Karbon çeliklerinin sülfürik asit ve etanollü sülfirik asit çözeltilerindeki korozyon davranışı
The Corrosion behaviour of carbon steels in sulphuric acid and ethanolic sulphuric acid solutions
- Tez No: 21938
- Danışmanlar: PROF. DR. MELİKE KABASAKALOĞLU
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Etanol, Karbon çeliği, Korozyon, Sülfürik asit çözeltileri, Ethanol, Carbon steel, Corrosion, Sulfuric acid solutions
- Yıl: 1992
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET Karbon Çeliklerinin Sülfürik Asit ve EtanoIIü Sülfürik Asit Çözeltilerindeki Korozyon Davranışı Bu çalışmada değişik yüzdede karbon içeren çeliklerin (1020, 1030,1040, 1050) oksijensiz 0,1M Na2S04 ve 0,05M H2S04 çözeltilerindeki pasifliği ve korozyon davranışı, kararlı-hal potansiyostatik metot kullanılarak incelenmiştir. Bu çeliklerin anodik polarizasyon eğrilerinde pasifleşme tepesi yoktur. Fakat transpasif patonsiyel bölgesinde anodik polarizasyondan sonra ters yönde potan siyel uygulaması yapılırsa, pasifleşme sağlann\ Bu çeliklerin tekrar pasifleşme ve Flade potansiyellerinin karşılaştırılması 1020 çeliğinin (karbon içeriği düşük) diğerlerinden daha kolay pasifleşebileceğini gösterir. Bütün çeliklerin hem asidik hem de nötral çözeltilerdeki katodik polarizasyon eğrileri aynıdır. Asidik çözeltilerde, bu eğriler korozyon potansiyeli civarında sınır akımı gösterirken; nötral çözeltilerde akım limit değere ulaşmadan önce Tafel bölgesi verirler. Asidik çözeltilerde korozyon reaksiyonunun hızını, hidrojen iyonlarının yüzeye difüzyonu belirlerken; nötral çözeltilerde, aktivasyon kontrollü hidrojen çıkışı, hızı belirler. Ayrıca 1020 çeliğinin etanollü sülfürik asit çözeltilerindeki pasiflik karakteri, hidro jen iyonu konsantrasyonu ve su/alkol oranı değiştirilerek araştırılmış; asit konsant rasyonu azaldıkça pasifliğin daha kolay gerçekleşüği görülmüştür. Su/alkol oranının büyümesi, kritik pasifleşme akımı büyümesine ve korozyon potansiyelinin negatife kaymasına neden olmuştur. Bu ortamlarda da katodik polarizasyon eğrileri, korozyon potansiyeli civarında sınn- akımı verirler.
Özet (Çeviri)
SUMMARY The Corrosion Behaviour of Carbon Steels in Sulphuric Acid and Ethanolic Sulphuric Acid Solutions In this study the passivity and the corrosion behaviour of steels having va rious carbon content (1020.1030,1040,1050) in oxygen free 0,1M Na2S04 and 0,05M H2SO4 solutions were investigated using steady-state potentiostatic method. There is no passivation peak in the anodic polarisation curves of these steels. Ho wever, following the polarisation at transpasif potential range, potential applications in the reverse direction cause repassivation. Cotnparision of the repassivation and Flade potentials of these steels show that steel 1020 (low carbon content) is passi- vated more easily than the others. Cathodic polarisation curves are the same for all steels both in acidic and neutral solutions. In acidic solutions these curves have li miting current region around the corrosion potential, while neutral solutions give a Tafel region before current reaches to limit value. So, in acidic solutions diffusion of hydrogen ions control the corrosion reaction rate, but in neutral solutions activa tion cotrolled hydrogen evalution control the corrosion rate. In addition the passivi ty characteristics of steel 1020 in ethanolic sulphuric acid solutions were investiga ted changing hydrogen ion concentration and water/alcohol concentration ratios. It was observed that the decrease in acid concentration the easier the passivity was ob tained. The increase in the water/alcohol ratio cause the increase in the critic passi vation current and shifts the corrosion potential towards negative values. In these media also the cathodic polarisation curves were found to exhibit li miting current around the corrosion potential.
Benzer Tezler
- Understanding the unusual passive behaviour of high strength hybrid steel in corrosive environments
Yüksek mukavemetli hibrit çeliğin korozif ortamlarda olağandışı pasif davranışının anlaşılması
BESTE PAYAM
Yüksek Lisans
İngilizce
2022
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ CEM ÖRNEK
- Karbon çeliklerinin mikroyapı görüntülerinden mekanik özelliklerinin derin öğrenme ile tahmini
Prediction of mechanical properties of carbon steels by deep learning from microstructure images
RIDVAN SERT
Yüksek Lisans
Türkçe
2024
Bilgisayar Mühendisliği Bilimleri-Bilgisayar ve KontrolGazi ÜniversitesiBilgisayar Mühendisliği Ana Bilim Dalı
DOÇ. DR. FECİR DURAN
- Mikro alaşım elementlerinin mikro alaşımlı karbon çeliklerinin şekillendirilebilirliğine etkisi
The effect of micro-alloying elements on the formability of microalloyed carbon steels
ALİ MURAT SANCAKTAR
Yüksek Lisans
Türkçe
2019
Metalurji Mühendisliğiİstanbul Üniversitesi-CerrahpaşaMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. ALİYE ARABACI
DOÇ. DR. SEBAHATTİN KIRTAY
- The Effect of microstructure and hardness on acoustic properties of hypoeutectoid plain-C steels
Mikroyapının ve sertliğin ötektoid-altı yalın karbon çeliklerinin akustik özelliklerine etkisi
YANKI KELEŞ
Yüksek Lisans
İngilizce
2002
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. C. HAKAN GÜR
PROF. DR. ERDOĞAN TEKİN
- Optimizing and investigation in tig welding parametric influence on tensile strength of dissimilar metals ss-304 and low carbon steel
Benzer olmayan metaller ss-304 ve düşük karbon çeliklerinin tig kaynak parametrelerinin çekme mukavemeti üzerindeki etkilerinin optimizasyonu ve araştırılması
ABDULADIM ABDULMAJID MOHAMED BOGHDADI
Yüksek Lisans
İngilizce
2020
Makine MühendisliğiKarabük ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. İSMAİL ESEN