Synthesis and characterization of polythiophene/montmorillonite and polythiophene/polypropylene composites
Politiofen/montmorillonit ve politiofen/polipropilen kompozitlerinin sentezi ve karakterizasyonu
- Tez No: 181142
- Danışmanlar: PROF. DR. ZUHAL KÜÇÜKYAVUZ
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Politiofen, Montmorillonit, Politiofen/Polipropilenkompozitleri, Nanokompozit, Isısal, Morfolojik, Elektriksel ve Mekanik Özellikler, Polythiophene, Montmorillonite, Polythiophene/Polypropylenecomposites, Nanocomposite, Thermal, Morphological, Electrical and MechanicalProperties
- Yıl: 2006
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada, politiofen(PTP)/montmorillonit(MMT) nanokompozitleri,yerinde polimerleştirme ve kimyasal oksidatif polimerizasyon yöntemleri ile eldeedildi. Yerinde polimerleştirme yönteminde, ağırlıkça % 90 ve % 95 MMT içerenkompozitler hazırlandı. Kimyasal oksidatif polimerizasyon yönteminde iseağırlıkça % 1-15 aralığında MMT içeren kompozitler sentezlendi. Örneklerintermal ve morfolojik özellikleri Differensiyal Taramalı Kalorimetre, TermalGravimetrik Analiz, X-ışını Kırınımı ve Taramalı Elektron Mikroskobu ileincelendi; elektriksel iletkenlikleri dört nokta yöntemi ile ölçüldü.PTP/MMT kompozitleri işlenemez olduğundan, PTP/polipropilen(PP)kompozitleri hazırlandı. Kompozitlerde PTP miktarları ağırlıkça % 2-30 aralığındadeğiştirildi. Mekanik özellikleri gerilme testi ile incelendi. Elektrikseliletkenliklerin ölçümü için dört nokta yöntemi kullanıldı. Morfolojikkarakterizasyonlar Taramalı Elektron Mikroskobu ile yapıldı.PTP oluşması ve PTP/MMT kompozitinde yer alması FTIR analizi iledoğrulandı. Differensiyal Taramalı Kalorimetre sonuçları, politiofenin 25-300 0Caralığında herhangi bir ısısal geçişi olmadığını gösterdi. Termal GravimetrikAnaliz sonuçları, PTP/MMT kompozitlerinin ısısal dayanıklılığının saf politiofeneoranla çok daha iyi olduğunu gösterdi. X-ışını Kırınımı analizi, yüksek MMTiçeriğinde tiofenin MMT kristal düzlemleri arasında polimerleşerek nanokompozitoluşturduğunu gösterdi. Taramalı Elektron Mikroskobu çalışmalarında,kompozitler yumaksı parçacıklar ve kümeler halinde gözlemlendi. PTP/MMTkompozitlerinin iletkenlikleri 10-3 S/cm mertebesindedir. PTP/PP kompozitlerininelastisite modülü değerlerinin PTP ilavesi ile arttığı, fakat uzama yüzdelerindekayda değer bir değişim görülmediği gözlendi. PTP miktarının artması elektrikseliletkenliği artırdı.
Özet (Çeviri)
In this study, polythiophene(PTP)/montmorillonite(MMT) nanocompositeswere synthesized by in situ intercalative polymerization and chemical oxidativepolymerization. In in situ intercalative polymerization method, compositescontaining 90 and 95% MMT were prepared. In chemical oxidativepolymerization method, a series of composites ranging from 1 to 15% by weightMMT were synthesized. Thermal and morphological properties of samples wereinvestigated by Differential Scanning Calorimeter (DSC), Thermal GravimetricAnalysis (TGA), X-ray Diffraction (XRD) and Scanning Electron Microscope(SEM); electrical conductivities were measured by four probe technique.Since PTP/MMT composites are unprocessable PTP/polypropylene(PP)composites were prepared. Amounts of PTP were changed in the range 2-30 % byweight in the composites. Mechanical properties were investigated by tensile tests.Four probe technique was used for measurement of electrical conductivities.Morphological characterizations were made by SEM.Formation of PTP and its incorporation in PTP/MMT composite wereconfirmed by FTIR analysis. DSC results showed that PTP does not have anythermal transition in the range 25-300 0C. TGA results showed that PTP/MMTcomposites have outstanding stability compared to that of PTP. XRD analysisrevealed the formation of nanocomposites resulting from intercalation ofthiophene in MMT at high MMT contents. Composites were observed as globularparticles and clusters in SEM studies. Conductivity values of PTP/MMTcomposites were in the order of 10-3 S/cm. It is observed that tensile modulus ofPTP/PP composites increases by the addition of PTP, but percentage strain atbreak does not appreciably change. Increasing PTP content increased electricalconductivity.
Benzer Tezler
- Synthesis and characterization of poly(dimethylsiloxane) and polythiophene composites
Polidimetilsiloksan ve politiofen kompozitlerinin sentezi ve karakterizasyonu
MEHMET SANKIR
Yüksek Lisans
İngilizce
2001
KimyaOrta Doğu Teknik ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. SAVAŞ KÜÇÜKYAVUZ
PROF. DR. ZUHAL KÜÇÜKYAVUZ
- Synthesis and characterization of a new soluble polythiophene derivative and its electrochromic application
Yeni bir çözünür politiyofen türevinin sentezi, karakterizasyonu ve elektrokromik cihazlarda kullanımı
SİMGE TARKUÇ
Yüksek Lisans
İngilizce
2006
KimyaOrta Doğu Teknik ÜniversitesiKimya Ana Bilim Dalı
PROF. LEVENT KAMİL TOPPARE
PROF. CİHANGİR TANYELİ
- Synthesis of polythiophene-based conjugated polymers and characterization of their complexes with amine-based additives
Politiyofen bazlı konjuge polimerlerin sentezi ve amin bazlı katkı maddeleri ile komplekslerinin karakterizasyonu
BERFİN CEMRE KELEŞ
Yüksek Lisans
İngilizce
2025
Kimyaİzmir Yüksek Teknoloji EnstitüsüKimya Ana Bilim Dalı
PROF. DR. ÜMİT HAKAN YILDIZ
- Synthesis and characterization of polythioptene and polythioplene/polybutadiene composites
Politiyofen ve politiyofen/polibutadien kompozitlerinin sentezi ve karakterizasyonu
SENEM KIRALP
Yüksek Lisans
İngilizce
2000
KimyaOrta Doğu Teknik ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. ZUHAL KÜÇÜKYAVUZ
- Plazma polimerizasyonu tekniği ile politiyofen ince filmlerin üretilmesi ve karakterizasyonlarının yapılması
Synthesis and characterization of polythiophene thin films via plasma polymerization technique
FATMA GÜL İNCE
Yüksek Lisans
Türkçe
2008
Fizik ve Fizik MühendisliğiÇanakkale Onsekiz Mart ÜniversitesiFizik Ana Bilim Dalı
YRD. DOÇ. DR. HİLAL GÖKTAŞ