Tronanın kalsinasyonu ve kalsine üründen soda üretimi
Başlık çevirisi mevcut değil.
- Tez No: 24743
- Danışmanlar: DOÇ. DR. SABRİ ÇOLAK
- Tez Türü: Yüksek Lisans
- Konular: Kimya Mühendisliği, Chemical Engineering
- Anahtar Kelimeler: Ankara-Beypazarı, Kalsinasyon, Soda, Trona, Ankara-Beypazarı, Calcination, Soda, Trona
- Yıl: 1992
- Dil: Türkçe
- Üniversite: Atatürk Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET Bu çalışmada, Beypazarı-ANKARA yöresi trona cevherinden flash kalsinasyon-liç-karbonatlaştırma kalsinasyon prosesi takip edilerek, hafif soda üretimi incelendi. Birinci basamakta trona cevheri, serbest düşmeli bir reaktörde flash kalsinasyona uğratıldı. Kalsinasyonda sıcaklık ve tanecik boyutunun ağırlık kaybı üzerine etkisi incelendi. Kalsinasyonda ağırlık kaybı, kalsinasyon sıcaklığının artışı ve tanecik boyutunun küçülmesi ile artmaktadır. -80+100 mesh'lik fraksiyonun 300 °C'da kalsinasyonunda ağırlık kaybı % 29.59 olarak bulundu. İkinci basamakta, kalsine cevher suda liç edildi. Liç deneylerinde, mekanik karıştırrrıalı ısıtıcılı bir cam reaktör kullanıldı. Reaksiyonun ilerleyişi pH/mv elektrod yardımıyla milivolt değerleri kaydediciye aktarılarak takip edildi. Liç deneyinde -80+100 mesh'lik flash kalsine edilmiş örnekle çalışıldı. Çözünme hızının liç sıcaklığı ile arttığı tesbit edildi. Kalsine tronanın su ile liç kinetiğinin -Ln(l-x) = 4.07106 exp (-4932/TU-0.445 şeklinde homojen birinci mertebe hız ifadesine uyduğu ve aktivasyon enerjisinin 9.8 kcal/mol olduğu bulundu. Üçüncü basamakta, NaHC03'ın kristallendlrilmesi incelendi. Kristallendirmede en iyi sonuç 50 °C'da çözme, 20 °C'da karbonatlaştırma yöntemiyle elde edildi. Prosesin son basamağında, NaHCÛ3 300 °C'da kalsine edilerek hafif soda üretildi. L
Özet (Çeviri)
ii SUMMARY In this study, the production of soda ash was investigated by following the proceses of flash calcination-leaching-carbonation-calcination, using trona ore from Beypazan-ANKARA. At the first stage, the tfona ore was flash calcined in a free-fall reactor. The effect of calcination temperature and particle size on weight loss was studied. It was found that the weight loss incrased with increasing calcination temperature and decreasing particle size. The veight loss of a fraction of -80+ 100 mesh was found as 29.59 %. At the second stage, the calcined ore was leached with water. In the leaching experiments, a glass reactor having a mechanical stirrer and a heater was used. The reaction proceed was recorded by means of a pH/mv electrode. In the leaching experinents, the fraction of -80+100 mesh of the calcined ore was used. It was observed that the dissolution rate increased with increasing temperature. It was found that the leaching kinetic fits a rate expression of a homogenous first order, which is as follow, -Ln( 1 -x)= 4.07 1 (P exp (-4932/T).t-0.445 and that the activation energy is 9.8 kcal/mol. At the third stage, the crystallization of NaHCC>3 was investigated. At the crystallization, the best result was obtained applying the dissolution process at 50 °C and carbonation at 20 °C. At the last stage of the proces, soda ash was produced by the calcination of NaHC03 at 300 °C
Benzer Tezler
- Trona based scrubbing of sulfur dioxide in a spray drier
Başlık çevirisi yok
F.ÇİĞDEM UÇAR
Yüksek Lisans
İngilizce
1990
Kimya MühendisliğiOrta Doğu Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. GÜNİZ GÜRÜZ
- Trona mineralinden ticari ölçek soda üretim proseslerinin bilgisayar destekli tasarım ve maliyetlendirilmesi
Computer aided desing and cost estimation model of commercial soda ash production processes from trona mineral
NİLÜFER DURMAZ
- Beypazarı trona mineralinin çözelti madenciliği ile değerlendirilmesi
Evaluation of Beypazarı trona deposit by solution mining technique
GÜLHAYAT SAYGILI(NASÜN)
- Baca gazı desülfürizasyon trona ve spray dryer uygulaması
Başlık çevirisi yok
BÜLENT İLHAN GONCALOĞLU
Yüksek Lisans
Türkçe
1993
Çevre MühendisliğiYıldız Teknik ÜniversitesiÇevre Mühendisliği Ana Bilim Dalı
PROF. DR. FERRUH ERTÜRK
- Trona mineralinden ticari ölçek soda-sodyum hidroksit üretimi: Entegre tesis tasarım ve ekonomik analiz
Production of soda ash and sodium hydroxide from trona mineral integrated process design and economic analysis
NALAN ERDÖL