Yeni nesil metal baskılanmış mikroküre sentezi ve bu mikrokürelerin ICP-OES ile bazı metallere karşı tayin performansının incelenmesi

A novel metal imprinted microbeads and investigation which is based on their performance against to the some metals by using the ICP-OES synthesis

  1. Tez No: 374614
  2. Yazar: SİBEL ÇOLAK
  3. Danışmanlar: YRD. DOÇ. DR. MUHARREM KARABÖRK
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya, Chemistry
  6. Anahtar Kelimeler: İyon baskılanmış polimer, Mikroküre, Önderiştirme, Katı-faz ekstraksiyonu, Cu(II) iyon, ICP-OES, Ionimprinted polymers, Microspheres, Preconcentration, Solid-phase extraction, Cu (II) ions, ICP-OES
  7. Yıl: 2014
  8. Dil: Türkçe
  9. Üniversite: Kahramanmaraş Sütçü İmam Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 92

Özet

Bu çalışmada, sulu çözeltilerden Cu(II) iyonlarının seçici olarak uzaklaştırılması için kullanılabilecek iyon baskılanmış polimerler hazırlanmıştır. Bu amaçla, polimerik adsorbentin sentez aşamasında fonksiyonel monomer olarak (E)-2-hidroksi-5-((vinilfenil)diazonil)benzaldehit kullanılmıştır. Kalıp molekül Cu+2 iyonu ile fonksiyonel monomer etkileştirilerek dispersiyon polimerizasyon tekniği ile Cu(II) baskılı poli[Cu(C15H11N2O2)] mikroküreleri sentezlenmiştir. Daha sonra baskılı polimerlerden Cu(II) iyonları 4 M HNO3 çözeltisi kullanılarak uzaklaştırmıştır. Böylece yapıda Cu(II) iyonlarına özgü seçici bölgeler oluşturulmuştur. Cu(II) baskılanmış poli[Cu(C15H11N2O2)] mikrokürelerinin spesifik yüzey alanı 374,26m2/g ve şişme oranı %80 olarak bulunmuştur. Maksimum adsorpsiyon kapasitesi, optimumpH, adsorpsiyon denge zamanı sırasıyla 153.03 mg/g, 8-10 aralığı ve 30 dakika olarak tespit edilmiştir. Elementel analiz sonuçlarına göre baskılama öncesi; C%: 55.72, H%:6.756, N%:0.555 baskılama sonrası C%:58.81, H%:6.998, N%:0.570 olarakbulunmuştur. C, H ve N yüzdelerindeki artış yapıdan kalıp molekülün uzaklaştığını göstermiştir. Baskılanmış mikrokürelerin bağıl seçicilik katsayısı Cu(II)/Ni(II), Cu(II)/Pb(II), Cu(II)/Zn(II) ve Cu(II)/Co(II) için sırasıyla 13.09, 57.88, 44.719 ve 35.006 olarak bulunmuştur. Bu sonuçlar; Cu(II) baskılanmış mikrokürelerin Cu(II) iyonlarına karşı daha seçici olduğunu göstermiştir. Yapılan tekrarlanabilirlik çalışmaları Cu(II) baskılanmış poli[Cu(C15H11N2O2)] mikrokürelerin adsorpsiyon kapasitesinde önemli bir azalma olmaksızın tekrar tekrar kullanılabilir olduğunu göstermiştir.

Özet (Çeviri)

In thisstudyionimprinted polymershave been prepared,whichcanbeusedfor theselectiveremovalofCu (II) ionsfromaqueous solution. For this purpose (E) 2-hydroxy-5-((vinylphenyl)diazonil) benzaldehydewas used as a functional monomer during the synthesis stage of polymericadsorbent. Cu(II) imprinted poly[Cu(C15H11N2O2)]microbeads were synthesized from the reaction of template ions Cu+2 with the functional monomer thanks to usage of the dispersion polymerization techniques.Then, Cu (II) ions were removed using 4 M HNO3 solution. So that the formed regions of the structure were specific selector for Cu (II) ions. The specific surface area of the Cu(II) imprinted poly[Cu(C15H11N2O2)]microbeads was found to be 374.26 m2/g, and the swelling ratio was about to %80.The maximum adsorption capacity, optimum pH and equilibrium adsorption timewere determined to be 153.03 mg/g, range of 8-10 and 30 min, respectively. According to the elemental analysis results, before imprinting; C%: 55.72, H%:6.756, N%:0.555 after imprinting; C%:58.81, H%:6.998, N%:0.570. C, Hand Npercentageincrease in thestructureof moleculeshowed that template molecule left the structure.The relative selectivity coefficients of imprinted microbeads for Cu(II)/Ni(II), Cu(II)/Pb(II), Cu(II)/Zn(II) and Cu(II)/Co(II) were 13.09, 57.88, 44.72 and 35.01, respectively. These results haveshownthat Cu(II) imprintedmicrospheres are more selective towards Cu(II) ions. The Cu(II) imprinted poly[Cu(C15H11N2O2)]microbeadscould be used many times without decreasing their adsorption capacities significantly.

Benzer Tezler

  1. İnsan plazmasından demir(III) iyonları uzaklaştırılması için demir(III) baskılanmış poli(GMA-MAC) mikroküre - kriyojel kompozit sisteminin hazırlanması

    Preparation of iron(III) imprinted poly(GMA-MAC) microbead - cryogel composite system for removal of iron(III) ions from human plasma

    BAHAR ERGÜN

    Yüksek Lisans

    Türkçe

    Türkçe

    2009

    BiyokimyaHacettepe Üniversitesi

    Kimya Ana Bilim Dalı

    DOÇ. DR. HANDAN YAVUZ

  2. Yeni nesil metal baskılanmış nanokompozit katı destek sentezi ve bu katı desteklerin metal iyonuna olan ilgisinin araştırılması

    A novel metal imprinting solid packet of synthesis and research of their affinity to metal ion

    ALİYE GÖK

    Yüksek Lisans

    Türkçe

    Türkçe

    2014

    KimyaKahramanmaraş Sütçü İmam Üniversitesi

    Kimya Ana Bilim Dalı

    YRD. DOÇ. DR. MUHARREM KARABÖRK

  3. Biyomoleküller için molekül baskılanmış polimerik yapay reseptör geliştirilmesi ve biyokromatografi uygulamaları

    Investigation of molecular imprinted polymeric artificial receptor for biomolecules and biochromatographic applications

    AYÇA ÖZCAN

    Doktora

    Türkçe

    Türkçe

    2007

    KimyaAnadolu Üniversitesi

    Kimya Ana Bilim Dalı

    DOÇ. DR. ARZU ERSÖZ

  4. Dietil fitalat baskılanmış mikroküreler ile sulu ortamdan fitalat esterlerinin uzaklaştırılması ve analitik uygulamaları

    Removal of phthalate esters in aqueous media with diethyl phthalate imprinted microspheres and analytical applications

    TUĞÇE YAZICI

    Yüksek Lisans

    Türkçe

    Türkçe

    2016

    KimyaUludağ Üniversitesi

    Kimya Ana Bilim Dalı

    DOÇ. DR. ELİF TÜMAY ÖZER

  5. Next-generation biosensor systems for environmental water quality monitoring

    Çevresel su kalitesi izleme için yeni nesil biyoensör sistemleri

    NİMET YILDIRIM TİRGİL

    Doktora

    İngilizce

    İngilizce

    2015

    BiyomühendislikNortheastern University

    Biyomühendislik Ana Bilim Dalı

    PROF. DR. APRİL Z. GU