Preperation of Al-Ti-alloy closed-cell metal foams via foaming of powder compacts

Toz kompakt köpükleştirme yöntemi ile Al-Ti alaşımlı kapalı hücre metal köpüklerin hazırlanması

  1. Tez No: 177059
  2. Yazar: NURETTİN DENİZ KARSU
  3. Danışmanlar: PROF. DR. MUSTAFA GÜDEN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Makine Mühendisliği, Metalurji Mühendisliği, Mechanical Engineering, Metallurgical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2008
  8. Dil: İngilizce
  9. Üniversite: İzmir Yüksek Teknoloji Enstitüsü
  10. Enstitü: Mühendislik ve Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 109

Özet

Al toz kompaktların köpükleştirilmesinde, ıslatılmış parçacık etkisinin uzamayave köpük kararlılığına etkilerini belirlemek için ağırlıkça %5 oranında 30?45, 45?56,56?90, 90?106, 106?160 ve 160?200 ?m boyutlu küresel Ti6Al4V tozu içeren Alkompaktların köpükleşme davranışları gözlemlenmiştir. Parçacık etkisini belirlemekiçin, parçacık içermeyen Al kompaktlar da hazırlanıp, köpükleştirilmiştir. Köpükleşmedeneyleri deney esnasında uzamayı ölçebilecek bir sistemle 700?730 ºC'de yapılmıştır.Köpükleşen kompaktlardan göbek delme yöntemi ile elde edilen küçük numunelerstatik hızlarda basma testine tabi tutulmuşlardır.Al kompaktlar 4 bölgeden oluşan karakteristik uzama göstermişlerdir. Ağırlıkça%5 oranında Ti6Al4V içeren kompaktlarda küçük parçacık boyutlarında, uzamanınnispi olarak az olduğu ve uzamanın, parçacık boyutunun artması ile arttığı bulunmuştur.Ağırlık oranınca farklı, 30?45 ?m boyutunda Ti6Al4V içeren kompaktlarla yapılanköpükleştirme deneylerinde, ağırlıkça %2'den daha az oranda Ti6Al4V içerenkompaktların Al kompaktlara benzer uzamalar gösterdiği bulunmuştur. Mikroskobikçalışmalar, Ti6Al4V katkısının drenajı azalttığını göstermiştir. Köpükleşme esnasındasıvı Al ile Ti6Al4V reaksiyona girerek TiAl3 parçacıkları oluşturmuştur. Nispetenküçük boyutlu parçacıklar içeren kompaktlarda reaksiyon tabakası hücre duvar veköşelerine dağılım gösterirken, büyük parçacık içeren kompaktlarda ise bu tabakaparçacığa bağlı kalmıştır. Ti6Al4V içeren kompaktlarda düşük drenaj ve azalanköpükleşme, literatürdeki mevcut kararlılık modelleri kullanılarak tartışılmıştır.Köpükleşmenin küçük parçacık içeren kompaktlarda azalması, toplam parçacık yüzeyalanı yüksek olması ve daha fazla TiAl3 parçacık oluşumu ile artan viskoziteyebağlanmıştır. Ti6Al4V içeren kompaktlarda ölçülen düşük basma mukavemetinin,kullanılan küçük boyutlu test numunelerinin kaba malzemenin özelliklerinigöstermemesinden kaynaklanmaktadır.

