Farklı başlangıç maddeleri kullanılarak sol-jel yöntemiyle monolitik silika aerojel ve silika aerojel sentezi ve karakterizasyonu

Synthesis and characterization of monolithic silica aerogel and silica aerogel with sol-gel method by using different starting materials

PDF İndir

  1. Tez No: 342852
  2. Yazar: YELİZ YILMAZ
  3. Danışmanlar: PROF. DR. HABİBE CANAN CABBAR
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya Mühendisliği, Chemical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2013
  8. Dil: Türkçe
  9. Üniversite: Gazi Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: Belirtilmemiş.

Özet

Silika aerojeller yüksek gözenekliliğe, yüksek yüzey alanına, yüksek ısıl yalıtım değerine, çok düşük yoğunluğa ve çok düşük dielektrik sabitine gibi sıra dışı özelliklere sahip nano yapılı malzemelerdir. Bu özelliklerinden dolayı yalıtım, kimya, elektronik gibi pek çok farklı sektörlerde kullanılmaktadır. Bu sebeple silika aerojellerin üretimi birçok araştırmanın temelini oluşturmaktadır. Bu çalışmada, farklı başlangıç maddeleri ve farklı parametreler kullanılarak sol-jel yöntemiyle silika aerojel sentezlenmiştir. Yapılan ilk deneysel çalışmada başlangıç maddesi olarak silis kumu ve feldspat kullanılmıştır. Sodyum silikat çözeltisi hazırlama aşamasında farklı pHlarda (2 - 7) çalışılmıştır. Jelleşme basamağında katalizör olarak HCl ve farklı derişimlerde (0,5 - 3 M) H2SO4 kullanılmıştır. Bir diğer parametre olarak ise farklı fırın sıcaklıklarında (50 ? 130 ?C) kurutma işlemi gerçekleştirilmiştir. pH değeri 6 olan hem silis kumundan hem de feldspattan elde edilen sodyum silikat çözeltisi, jelleşme basamağında HCl katalizörü kullanımı sonrası elde edilen jelin 110 ?C?de kurutulmasıyla elde edilen silika aerojellerin yüzey alan değerleri sırasıyla 754 m2/g, 802 m2/g ve ortalama gözenek çap değerleri ise 31 Å olarak belirlenmiştir. Yapılan bir diğer çalışmada silika kaynağı olarak tetraetilortosilikat (TEOS), polietilen glikol (PEG) VE HNO3 katalizörü kullanılarak sol-jel yöntemiyle monolitik silika aerojel sentezlenmiştir. Farklı katalizör konsantrasyonlarında ve gerek üreli gerekse üresiz ortamda sentezlenen monolitik silika aerojellere karakterizasyon çalışmaları yapılmıştır. Bu çalışmalar neticesinde üre kullanılmadan ve 0,6 ml HNO3 varlığında en iyi yüzey alanı sonucunun (1200 m2/g) elde edildiği gözlemlenmiştir.

Özet (Çeviri)

Silica aerogels are nano-structered materials, which have unusual features such as high porosity, high surface area, high thermal isolatioın value, very low density and very low dielectric constant. Due to these properties, they are used in many sectors such as construction, pharmacy, chemistry, electronic. Thus, the productiıon of silica aerogels forms the basis of many studies. In this study, silica aerogels was synthesized with left-gel method by using different starting substances and different parameters. In the first experimental study, silica sand and feldspar were used as a starting substance. In the preparation phase of sodium silicate solution was worked with different pH (2-7). In gelation phase, as a catalytic HCI and H2SO4 was used with different concentration (0,5-3M). As another parameter, drying process was realized with different oven temperature (50-130 ?C ). Sodium silicate solution, of which pH value was 6, was obtained both silica sand and feldspar. In gelation phase, after HCl katalizör was used gel was dried in 110 ?C. Silica aerogels were obtained. The surface area value of these silica aerogels was determined as 744 m2/g, 802 m2/g in order and average pore diameter was 31 A. In another study, monolithic silica aerogel was synthesized with left-gelş method, using tetraetilortosilikat (TEOS) as silica source, polietilen glycol (PEG) and HNO3 catalytic for monolithic silica aerogel, which was synthesized in different catalyst concentrations and in environment either with urea or not, was done charactereization study. As a result of these studies, ıt was observed that not using area and with 0,6 m HNO3 the best surface area result that was obtained was (1200 m2/g).

Benzer Tezler

  1. Tez No

    202

    Bazı esterlerin kinetik incelenmesi ve termodinamik parametrelerin belirlenmesi

    Kinetic study and detesmination of thermodnamic parameters of some esters

    İBRAHİM TAŞ

    Yüksek Lisans

    Türkçe

    Türkçe

    1986

    Kimya MühendisliğiUludağ Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. MUSTAFA CEBE

  2. Tez No

    252

    İzmir'de bazı yolların kapatılarak yaya bölgeleri oluşturma da kent peyzajını geliştirme açısından yeniden planlanması üzerinde araştırmalar

    Başlık çevirisi yok

    BAHAR TÜRKYILMAZ

    Yüksek Lisans

    Türkçe

    Türkçe

    1985

    Şehircilik ve Bölge PlanlamaEge Üniversitesi

    Şehir ve Bölge Planlama Ana Bilim Dalı

  3. Tez No

    7

    Testosteron dihidrotestosteron ve östrojenin benign prostat hiperplazisindeki etyolojik rolleri

    The roles of testosterone, dihydrotestosterone and estradiole on the etiology of benign prostatic hyperplasia

    HALUK TOKUÇOĞLU

    Tıpta Uzmanlık

    Türkçe

    Türkçe

    1986

    ÜrolojiGazi Üniversitesi

    Üroloji Ana Bilim Dalı

  4. Tez No

    10

    Süt formüllerinin tüketim uygulamaları ve süt formüllerinin C vitamini içeriği ile pH değerleri

    Başlık çevirisi yok

    GÖNÜL VAROL

    Yüksek Lisans

    Türkçe

    Türkçe

    1986

    Besin Hijyeni ve Teknolojisiİstanbul Üniversitesi

    Çocuk Gelişimi Ana Bilim Dalı

    DOÇ. DR. TÜRKAN KUTLUAY

  5. Tez No

    11

    Türkiye'de aile planlaması çalışmalarında erkeklerin önemi, hastane personeli ile fabrika işçilerinin doğum kontrol yöntemlerine karşı tutum ve davranranışlarında farklılığın araştırılması

    Başlık çevirisi yok

    KAMİL MALKOÇLU

    Yüksek Lisans

    Türkçe

    Türkçe

    1987

    Demografiİstanbul Üniversitesi

    Aile Sağlığı Ana Bilim Dalı

    DOÇ. DR. DERİN KÖSEBAY

Geri Dön