Toz metalurjisi yöntemiyle üretilen Fe-C-Mo-Cr7C3 kompozitinin abrasiv aşınma dayanımının araştırılması

The investigation of abrasive wear of Fe-C-Mo-Cr7C3 composite producted by powder metallurgy process

  1. Tez No: 134788
  2. Yazar: MUSTAFA AY
  3. Danışmanlar: YRD. DOÇ. DR. AHMET HASÇALIK
  4. Tez Türü: Yüksek Lisans
  5. Konular: Makine Mühendisliği, Teknik Eğitim, Mechanical Engineering, Technical Education
  6. Anahtar Kelimeler: Powder metallurgy, ferrous based composites, abrasive wear
  7. Yıl: 2003
  8. Dil: Türkçe
  9. Üniversite: Fırat Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Makine Eğitimi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 134

Özet

Bu çalışmada Fe tozuna ağırlıkça % 3 oranında Mo, % 1.5 oranında C ve % 4, %8, %12 oranlarında (ortalama 25um, 50um, 80um tane boyutlarında) ferrokrom tozlan katılarak toz metalürjisi yöntemi ile üretilmiş olan Fe-C-Mo-Cr kompozitinin abrasiv aşınma davranışı üzerinde krom karbürün (Cr7C3) etkisi incelenmiştir. Deney çalışmalarında, üretilen numunelerin mikroyapıları optik mikroskop, Taramalı elektron mikroskobu SEM (Scanning Elektron Microscopy), EDS (Energy Dispersive Spectrograf) noktasal analiz çalışmaları ve X - Işınlan difraksiyonu (X - Ray Difraction) çalışmaları ile belirlenmiş ve mikrosertlikleri tespit edilmiştir. Aşınma testleri özel olarak imal edilmiş olan pin on disk aşınma test cihazında farklı yüklerde (ION, 20N, 3 ON) yapılarak numunelerin aşınma dirençleri tespit edilmiştir. Yapılan testler sonucunda, takviye elemanının tane boyutunun artmasıyla aşınma oranının arttığı ve deney şartlarında en iyi aşınma direncini ortalama 25um tane boyutundaki ağırlıkça %12 ferrokrom katkılı numunenin gösterdiği saptanmıştır. Çalışma altı bölümden oluşmaktadır. Birinci bölümde konuya giriş yapılarak ilgili literatür ve çalışmanın amacı verilmiştir. İkinci bölümde toz metalürji yöntemi açıklanmıştır. Üçüncü bölümde aşınma mekanizması, türleri, ölçüm teknikleri ve aşınmayı etkileyen faktörler incelenmiştir. Dördüncü bölümde deney ve ölçüm yöntemi açıklanmıştır. Beşinci bölümde deney sonuçlan tartışılarak yorumlanması ve son bölümde ise deneyler sonunda elde edilen sonuçlar verilerek, öneriler sunulmuştur.Anahatar Kelimeler : Toz metalürjisi, Fe esaslı kompozitler, abrasiv aşınma

Özet (Çeviri)

In this study, the effect of chrome carbide (O7C3) on abrasive wear of Fe-C-Mo- Cr7C3 composite produced by powder metallurgy, containing 3 wt.% Mo, 1,5 wt.% C and 4, 8, 12 wt.% Ferrochromium with the average particle size of 25 urn, 50um and 80um was investigated. In the experiments, microstnictures of the samples were examined by optic and Scanning electron microscopy, EDS (Energy Dispersive Spectrograph), X- ray diffraction method and microhardnes were measured. Wear resistances of samples were determined using different loads (ION, 20N, 30N) by pin on disc wear test machine developed for this experiment. In the experiments it has been found that with the increasing particle size of reinforcing element, wear rate increased and the 12 wt. % ferrocliromium reinforced sample showed the highest wear resistance in the experiment conditions. The study consists of six chapters. In the first chapter of study, introduction, literature related to the subject and purpose of study were given. In the second chapter, powder metallurgy was described. In the third chapter, the mechanisms of the wear, various wear types, measurement techniques and the factors affecting the wear were presented. In the fourth chapter, material and method were described. In the fifth chapter, the results were discussed and in the final chapter, general results and recommendation have been presented.

Benzer Tezler

  1. T/M paslanmaz çelik implantların üretimi ve teknolojik özellikleri üzerine bir araştırma

    Production of P/M stainless steel implants and investigation on their technological properties

    NACİ KURGAN

    Doktora

    Türkçe

    Türkçe

    2005

    Makine MühendisliğiCelal Bayar Üniversitesi

    PROF.DR. REMZİ VAROL

  2. Kendiliğinden ilerleyen yüksek sıcaklık sentezi ile tufalden demir esaslı kompozit (Mo2FeB2-Fe) üretimi

    Production of iron based composite (Mo2FeB2-Fe) from scale by self propagating high temperature synthesis

    BUSE YILMAZ

    Yüksek Lisans

    Türkçe

    Türkçe

    2019

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DOÇ. DR. CEVAT BORA DERİN

  3. TIG kaynağı ile birleştirilmiş demir esaslı T/M malzemelerin kaynak bölgesinin mekanik özelliklerinin belirlenmesi

    Determination of mechanical properties of the weld region of iron based T/M materials joined by TIG welding

    ONUR ELEKTİRİKÇİ

    Yüksek Lisans

    Türkçe

    Türkçe

    2007

    Makine MühendisliğiCelal Bayar Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. CEVDET MERİÇ

  4. Al-Fe-V-Si alaşımlarının yüksek sıcaklık aşınma özelliklerinin incelenmesi

    Investigation of elevated temperature wear properties of Al-Fe-V-Si aluminium alloys

    EMRAH KORAMAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2011

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DOÇ. DR. MURAT BAYDOĞAN

    PROF. DR. ALİ KALKANLI

  5. Mekanik alaşımlama süreçleriyle MoS2-grafit katı yağlayıcı katkılı Fe-C esaslı kompresör parçalarının geliştirilmesi ve karakterizasyonu

    Development and characterization of iron based and MoS2, graphite solid lubricant reinforced compressor parts synthesized by mechanical alloying

    MERVE UYSAL

    Yüksek Lisans

    Türkçe

    Türkçe

    2016

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. MUSTAFA LUTFİ ÖVEÇOĞLU