MgO-kısmen stabilize zirkonya dental altyapı seramiklerin üretimi ve karakterizasyonu
Production and characterization of MgO partially stabilized zirconia dental ceramics
- Tez No: 336978
- Danışmanlar: YRD. DOÇ. DR. CEMİLE BETÜL EMRULLAHOĞLU ABİ
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Mühendislik Bilimleri, Seramik Mühendisliği, Metallurgical Engineering, Engineering Sciences, Ceramic Engineering
- Anahtar Kelimeler: Mg-KSZ, soğuk izostatik presleme, sinterleme, karakterizasyon, Mg-PSZ, cold isostatic pressing, sintering, characterization
- Yıl: 2013
- Dil: Türkçe
- Üniversite: Afyon Kocatepe Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 127
Özet
Dental uygulamalarda kullanılan üç çeşit zirkonyum içeren seramik sistemi mevcuttur. Bunlar, yitriyum tetragonal zirkonya polikristalleri (3Y-TZP), magnezyum kısmen stabilize zirkonya (Mg-KSZ) ve zirkonya ile toklaştırılmış alümina (ZTA) şeklinde sınıflandırılırlar. MgO diğer kararlılaştırıcı oksitlere göre daha ucuz ve bol bulunuduğu için kısmen stabilize edilmiş ZrO2 esaslı seramiklerde en fazla araştırmaya konu olmuş katkıdır. Bu çalışma üç aşamadan oluşmaktadır. Birinci aşamada monoklinik zirkonyaya magnezyum klorür ve kalsiyum oksit katkısı ile Mg-kısmen stabilize zirkonya (Mg-KSZ) tozu hazırlanmıştır. İkinci aşamada, hazırlanan tozlar kuru presleme ve soğuk izostatik presleme ile şekillendirilmiştir ve şekillendirilen numuneler 1400, 1450 ve 1500°C olmak üzere üç farklı sıcaklıkta sinterlenmiştir. Sinterlenen numunelerin görünür, kapalı ve toplam gözenek yüzdeleri, bulk yoğunlukları hesaplanmıştır. Ayrıca XRD ile faz analizleri, üç nokta eğme dayanımı ve mikro sertlik gibi mekanik özellikleri belirlenmiş, SEM ile mikroyapıları incelenmiştir. Ayrıca piyasadan hazır olarak temin edilen % 3 mol yittria ile stabilize edilmiş zirkonya tozu da aynı şekilde şekillendirilip sinterlenmiş ve elde edilen sonuçlar kıyaslanmıştır. Sonuç olarak elde edilen zirkonya tozu yüksek oranda kübik faz yanında tetragonal zirkonya ve kalsiyum zirkonat fazı içermektedir. Sinterlenen ürünler yüksek oranda gözenek içermektedir, bu nedenle magnezyum nitrat ve magnezyum klorür katkısı ile ilave olarak iki adet reçete oluşturulmuş ve bunlar attritör değirmende öğütülerek sinterlenmiştir. Neticede daha ince taneli bir yapı ve yüksek yoğunluk elde edilmiştir.
Özet (Çeviri)
There are three types of zirconium containing ceramic systems in literature for dental applications. These are classified as yittrium tetragonal zirconia polycrystals (3Y-TZP), magnesium partial stabilized zirconia (Mg-KSZ) and zirconia toughened alumina (ZTA). MgO is an additive in partial stabilized ZrO2 based ceramics, which is widely studied. This study consists of three steps. In the first step. Mg-partial stabilized zirconia (Mg-PSZ) powder was prepared with the addition of magnesium cloride and calcium oxide to the monoclinic zirconia powder. Further step involves dry pressing and cold isostatic pressing of the powders obtained and sintering process of the compacts at three different temperature. Percentages of apparent porosity, closed porosity, total porosity of the samples were calculated. Phase analysis and microstructure investigations were also evaluated by XRD and SEM and mechanical properties were measured by 3-point bending tests and microhardness tests. A commercially available powder stabilized with %3 mol yttria was prepared and sintered in the same conditions by the aim of comparison. As a result, zirconia powder prepared by magnesium cloride and calcium oxide contain a high amount of cubic zirconia with tetragonal phase and calcium zirconate phases. The results showed that the samples synthesized in this study contain high porosity accordingly, two more recipes were prepared by adding magnesium cloride and magnesium nitrate and these powder mixtures were attrition milled before sintering. Consequently, fine grained microstructures and high densities were obtained.
Benzer Tezler
- Characterization studies on zirconia partially stabilized with Y2O3 developed via high energy milling
Yüksek enerjili öğütme sistemleri ile üretilen Y2O3 ile kısmen stabilize zirkonyanın karakterizasyonu
TOYGAN SÖNMEZ
Yüksek Lisans
İngilizce
2009
Metalurji Mühendisliğiİstanbul Teknik Üniversitesiİleri Teknolojiler Ana Bilim Dalı
PROF. DR. M. LÜTFİ ÖVEÇOĞLU
- Zirkonya esaslı refrakter kompozitlerin üretim parametrelerinin geliştirilmesi
Improvement of parameters for production of refractory composites based on zirconia
ÇAĞATAY DURMUŞ
Doktora
Türkçe
2015
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ÖMER SERDAR ÖZGEN
- Refrakter üretimine yönelik olarak zirkonya stabilizasyon çalışmaları
Stabilization studies of zirconia for production of refractories
VEDAT KÖROĞLU
Yüksek Lisans
Türkçe
2013
Seramik Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ÖMER SERDAR ÖZGEN
- Mullit katkılı farklı oksitlerle stabilize edilmiş zirkonya seramiklerinin üretimi, karakterizasyonu ve aşınma özelliklerinin incelenmesi
Production, characterization and investigation of wear properties of zirconia ceramics with mullite additives and stabilized with different oxides
MEHMET AKİF HAFIZOĞLU
Doktora
Türkçe
2021
Makine MühendisliğiSivas Cumhuriyet ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. AHMET AKKUŞ
- Processing and analysis of zirconia based refractories
Zirkonya esaslı refrakterlerin proses ve analizleri
SINA SADIGH AKBARI
Yüksek Lisans
İngilizce
2015
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ÖMER SERDAR ÖZGEN