Toz metalurjisi yöntemiyle yüzeyine karbür takviye edilmiş düşük karbonlu çeliklerin üretilmesi ve mikroyapısı

Producing of low carbon steels having surfaces reinforced with carbide by powder metallurgy technique and microstructure

  1. Tez No: 185311
  2. Yazar: SEVAL HALE MAHMUTOĞLU
  3. Danışmanlar: DOÇ. DR. MEHMET EROGLU
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Yüzey Kompoziti, Fonksiyonel Olarak Değişen Malzeme, TozMetalurjisi, Vanadyum Karbür, Mikro Yapı, Sertlik, Surface Composite, Functionally Graded Material, Powder Metallurgy, VanadiumCarbide, Microstructure, Hardness
  7. Yıl: 2006
  8. Dil: Türkçe
  9. Üniversite: Fırat Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 112

Özet

ÖZETYüksek Lisans TeziTOZ METALURJİSİ YÖNTEMİYLE YÜZEYİNE KARBÜR TAKVİYE EDİLMİŞ DÜŞÜKKARBONLU ÇELİKLERİN ÜRETİLMESİ VE MİKROYAPISISeval Hale MAHMUTOĞLUFırat ÜniversitesiFen Bilimleri EnstitüsüMetalurji ve Malzeme Mühendisliği Anabilim Dalı2006, Sayfa :98Bu çalışmada yüzeyi farklı oranlarda grafit ve VC ile alaşımlandırılmış düşük karbonluçelikler toz metalurjisi yöntemi ile üretilmişlerdir. Çalışmada alaşımlı yüzeyin ve düşük karbonlu anamalzemenin bölgesinin toz karışımları ayrı ayrı hazırlanmıştır. Alaşımlı kısmı oluşturmak için grafitiçeriği %0.6 ve %1.2 ancak vanadyum karbür içeriği %5, %10, %15, %20 ve %25 olacak şekildedeğişen iki ayrı toz karışımı hazırlanmıştır. Numunelerin düşük karbonlu çelik kısmını oluşturmak içinise %0.2 grafit içeren Fe-grafit toz karışımı hazırlanmıştır.Kalıba önce düşük grafit içerikli tozlar veonun üzerine yüksek alaşımlı tozlar konularak oda sıcaklığında 800MPa basınç altında presleme işlemigerçekleştirilmiştir. Preslenme işleminden sonra preslenmiş numuneler 1200 oC'de 60 dk süre ilesinterlenmişlerdir. Sinterleme işleminden sonra elde edilen numunelerde mikroyapı incelemeleri(EDX, element dağılım haritası, X ışınları analizi dahil) ve sertlik ölçümleri gerçekleştirilmiştir.Mikroyapı incelemeleri sonucunda bütün numunelerde yüzey alaşımlanmış bölgeden düşük karbonluana malzemeye doğru mikroyapısal olarak dört bölge tespit edilmiştir. Bunlar yüksek alaşımlı bölge,kısmen alaşımlandırılmış bölge, geçiş bölgesi ve düşük karbonlu ana malzemedir. Özellikle geçişbölgesinin oluşumunda yüksek alaşımlı bölgeden düşük karbonlu bölgeye doğru meydana gelenkarbon difüzyonu neden olmuştur. Ayrıca karbon difüzyonu nedeniyle fonksiyonel olarak değişenmalzeme oluşumu da gerçekleşmiştir. Sertlik ölçümleri sonucunda en yüksek sertlikler vanadyumkarbür (V8C7) üzerinde elde edilmiş olup, düşük karbonlu ana malzemeye doğru düşüş göstermiştir.Sonuç olarak; bu çalışmayla yüzeyi alaşımlanmış fonksiyonel olarak değişen malzemelerin tozmetalurjisi yöntemi ile üretilebileceği gerek mikroyapısal gerekse sertlik ölçümleri ile gösterilmiştir.

