InSe ve InSe:Zn yarı iletkenlerin Bridgman/Stockbarger tekniğiyle büyütülmesi ve yapısal karakterizasyonu
Growth of InSe and InSe:Zn semiconductors by Bridgman/Stockbarger technique and structural characterizations
- Tez No: 352162
- Danışmanlar: YRD. DOÇ. DR. BEKİR GÜRBULAK
- Tez Türü: Yüksek Lisans
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: InSe, InSe:Zn, Brigdman-Stockbarger Tekniği, XRD, SEM, EDX, InSe, InSe:Zn Brigdman-Stockbarger Technique, XRD, SEM, EDX
- Yıl: 2014
- Dil: Türkçe
- Üniversite: Atatürk Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 70
Özet
Nano ve optoelektronik teknolojinin ilerlemesinde yarıiletkenlerin önemi giderek artmaktadır. Ancak, kullanılacak yarıiletkenlerin hem kolay elde edilebilir hem de uygulama alanın geniş olması daha da önem arz etmektedir. Bu maksatla, uygulama alanlarının çok olduğu ve karakteristiklerinin tam olarak belirlendiği yarıiletkenlere ihtiyaç duyulmaktadır.Bu çalışma ile InSe ve InSe:Zn ikili yarıiletken bileşikleri, bölümümüz kristal büyütme laboratuvarında, modifiye edilmiş Bridgman-Stockbarger metodu ile büyütüldü. Numunelerin, yapısal ve morfolojik karakterizasyonları X-ışını kırınımı (XRD), taramalı Elektron Mikroskobu (SEM) ve Enerji ayrımlı X-ışını spektroskopisi (EDX) teknikleri kullanılarak gerçekleştirildi. XRD sonuçları, büyütülen numunelerin hekzagonal kristal yapıya sahip olduklarını ve Zn katkılamanın pik şiddetlerini artırdığını gösterdi. XRD sonuçları kullanılarak, örgü parametreleri InSe için a =b= 4.002 Å, c = 17.160 Å ve ve InSe:Zn (0012) için ise a =b= 5.845 Å ve c = 16.788 Å olarak hesaplandı. SEM sonuçlarından, ortalama tanecik büyüklüğünün sırasıyla, InSe için 42-155 nm ve InSe:Zn için 50-125 nm aralığında olduğu gözlendi. EDX sonuçları, In ve Se elementlerinin ağırlıkça %57.04 ve %38.46 olarak yapıda yer aldığını gösterdi. In ve Se miktarlarının büyütmenin hemen başlangıcında hesaplanan stokiyometrik değerlere oldukça yakın olduğu gözlendi.
Özet (Çeviri)
The importance of semiconductors paving the way for nano and optoelectronic technology has recently been increasing. But, producing them easily and having their vast application fields are most important. For that reason, the crystals having wide application field and their characteristics which are determinated are needed.InSe and InSe:Zn binary semiconductor compounds were grown in our crystal growth laboratory by the modified Bridgman-Stockbarger method. The structural and morphological characterizations of the samples were carried out by X-ray diffraction (XRD), Scanning Electron Microscopy (SEM) and Energy-dispersive X-ray spectroscopy (EDX) techniques. The XRD results indicated that the grown films had hexzagonal structure and Zn doping increased the peak intensities. The lattice parameters were calculated to be a=b= 4.002 Å, c = 17.160 Å for InSe and a=b= 5.845 Å ve c = 16.788 Å for (0012) InSe:Zn using the XRD results.From the SEM results, it was observed that the average grain size values for InSe and InSe:Zn were between 42-155 nm and 50-125 nm, respectively. EDX results showed that In and Se elements were in weight 57.04% and 38.46% in the structure. It was observed that the amounts for the In and Se were quite close to the stochiometric values calculated just before the growth.
Benzer Tezler
- p-InSe:Mn yarı iletkeninin Schottky kontak davranışı
The schottky contact behaviour of p-InSe:Mn semiconductor
ZEYNEP ELKOCA
Yüksek Lisans
Türkçe
2010
Fizik ve Fizik MühendisliğiAtatürk ÜniversitesiFizik Ana Bilim Dalı
DOÇ. DR. SONGÜL DUMAN
- Encapsulation of echium oil and saffron extract in electrospun nanofibers
Echıum yağı ve safran ekstraktının elektroeğrilmiş nanoliflerde enkapsülasyonu
ZAHRA NAJAFI
Doktora
İngilizce
2022
Gıda Mühendisliğiİstanbul Teknik ÜniversitesiGıda Mühendisliği Ana Bilim Dalı
PROF. DR. NEŞE ŞAHİN YEŞİLÇUBUK
PROF. DR. FİLİZ ALTAY
- Kuzeydoğu Anadolu kökenli bazı yenilebilir bitki ekstraktlarının biyolojik aktivite ve fenolik asit profil değişiminin ekstraksiyon tekniği tabanlı incelenmesi
Extraction technique based investigation of changings in biological activity and phenolic acid profile of the extracts from some edible North Eastern Anatolia originplants
İNAN DURSUN
- Deneysel diyabet oluşturulan ratlarda selenyum uygulamasının serum ve doku mineral madde düzeyleri ile bazı biyokimyasal parametrelere etkileri
The effects of selenium on mineral status of serum and tissue and some biochemical parameters in experimental diabetic rats
SERPİL ÇİÇEK
Doktora
Türkçe
2017
BiyokimyaSelçuk ÜniversitesiVeteriner Biyokimya Ana Bilim Dalı
PROF. SEYFULLAH HALİLOĞLU
- Endemik guvatr etiyopatogenezinde iyod, selenyum, bakır ve çinko düzeylerinin önemi
Başlık çevirisi yok
MURAT ŞALK
Tıpta Uzmanlık
Türkçe
1997
Endokrinoloji ve Metabolizma HastalıklarıGATAİç Hastalıkları Ana Bilim Dalı
DOÇ. DR. METİN ÖZATA