma direnci göstermiştir (p<0,05). Herhangi bir intraradiküler preparasyon yapılmayan anüler şerit fiber grubu (RB-EXF) COMP grubundan anlamlı derecede üstün bulunurken fiber post gruplarıyla istatistiksel olarak benzer performans sergilemiştir (p>0,05). Gruplar arasında kırık tipleri açısından istatistiksel anlamlı bir ilişki bulunmamakla birlikte (p>0,05), en yüksek onarılabilir kırık oranı %60,0 ile RB-EXF grubunda; en yüksek onarılamaz kırık oranı ise %80,0 ile COMP ve pFP-EXF gruplarında gözlenmiştir. Kritik duvar kalınlığına sahip endodontik tedavili dişlerde, dikey omurga desteği sağlayan konvansiyonel veya anatomik cam fiber post uygulamaları maksimum yük taşıma kapasitesi sunmaktadır. Bununla birlikte, kök kanalından ek madde uzaklaştırılmasından kaçınılan klinik durumlarda, koronal anüler polietilen şerit fiber ve kısa fiber destekli akışkan kompozit kombinasyonu (RB-EXF), yüksek kırılma dayanımı ve üstün onarılabilirlik potansiyeliyle güvenilir bir minimal invaziv tedavi alternatifidir.
Özet (Çeviri)
The aim of this in vitro study was to comparatively evaluate the effects of different fiber post systems and fiber-reinforced composite (FRC) core materials on the fracture resistance and failure modes of endodontically treated mandibular premolars located at the threshold of post-core versus direct restoration indications with a critical coronal wall thickness of 1,6 mm. One hundred and twenty extracted single-rooted human mandibular premolars were selected for the study. The specimens were randomly allocated into 8 experimental groups (n=15): Group 1: Control (CTRL); Group 2: Conventional composite (COMP) Group 3: EverX Flow + Composite (EXF) Group 4: Ribbond + EverX Flow + Composite (RB-EXF) Group 5: EverX Flow post + EverX Flow core (EXF-Mon) Group 6: Ribbond post + Ribbond + EverX Flow (RBP-EXF) Group 7: Prefabricated fiber post + EverX Flow (pFP-EXF) Group 8: Anatomical fiber post + EverX Flow (aFP-EXF) Following root canal treatment and post-restoration procedures, all specimens were subjected to thermal cycling (5500 cycles, 5-55 °C) to simulate the oral environment. Fracture resistance was determined in Newtons (N) using a universal testing machine with static loading applied at a 45° angle and a crosshead speed of 1 mm/min. Failure modes were examined under a stereomicroscope and classified as repairable or irreparable. Data were statistically analyzed using One-Way ANOVA and Bonferroni post-hoc tests. Significant differences in fracture resistance were found among the groups (p<0,001). The intact CTRL group exhibited the highest fracture resistance. Among the experimental groups, fiber post-retained restorations pFP-EXF and aFP-EXF demonstrated significantly higher fracture resistance compared to the COMP and postless EXF groups (p<0.05). The non-intraradicular annular polyethylene ribbon fiber group (RB-EXF) yielded significantly higher values than the COMP group and performed statistically similarly to the glass fiber post groups (p>0.05). Although no statistically significant correlation was found regarding failure modes (p>0.05), the highest repairable failure rate was observed in the RB-EXF group (60.0%), while the highest irreparable failure rate was found in the COMP and pFP-EXF groups (80.0%). In endodontically treated teeth with critical wall thickness, conventional or anatomical glass fiber post applications providing vertical ridge support offer maximum load-bearing capacity. However, in clinical scenarios where additional radicular tissue removal is contraindicated, the combination of coronal annular polyethylene ribbond fiber and short fiber-reinforced flowable composite (RB-EXF) serves as a reliable minimally invasive alternative due to its high fracture resistance and superior repairability potential.
Benzer Tezler
- Farklı miktarlarda doku kaybına uğrayan endodontik tedavi görmüş dişlerde çeşitli restorasyon tekniklerinin kırılma direncine etkisi
Evaluation of the influence of different restoration techniques on the fracture resistance of endodontically treated teeth with various amounts of tissue loss
ELİF TÜRKEŞ
Doktora
Türkçe
2017
Diş Hekimliğiİstanbul ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
PROF. DR. YASEMİN BENDERLİ GÖKÇE
- Açık apeksli üst çene ön dişlerde revitalizasyon tedavisi sonrası uygulanan indirekt restorasyonların kırılma dayanımı üzerine etkisinin karşılaştırılması: İn-vitro çalışma
Comparison of the effect of indirect restorations on the fracture resistance of open-apex maxillary anterior teeth following revitalization therapy: An in-vitro study
ALPEREN FAHRİ KEREMİT
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiEge ÜniversitesiEndodonti Ana Bilim Dalı
DOÇ. DR. BURCU ŞEREFOĞLU POLAT
- Bazı esterlerin kinetik incelenmesi ve termodinamik parametrelerin belirlenmesi
Kinetic study and detesmination of thermodnamic parameters of some esters
İBRAHİM TAŞ
Yüksek Lisans
Türkçe
1986
Kimya MühendisliğiUludağ ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. MUSTAFA CEBE
- İzmir'de bazı yolların kapatılarak yaya bölgeleri oluşturma da kent peyzajını geliştirme açısından yeniden planlanması üzerinde araştırmalar
Başlık çevirisi yok
BAHAR TÜRKYILMAZ
Yüksek Lisans
Türkçe
1985
Şehircilik ve Bölge PlanlamaEge ÜniversitesiŞehir ve Bölge Planlama Ana Bilim Dalı
- Testosteron dihidrotestosteron ve östrojenin benign prostat hiperplazisindeki etyolojik rolleri
The roles of testosterone, dihydrotestosterone and estradiole on the etiology of benign prostatic hyperplasia
HALUK TOKUÇOĞLU