Özet (Çeviri)

The foaming behavior of 5 wt% 30-45, 45-56, 56-90, 90-106, 106-160 and160-200 ?m size spherical Ti6Al4V particle-added Al powder compacts wereinvestigated for determining the effects of wetted particles on the expansion andstability of Al powder compacts. In order to determine the effect of particle-addition onthe foaming behavior, Al compacts without particle addition prepared with samemethod were also foamed. Foaming experiments were performed using an in-situ foamexpansion measuring system at 700-730 ºC. Small compression test samples werefurther core drilled from Ti6Al4V-Al foam samples and tested at quasi-static strainrates.Al compacts showed the characteristic expansion-time curve, composing of 4distinct regions. The expansion of 5 wt% Ti6Al4V-added compacts was found to berelatively low at small size particle additions, but increased with increasing particle size.Measurements of foam expansions of 30-45 ?m size Ti6Al4V-added compacts withvarious weight percentages of particles showed that when the wt% of particles is lowerthan 2 wt%, the expansion behavior of the compacts became very similar to that of pureAl. Microscopic studies have further shown that Ti6Al4V addition reduced the drainageas compared with pure Al compacts. In foaming of Ti6Al4V-Al compacts, the liquid Alreacted with Ti6Al4V particles and formed TiAl3 particles. In relatively small sizeparticle-added foams, TiAl3 particles dispersed through cell walls and cell edges, but atincreased particle size, these particles were found next to the Ti6Al4V particles. Thereduced drainage and lower foam expansions in the foaming of Ti6Al4V-addedcompacts were discussed based on the foam stabilization models in the literature. Thereduced foamability of the compacts in small particle size Ti6Al4V addition wasattributed to relatively high viscosities, due to higher cumulative surface area of theparticles and higher rate of reaction between liquid Al and Ti6Al4V. The lowercompression strength measured in Ti6Al4V-added foams was attributed to smallspecimen sizes, which could not show the mechanical properties of the bulk material.

Benzer Tezler

  1. P-galyum arsenür (GaAs)/anodik izolasyon filmlerin arayüzey özelliklerinin incelenmesi

    Investigation of interface properties in p-gallium arsenide (GaAs)/anodic insulator films

    HAYRETTİN YÜZER

    Doktora

    Türkçe

    Türkçe

    1994

    Kimya Mühendisliğiİstanbul Teknik Üniversitesi

    PROF.DR. A. HİKMET ÜÇIŞIK

  2. Dizel motorların doğal gaz motorlarına dönüştürülmesi

    conversion of diesel engines to natural gas engines

    FUAT PANCAR

    Yüksek Lisans

    Türkçe

    Türkçe

    1994

    Makine Mühendisliğiİstanbul Teknik Üniversitesi

    DOÇ.DR. ERTUĞRUL ARSLAN

  3. Carbon aerogel supported pure Pt and bimetallic Pt-Cu nanoparticles by supercritical deposition as electrocatalysts for polymer electrolyte membrane fuel cells

    Polimer elektrolit membranlı yakıt pilleri için elektrokatalizör olarak karbon aerojel destekli saf Pt ve Pt-Cu ikili alaşım nanoparçacıklarının süperkritik depozisyon yöntemi ile hazırlanması ve karakterizasyonu

    ŞANSIM BENGİSU BARIM

    Yüksek Lisans

    İngilizce

    İngilizce

    2016

    Kimya MühendisliğiKoç Üniversitesi

    Kimya ve Biyoloji Mühendisliği Ana Bilim Dalı

    PROF. CAN ERKEY

  4. Otomotivde yaygın kullanılan saplama bağlantı elemanlarının kaynaklanabilirliğinin altı sigma metodu ile optimizasyonu

    Optimization of weldability of stud joining elements commonly used in automotive with six sigma methodology

    UTKU CAN KUMRU

    Yüksek Lisans

    Türkçe

    Türkçe

    2021

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Malzeme Mühendisliği Ana Bilim Dalı

    DOÇ. DR. DERYA DIŞPINAR

  5. Alternatif medya yaklaşımıyla Kürtçe dijital kültür-sanat dergiciliği

    The publication of Kurdish digital culture and art magazines through an alternative media approach

    LEYLA ÖZKAPLAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2022

    GazetecilikGalatasaray Üniversitesi

    Radyo Televizyon ve Sinema Ana Bilim Dalı

    DOÇ. DR. CEREN SÖZERİ ÖZDAL