Farklı baskı açıları ve kürleme süreleri kullanılarak 3 boyutlu yazıcı ile üretilen lingual retainerların mekanik özelliklerinin değerlendirilmesi
Evaluation of the mechanical properties of three-dimensionally printed lingual retainers fabricated using different printing orientations and post-curing times
- Tez No: 1024346
- Danışmanlar: DOÇ. DR. BARIŞ BAŞER
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Üç boyutlu baskı, lingual retainer, baskı açısı, post-kürleme, eğilme dayanımı, mikrosertlik, yüzey pürüzlülüğü, Three-dimensional printing, lingual retainer, printing orientation, post-curing, flexural strength, microhardness, surface roughness
- Yıl: 2026
- Dil: Türkçe
- Üniversite: Karadeniz Teknik Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Ortodonti Ana Bilim Dalı
- Bilim Dalı: Ortodonti Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu in vitro çalışmanın amacı, farklı baskı açıları ve post-kürleme süreleri kullanılarak üç boyutlu yazıcı ile üretilen lingual retainerların eğilme dayanımı, mikrosertlik ve yüzey pürüzlülüğü özelliklerinin değerlendirilmesidir. Çalışmada SprintRay Pro S dijital ışık işleme (DLP) üç boyutlu yazıcısı ve SprintRay OnX Tough 2 reçinesi kullanılarak toplam 144 adet numune üretildi. Numuneler baskı açısına (0°, 45° ve 90°) ve post-kürleme süresine (1, 10 ve 20 dakika) göre dokuz gruba ayrıldı (n=16). Eğilme dayanımı testleri üç nokta eğme yöntemiyle gerçekleştirildi. Mikrosertlik ölçümleri Vickers sertlik testi ile, yüzey pürüzlülüğü ölçümleri ise profilometre kullanılarak yapıldı. Baskı açısı eğilme dayanımı, mikrosertlik ve yüzey pürüzlülüğü üzerinde istatistiksel olarak anlamlı etki gösterdi (p<0,05). Eğilme dayanımı açısından en yüksek ortalama değer 45° baskı açısında elde edilirken, 0° baskı açısında anlamlı derecede daha düşük değerler saptandı. Post-kürleme süresi eğilme dayanımı ve mikrosertlik üzerinde anlamlı etki gösterirken, yüzey pürüzlülüğü üzerinde anlamlı bir etkisi bulunmadı. Mikrosertlik açısından en yüksek değerler 0° baskı açısında elde edilirken, 45° ve 90° gruplarında daha düşük değerler gözlendi. Yüzey pürüzlülüğü bakımından ise en yüksek değerler 90° baskı açısında belirlenirken, 0° ve 45° baskı açıları arasında anlamlı fark bulunmadı. Çalışmanın bulguları, üç boyutlu baskı ile üretilen lingual retainerların mekanik özelliklerinin baskı açısı ve post-kürleme protokolünden etkilendiğini göstermektedir. Eğilme dayanımı açısından 45° baskı açısı daha avantajlı bulunurken, mikrosertlik bakımından 0° baskı açısı daha yüksek değerler sağlamıştır. Yüzey pürüzlülüğü ise esas olarak baskı açısından etkilenmiş, post-kürleme süresinden anlamlı düzeyde etkilenmemiştir. Bu sonuçlar, lingual retainer üretiminde baskı yönelimi ve post-kürleme protokollerinin materyalin mekanik performansını optimize etmek amacıyla dikkatle seçilmesi gerektiğini göstermektedir.
