Farklı çimento tipleri ile üretilen betonların yüksek sıcaklık ve değişik soğutma koşulları altındaki fiziksel ve mekanik özelikleri
Physical and mechanical properties of concretes produced with different cement types at elevated temperatures and different cooling conditions
- Tez No: 244474
- Danışmanlar: YRD. DOÇ. DR. ÖMER FATİH ESER
- Tez Türü: Yüksek Lisans
- Konular: İnşaat Mühendisliği, Civil Engineering
- Anahtar Kelimeler: Çimento, Beton, Yüksek Sıcaklık, Soğutma Türü, Basınç Dayanımı, Cement, Concrete, High Temperature, Cooling Type, Compressive Strength
- Yıl: 2009
- Dil: Türkçe
- Üniversite: Eskişehir Osmangazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Yapı Bilim Dalı
- Sayfa Sayısı: 111
Özet
Yüksek sıcaklık, yapılarda dayanıklılık sorununa neden olan önemli fiziksel etkilerden biridir. Herhangi bir nedenle yüksek sıcaklık etkisinde kalan betonların fiziksel ve mekanik özeliklerinde bazı değişiklikler meydana gelir. Meydana gelebilecek bu değişiklikler performans açısından oldukça önem taşımaktadır. Bu çalışmada, yüksek sıcaklığın ve söndürme türünün betonun fiziksel ve mekanik özeliklerine etkileri deneysel olarak araştırılmıştır. Deneysel çalışma, numune üretimi, kürü, yüksek sıcaklık etkisi, soğutma süreci, fiziksel ve mekanik deneyler olmak üzere beş aşamada gerçekleştirilmiştir. Üretimde, CEM I 42.5 R ve CEM III/A 32.5 N çimentosu, tane boyutu 0-4 mm olan nehir kumu, 4-16, 16-31.5 mm olan kırmataşlar kullanılmıştır. Yüksek sıcaklığın betonun fiziksel ve mekanik özeliklerine etkilerini araştırmak için beton numuneleri 28 ve 56 günlük kür sürelerinin sonunda, TS EN 1363-1'e uygun olarak 3 saat süreyle 150, 300, 450 ve 600 ºC olmak üzere dört farklı sıcaklıkta ısıtılmış, soğutma işlemi havada ve suda olmak üzere iki farklı grupta gerçekleştirilmiştir. Oda sıcaklığına kadar soğutulan numunelerde, birim ağırlık, ultrases geçiş hızı, hacimce su emme değerleri, yarmada çekme dayanımı, yüzey sertliği dayanımı ve basınç dayanımı değerleri belirlenmiştir. Deney sonuçları istatistiksel yöntemle de değerlendirilmiş, yüksek sıcaklık ve soğutma türünün betonun basınç dayanımına etkisi istatistiksel olarak yorumlanmıştır. Deney sonuçları; yüksek sıcaklıkların ve söndürme türünün betonlar üzerinde kayda değer fiziksel ve mekanik etkiler yaptığını göstermiştir. Özellikle 600 ºC'de betonların dayanımlarında çok büyük kayıpların meydana geldiği, kayıpların havada soğutma uygulanan betonlarda suda soğutma uygulananlara göre daha az olduğu görülmüştür.
Özet (Çeviri)
High temperature is one of the important physical effects that lead to durability problem. The physical and mechanical properties of concretes change if they are exposed to high temperatures. These changes are very important for its performance. In this study, the effects of high temperatures and extinguishing type on the physical and mechanical properties of the concrete were investigated by experimentally. Experimental study comprises of five stages as specimen production, cure, high temperature process, cooling process, physical and mechanical tests. In the production, CEM I 42.5 R and CEM III/A 32.5 N cements, river sand in the range of 0-4 mm size, crushed stone in the range of 4-16 and 16-31.5 mm sizes are used. For investigating the effect of high temperature on physical and mechanical properties of concrete, concrete specimens after 28 and 56 days curing periods, are exposed to 150, 300, 450 and 600 °C for 3 hours according to TS EN 1363-1 and samples cooled to the room temperature in water and in air. Unit weight, ultrasonic pulse velocity, values of water absorption by volume, tensile splitting strength, surface hardness strength and compressive strength are determined and recorded after cooling the specimens to the room temperatures. Experimental results are evaluated by using statistical method, the effects of high temperature and cooling type to compressive strength of concrete has been interpreted as statistically. Experimental results have shown that elevated temperatures and type of extinguishing have significant effects on the physical and mechanical properties of concretes. Important strength losses in concrete were observed especially for 600 °C and these strength losses to be less than in air cooling to in water cooling.
Benzer Tezler
- Kendiliğinden yerleşen borlu aktif belit çimentolu betonların yüksek sıcaklık altındaki performansı
Compacting concretes boron active belite cement performance of self-under high temperature
NESLİHAN GÖK
Yüksek Lisans
Türkçe
2019
İnşaat MühendisliğiAtatürk Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ALİ ÖZ
- Beton basınç dayanımını etkileyen faktörlerin incelenmesi
Investigation of the factors affecting the strength of concrete
İBRAHİM ÖZBEBEK
Yüksek Lisans
Türkçe
2002
İnşaat MühendisliğiÇukurova Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. CENGİZ DURAN ATİŞ
- Farklı çimento tipleri ile üretilen betonlarda sülfat etkisinin incelenmesi
Effect of sulfate on concrete properties produced by different portland cements
BEHİYE BERİL KESER
Yüksek Lisans
Türkçe
2022
İnşaat MühendisliğiToros Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. ÖMER ARIÖZ
- Experimental evaluation and modelling of the compressive strength of concretes produced with different strength classes of cements
Farklı dayanım sınıfları ile üretilen betonların basınç dayanımlarının deneysel olarak değerlendirilmesi ve modellenmesi
MUHAMMED BURAK BOZGEYİK
Yüksek Lisans
İngilizce
2019
İnşaat MühendisliğiHasan Kalyoncu Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DOÇ. DR. KASIM MERMERDAŞ
- Hafif agregalar kullanılarak yalıtım özelliği yüksek duvar yapı malzemelerinin geliştirilmesi, ısıl ve ses performanslarının incelenmesi
The development of high insulation building materials by using light-weight aggregates and investigation of the thermal and acoustic performance
RECEP DOĞMUŞ
Yüksek Lisans
Türkçe
2016
Mühendislik BilimleriBatman ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. ZEKİ ARGUNHAN