Özet (Çeviri)

ABSTRACTMaster ThesisPRODUCING OF LOW CARBON STEELS HAVING SURFACES REINFORCEDWITH CARBIDE BY POWDER METALLURGY TECHNIQUE ANDMICROSTRUCTURESeval Hale MAHMUTOĞLUFırat UniversityGraduate School of Natural and Applied SciencesDepartment of Metallurgical and Materials Engineering2006, Page : 98In the present study, low carbon steel specimens of which surfaces were alloyed with differentamounts of graphite and vanadium carbides have been produced by powder metallurgytechnique. In the study the powder mixtures for surface alloyed side and for low carbon parentmetal were prepared, respectively. To produce surface alloyed side two different Fe-graphitepowder mixtures containing two different amounts of graphite powder (0.6 wt% and 1.2 wt%)with the same amount of vanadium carbide powder changing as 5, 10 , 15, 20 and 25 wt%were prepared. To produce the side of low carbon steel the powder mixture containing 0.2 wt%graphite were prepared. The low graphite powder mixture was filled into the mould first andthe alloyed powder mixture was filled on the low graphite powder and compacted with apressure of 800 MPa at room temperature. After compacting process, the specimens weresintered at 1200 oC for 60 min. After sintering operation, microstructural investigation includingSEM, EDX, elemental mapping and X-ray, and hardness measurements were performed. Fromthe results of microstructural investigation, from the surface alloyed side to low carbon steelside, it was observed four different microstructural regions, namely high alloyed region,partially alloyed region, transient region and low carbon steel parent metal. Especially, carbondiffusion from high alloyed side to low carbon parent metal caused the formation of transientregion .In addition, functionally graded material produced because of carbon diffusion. Fromthe results of hardness measurement, higher values were obtained for vanadium carbide (V8C7)and the hardness values showed a decrease towards the low carbon steel side. As a result, thisstudy showed that surface alloyed and functionally graded materials can be obtained by powdermetallurgy route as shown by microstructural investigations and hardness measurements.

Benzer Tezler

  1. Copper - diamond composite fabrication by electroforming process for thermal management applications

    Elektroşekillendirme ile üretilen ısıl yönetim amaçlı bakır - elmas kompozit kaplamalar

    GÖKÇE EVREN

    Yüksek Lisans

    İngilizce

    İngilizce

    2020

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. MUSTAFA KAMİL ÜRGEN

  2. Investigation of the cutting performances of the diamond tools used in the natural stone industry

    Doğal taş sanayisinde kullanılan elmaslı kesicilerin kesim performansının incelenmesi

    BERRAK BULUT

    Doktora

    İngilizce

    İngilizce

    2021

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. MURAT BAYDOĞAN

  3. The effect of Ni on the microstructure, wear and corrosion behaviors of microalloyed steels produced by powder metallurgy

    Toz Metalürjisi ile üretilen Nb-V mikroalaşımlı çeliklere Ni ilavesinin aşınma ve korozyon özelliklerine etkisi

    MOHAMED AHMED AHSSI

    Doktora

    İngilizce

    İngilizce

    2023

    Makine MühendisliğiKarabük Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    DOÇ. DR. MEHMET AKİF ERDEN

  4. Toz metalurjisi ile üretilen takım çeliklerinin sıcak daldırma yöntemiyle alüminyum kaplama sonrası yüzey karakterizasyonu

    Surface characterization of powder metallurgy tool steels after hot dip aluminizing

    ANIL ÇALIŞKAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. MURAT BAYDOĞAN

  5. B4C takviyeli TZM alaşımının spark plazma sinterleme yöntemiyle tek adımda üretilmesi ve yüzeyinin borürlenmesi

    Production of B4C reinforced tzm alloy and boriding its surface in one step by spark plasma sintering (SPS) method

    AYBERK ÇETİNBAĞ

    Yüksek Lisans

    Türkçe

    Türkçe

    2021

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. GÜLTEKİN GÖLLER

    DR. ÖĞR. ÜYESİ ÖZDEN ORMANCI ÖZTÜRK