Özet (Çeviri)
The aim of this in vitro study was to evaluate the flexural strength, microhardness, and surface roughness of three-dimensionally printed lingual retainers fabricated using different printing orientations and post-curing times. A total of 144 specimens were fabricated using a SprintRay Pro S digital light processing (DLP) three-dimensional printer and SprintRay OnX Tough 2 resin. The specimens were divided into nine groups according to printing orientation (0°, 45°, and 90°) and post-curing time (1, 10, and 20 minutes) (n=12). Flexural strength was evaluated using a three-point bending test. Microhardness was measured using the Vickers hardness test, while surface roughness was assessed using a profilometer. Printing orientation had a statistically significant effect on flexural strength, microhardness, and surface roughness (p<0.05). The highest mean flexural strength was observed in the 45° printing orientation, whereas the 0° orientation exhibited significantly lower values. Post-curing time significantly affected flexural strength and microhardness but had no significant effect on surface roughness. The highest microhardness values were obtained in the 0° printing orientation, while lower values were observed in the 45° and 90° groups. Regarding surface roughness, the highest values were recorded in the 90° printing orientation, whereas no significant difference was found between the 0° and 45° groups. The findings of this study demonstrate that the mechanical properties of three-dimensionally printed lingual retainers are influenced by both printing orientation and post-curing protocol. The 45° printing orientation exhibited superior flexural strength, whereas the 0° orientation provided higher microhardness values. Surface roughness was primarily affected by printing orientation and was not significantly influenced by post-curing time. These findings suggest that the selection of an appropriate printing orientation and post-curing protocol is essential for optimizing the mechanical performance of three-dimensionally printed lingual retainers.
Benzer Tezler
- Microneedles for DNA extraction in plant studies
Bitki çalışmalarında DNA ekstraksiyonu için mikroiğneler
EMRE ECE
Yüksek Lisans
İngilizce
2024
Mühendislik Bilimleriİhsan Doğramacı Bilkent ÜniversitesiMalzeme Bilimi ve Nanoteknoloji Ana Bilim Dalı (disiplinlerarası)
DOÇ. DR. FATİH İNCİ
- Farklı üretim açıları ve farklı destek çaplarının eklemeli yöntem ile üretilen daimi restorasyonlarda yüzey pürüzlülüğüne etkisi
Effect of different printing orientation and support diameters on surface roughness of permanent restorations fabricated by additive manufacturing
ERVA NUR SAHİP
Diş Hekimliği Uzmanlık
Türkçe
2026
Diş HekimliğiHatay Mustafa Kemal ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ BİLGE ERGÜNBAŞ
- Farklı baskı parametreleri ve yıkama protokolleri uygulanarak 3 boyutlu yazıcılarla üretilen şeffaf retansiyon plaklarının mekanik, fiziksel özellikleri ve renk stabilitelerinin değerlendirilmesi
Evaluation of mechanical and physical properties and color stability of clear retainers fabricated by three-dimensional printers with different printing parameters and washing protocols
NİLAY KARABULUT AYDIN
Diş Hekimliği Uzmanlık
Türkçe
2026
Diş HekimliğiKaradeniz Teknik ÜniversitesiOrtodonti Ana Bilim Dalı
DOÇ. DR. BARIŞ BAŞER
- İki farklı tam seramik kor materyalinin baskı dayanıklılığı ve marjinal uyumu üzerine farklı marjinal dizayn ve taper açılarının etkisi
The effect of different margin designs and taper angles on the compressive strength and marginal fit of two different all ceramic cores
H.NALAN BOZOĞULLARI
Doktora
Türkçe
2007
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF.DR. ÖZGÜR İNAN
- Farklı tipte 3B yazıcılar kullanılarak, farklı yerleştirme açıları ve farklı eğim konfigürasyonları ile üretilen tam protez kaide materyallerinin dönüşüm derecesi, sitotoksisite ve kandida tutulumu yönünden karşılaştırılması
Comparison of degree of conversion, cytotoxicity and candida albicans retention of complete denture base materials produced with different types of 3D printers, build orientations, and curvature configurations
BARIŞ SÖZÜÖZ
Doktora
Türkçe
2025
Diş HekimliğiSağlık Bilimleri ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. OSMAN CUMHUR SİPAHİ